Photo-reactive Surfactant and Macromolecular Supramolecular Structures

For the first time nonwoven fibrous scaffolds were electrospun from a low molar mass gemini ammonium surfactant, N,N–-didodecyl-N,N,N–,N–-tetramethyl-N,N–-ethanediyl-di-ammonium dibromide (12-2-12). Cryogenic transmission electron microscopy (cryo-TEM) and solution rheological experiments revealed micellar morphological transitions of 12-2-12 in water and water:methanol (1:1 vol). Electrospinning efforts of 12-2-12 from water did not produce fibers at any concentration, however, electrospinning 12-2-12 in water:methanol at concentrations greater than 2C* produced, hydrophilic continuous fibers with diameters between 0.9 and 7 μM. Photo-reactive surfactants were synthesized to electrospin robust surfactant membranes. Before electrospinning it was important to fundamentally understand the structure-property relationship of gemini surfactants. The thermal and solution properties were explored for a series of ammonium gemini surfactants using differential scanning calorimetry (DSC), polarized light microscopy (PLM), and conductivity experiments. The Kraft temperature (Tk) was measured in water and water:methanol (1:1 vol) to investigate the influence of solvent on the surfactant solution properties. Other experiments investigate how associated photo-curable architectures are applicable in macromolecular architectures, to gain a fundamental understanding of how hydrogen bonding associations influence the photo-reactivity of functionalized acrylic copolymers. Novel hot melt pressure sensitive adhesives (HMPSAs) were developed from acrylic terpolymers of 2-ethylhexyl acrylate (EHA), 2-hydroxyethyl acrylate (HEA), and methyl acrylate (MA) functionalized with hydrogen bonding and photo-reactive functionalities. The synergy of hydrogen bonding and photo-reactivity resulted in higher peel values and rates of cinnamate photo-reactivity with increasing urethane concentration. Random copolymers of poly(n-butyl acrylate (nBA)-co-2-hydroxyethyl methacrylate (HEMA)) were functionalized with hydrogen bonding and photo-reactive groups to explore the photo-curing of associated macromolecular architectures. The influence of urethane hydrogen bonding on the photo-reactivity of cinnamate-functionalized acrylics was investigated with photo-rheology and UV-vis spectroscopy. Cinnamate-functionalized samples displayed an increase in modulus with exposure time, and the percentage increase in modulus decreased as the urethane content increased. The synergy of hydrogen bonding and photo-reactive groups resulted in higher rates of cinnamate photo-reactivity with increasing urethane concentration. Electrospun fibers were in situ photo-crosslinked to develop fibrous membranes from cinnamate functionalized low Tg acrylics. Electrospinning was conducted approximately 55 °C above the Tg of the cinnamate acrylate and the electrospun fibers did not retain their fibrous morphology without photo-curing. However, electrospun fibers were collected that retained their fibrous morphology and resisted flow when in situ photo-cured during electrospinning. The intermolecular photo-dimerization of cinnamates resulted in a network formation that prevented the low Tg cinnamate acrylate from flowing.

Name thesis:degree_name

Ph. D.

Level thesis:degree_level

doctoral

Discipline thesis:degree_discipline

Chemistry

Department dc:contributor.department

Chemistry

Grantor dc:publisher

Virginia Tech

Year dc:date.issued

2009

Author dc:creator

• Cashion, Matthew Paul

Chair dc:contributor.committeechair

• Long, Timothy E.

Committee members dc:contributor.committeemember

• Moore, Robert Bowen
• Turner, S. Richard
• Davis, Richey M.
• Madsen, Louis A.

• photo-curing
• gemini surfactants
• n-butyl acrylate
• 2-hydroxyethyl acrylate
• cinnamate
• hydrogen bonding
• adhesives
• electrospinning
• photo-rheology

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Dc Identifier Other

etd-05142009-143351

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/27714