{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/28826"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/28826","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Wood Material Behavior in Severe Environments","abstract":"An improved knowledge of wood material behavior in hot-pressing environments can provide the benefit of an increased understanding of material properties during the manufacture of wood-based composites as well as insight into the development of new processes and products which manipulate the viscoelastic nature of wood. Two specific areas where additional knowledge is needed are: the high temperature equilibrium moisture content (EMC) behavior and the moisture dependent softening behavior. EMC data was collected and desorption isotherms were generated for mature and juvenile wood of aspen, loblolly pine and yellow-poplar at 50 and 160°C. High temperature EMC behavior was found to be distinct from that at lower temperatures, and considerable differences between the isotherms for juvenile and mature wood were detected. Substantial thermal degradation was observed during desorption at 160 °C and found to be strongly influenced by relative humidity. The thermal softening behavior of wood was evaluated using dielectric thermal analysis (DETA) at moisture levels from 0 to 20 percent. Coincident in situ relaxations of hemicellulose and amorphous cellulose in the range of 20 to 200 °C were observed and found to exhibit the characteristics of a secondary (glass) transition. The moisture dependence of this transition was characterized, and differences in the observed Tg were detected between juvenile and mature wood. Time-temperature superposition was also shown to be applicable to the wood-water system.","abstract_html":"An improved knowledge of wood material behavior in hot-pressing environments can provide the benefit of an increased understanding of material properties during the manufacture of wood-based composites as well as insight into the development of new processes and products which manipulate the viscoelastic nature of wood. Two specific areas where additional knowledge is needed are: the high temperature equilibrium moisture content (EMC) behavior and the moisture dependent softening behavior. EMC data was collected and desorption isotherms were generated for mature and juvenile wood of aspen, loblolly pine and yellow-poplar at 50 and 160°C. High temperature EMC behavior was found to be distinct from that at lower temperatures, and considerable differences between the isotherms for juvenile and mature wood were detected. Substantial thermal degradation was observed during desorption at 160 °C and found to be strongly influenced by relative humidity. The thermal softening behavior of wood was evaluated using dielectric thermal analysis (DETA) at moisture levels from 0 to 20 percent. Coincident in situ relaxations of hemicellulose and amorphous cellulose in the range of 20 to 200 °C were observed and found to exhibit the characteristics of a secondary (glass) transition. The moisture dependence of this transition was characterized, and differences in the observed Tg were detected between juvenile and mature wood. Time-temperature superposition was also shown to be applicable to the wood-water system.","abstract_has_math":false,"creators":["Lenth, Christopher Allen"],"institution":"Virginia Tech","degree_name":"Ph. D.","degree_level":"doctoral","degree_discipline":"Wood Science and Forest Products","degree_department":"Wood Science and Forest Products","school":null,"contributors":[],"advisors":[],"committee_chairs":["Kamke, Frederick A."],"committee_members":["Watson, Layne T.","Loferski, Joseph R.","Dillard, David A.","Zink-Sharp, Audrey G.","Frazier, Charles E."],"year":1999,"date_issued":"1999-05-11","date_published":"1999-05-11","updated_at":"2026-07-22T22:20:35Z","subjects":["high temperature","equilibrium moisture content","viscoelasticity","thermal softening"],"languages":[],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-08302000-12360026"],"render_values":[{"text":"etd-08302000-12360026","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/10919/28826","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.committeechair","label":"Committee Chair","values":["Kamke, Frederick A."]},{"key":"dc:contributor.committeemember","label":"Committee Member","values":["Watson, Layne T.","Loferski, Joseph R.","Dillard, David A.","Zink-Sharp, Audrey G.","Frazier, Charles E."]},{"key":"dc:contributor.department","label":"Department","values":["Wood Science and Forest Products"]},{"key":"dc:creator","label":"Author","values":["Lenth, Christopher Allen"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2014-03-14T20:15:48Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2014-03-14T20:15:48Z","2001-09-06"]},{"key":"dc:date.issued","label":"Date","values":["1999-05-11"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Tech"]},{"key":"dc:type","label":"Dc Type","values":["Dissertation"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Wood Science and Forest Products"]},{"key":"thesis:degree_level","label":"Degree Level","values":["doctoral"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Ph. D."