Curing Characteristics of Photopolymer Resin With Dispersed Glass Microspheres in Vat Polymerization 3D Printing

The curing characteristics of photopolymer resin determine the relationship between the vat polymerization (VP) process parameters and the layer thickness, geometric accuracy, and surface quality of the 3D printed specimen. Dispersing filler material into the photopolymer resin changes its curing characteristics because the filler scatters and absorbs light, which modifies the curing reaction. However, the ability to cure photopolymer resin with high filler volume fraction is important to 3D print material specimens for specific engineering applications, e.g. structural polymer composite materials, electrical and thermal conductive materials, and ceramic materials for biological and high-temperature environments. We methodically measure the curing characteristics of diacrylate/epoxy photopolymer resin with dispersed glass microspheres. The experiments show that the curing depth, degree-of-cure, and surface roughness depend on both the light exposure dose and the filler fraction. We determine that the degree-of-cure increases with increasing filler fraction for constant exposure dose, and approaches 90% with increasing exposure dose, independent of the filler fraction. The geometric accuracy of the 3D printed specimens decreases with increasing exposure dose and with increasing filler volume fraction due to so-called profile broadening. Finally, we show that the average surface roughness of the 3D printed specimens decreases with increasing exposure dose and filler fraction. This work has implications for VP of photopolymer resins with high filler fraction.

Name thesis:degree_name

Master of Science

Level thesis:degree_level

masters

Discipline thesis:degree_discipline

Mechanical Engineering

Department dc:contributor.department

Mechanical Engineering

Grantor dc:publisher

Virginia Tech

Year dc:date.issued

2023

Author dc:creator

• Liang, Jingyu

Chair dc:contributor.committeechair

• Raeymaekers, Bart

Committee members dc:contributor.committeemember

• West, Robert L.
• Williams, Christopher Bryant

• Vat polymerization
• photopolymer
• glass microspheres
• filler material
• degree of cure
• curing depth
• surface roughness

Statement dc:rights

• Creative Commons Attribution-NonCommercial 4.0 International

Licence dc:rights.uri

• http://creativecommons.org/licenses/by-nc/4.0/

Language dc:language.iso

en

Dc Identifier Other

vt_gsexam:37782

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/115679