Chemical and Biological Treatment of Acid Mine Drainage for the Removal of Heavy Metals and Acidity

This dissertation reports the design of a process (patent pending) to remove iron from acid mine drainage (AMD) without the formation of metal hydroxide sludge. The system includes the oxidation of ferrous iron in a packed bed bioreactor, the precipitation of iron within a fluidized bed, the removal of manganese and heavy metals (Cu, Ni, Zn) in a trickling filter at high (>9) pH, with final neutralization in a carbonate bed. The technique avoided the generation of iron oxyhydroxide sludge. In the packed bed bioreactor, maximum substrate oxidation rate (R_,max) was 1500 mg L⁻¹ h⁻¹ at dilution rates of 2 h⁻¹, with oxidation efficiency at 98%. The half-saturation constant (similar to a Ks) was 6 mg L⁻¹. The oxidation rate was affected by dissolved oxygen below 2 mg L⁻¹, with a Monod-type Ko for DO of 0.33 mg L⁻¹. Temperature had a significant effect on oxidation rate, but pH (2.0 to 3.25) and supplemental CO₂ did not affect oxidation rates. Iron hydroxide precipitation was not instantaneous when base was added at a OH/Fe ratio of less than 3. Induction time was found to be a function of pH, sulfate concentration and iron concentration, with a multiple R² of 0.84. Aqueous [Al (III)] and [Mn (II)] did not significantly (α = 0.05) affect induction time over the range of concentrations investigated. When specific loading to the fluidized bed reactor exceeded 0.20 mg Fe m⁻² h⁻¹, dispersed iron particulates formed leading to a turbid effluent. Reactor pH determined the minimum iron concentration in the effluent, with an optimal at pH 3.5. Total iron removals of 98% were achieved in the fluidized bed with effluent [Fe] below 10 mg L⁻¹. Further iron removal occurred within the calcium carbonate bed. Heavy metals were removed both in the fluidized bed reactor as well as in the trickling filter. Oxidation at pH >9 caused manganese to precipitate (96% removal); removals of copper, nickel, and zinc were due primarily to sorption onto oxide surfaces. Removals averaged 97% for copper, 70% for nickel and 94% for zinc. The treatment strategy produced an effluent relatively free of iron (< 3 mg/L), without the formation of iron sludge and may be suitable for AMD seeps, drainage from acidic tailings ponds, active mine effluent, and acidic iron-rich industrial wastewater.

Name thesis:degree_name

Ph. D.

Level thesis:degree_level

doctoral

Discipline thesis:degree_discipline

Civil Engineering

Department dc:contributor.department

Civil Engineering

Grantor dc:publisher

Virginia Tech

Year dc:date.issued

1997

Author dc:creator

• Diz, Harry Richard

Chair dc:contributor.committeechair

• Novak, John T.

Committee members dc:contributor.committeemember

• Cherry, Donald S.
• Knocke, William R.
• Love, Nancy G.
• Rimstidt, J. Donald

• iron biooxidation
• iron precipitation
• iron removal technology
• acid mine drainage

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Dc Identifier Other

etd-81697-135443

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/30713