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["high temperature","equilibrium moisture content","viscoelasticity","thermal softening"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.other","label":"Dc Identifier Other","values":["etd-08302000-12360026"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/28826"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["An improved knowledge of wood material behavior in hot-pressing environments can provide the benefit of an increased understanding of material properties during the manufacture of wood-based composites as well as insight into the development of new processes and products which manipulate the viscoelastic nature of wood. Two specific areas where additional knowledge is needed are: the high temperature equilibrium moisture content (EMC) behavior and the moisture dependent softening behavior. EMC data was collected and desorption isotherms were generated for mature and juvenile wood of aspen, loblolly pine and yellow-poplar at 50 and 160°C. High temperature EMC behavior was found to be distinct from that at lower temperatures, and considerable differences between the isotherms for juvenile and mature wood were detected. Substantial thermal degradation was observed during desorption at 160 °C and found to be strongly influenced by relative humidity. The thermal softening behavior of wood was evaluated using dielectric thermal analysis (DETA) at moisture levels from 0 to 20 percent. Coincident in situ relaxations of hemicellulose and amorphous cellulose in the range of 20 to 200 °C were observed and found to exhibit the characteristics of a secondary (glass) transition. The moisture dependence of this transition was characterized, and differences in the observed Tg were detected between juvenile and mature wood. Time-temperature superposition was also shown to be applicable to the wood-water system."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["Ph. D."]},{"key":"dc:title","label":"Title","values":["Wood Material Behavior in Severe Environments"]}]}],"canonical_facts":{"dc:contributor.committeechair":["Kamke, Frederick A."],"dc:contributor.committeemember":["Watson, Layne T.","Loferski, Joseph R.","Dillard, David A.","Zink-Sharp, Audrey G.","Frazier, Charles E."],"dc:contributor.department":["Wood Science and Forest Products"],"dc:creator":["Lenth, Christopher Allen"],"dc:date.accessioned":["2014-03-14T20:15:48Z"],"dc:date.available":["2014-03-14T20:15:48Z","2001-09-06"],"dc:date.issued":["1999-05-11"],"dc:description.abstract":["An improved knowledge of wood material behavior in hot-pressing environments can provide the benefit of an increased understanding of material properties during the manufacture of wood-based composites as well as insight into the development of new processes and products which manipulate the viscoelastic nature of wood. Two specific areas where additional knowledge is needed are: the high temperature equilibrium moisture content (EMC) behavior and the moisture dependent softening behavior. EMC data was collected and desorption isotherms were generated for mature and juvenile wood of aspen, loblolly pine and yellow-poplar at 50 and 160°C. High temperature EMC behavior was found to be distinct from that at lower temperatures, and considerable differences between the isotherms for juvenile and mature wood were detected. Substantial thermal degradation was observed during desorption at 160 °C and found to be strongly influenced by relative humidity. The thermal softening behavior of wood was evaluated using dielectric thermal analysis (DETA) at moisture levels from 0 to 20 percent. Coincident in situ relaxations of hemicellulose and amorphous cellulose in the range of 20 to 200 °C were observed and found to exhibit the characteristics of a secondary (glass) transition. The moisture dependence of this transition was characterized, and differences in the observed Tg were detected between juvenile and mature wood. Time-temperature superposition was also shown to be applicable to the wood-water system."],"dc:description.degree":["Ph. D."],"dc:identifier.other":["etd-08302000-12360026"],"dc:identifier.uri":["http://hdl.handle.net/10919/28826"],"dc:publisher":["Virginia Tech"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:subject":["high temperature","equilibrium moisture content","viscoelasticity","thermal softening"],"dc:title":["Wood Material Behavior in Severe Environments"],"dc:type":["Dissertation"],"thesis:degree_discipline":["Wood Science and Forest Products"],"thesis:degree_level":["doctoral"],"thesis:degree_name":["Ph. D."],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:20:35Z"}