Effects of Surface Condition and Environmental Exposure on the Bond between CFRP and Steel

As the existing steel infrastructure inevitably continues to age and deteriorate, engineers are increasingly looking for innovative and effective methods for repairing and maintaining existing structures. Structural steel components can degrade due to the surrounding environmental conditions, and are susceptible to corrosion damage when exposed to aggressive environments and deicing salts. The conventional methods for repairing steel structures can be labor-intensive and time-consuming, and add considerable weight to the existing structure. One alternative is utilizing carbon fiber reinforced polymers (CFRP). Many studies have documented the ability of CFRPs to enhance the strength of existing structures. Furthermore, CFRP offers the benefits of being non-corrosive and having a high strength-to-weight ratio. Most studies on steel strengthening have focused on the bond behavior of CFRP to steels having a smooth surface condition, which are not representative of deteriorated structures in greater need of retrofitting. Further research has examined the durability of CFRP-steel bonds relative to environmental conditions that do not reflect the service life conditions for typical applications. In this work, a comprehensive study is conducted on the effects of the surface condition and environmental exposure on the bond between CFRP and steel. The influence of corrosion and simulated corrosion pitting is evaluated to determine whether structures with non-uniform surfaces are adequate for CFRP retrofits. In addition, the durability of CFRP-steel bonded systems is investigated through laboratory hygrothermal aging and in-situ environmental conditioning to multiple environments in Virginia. The research can be useful in the development of guidelines that will assist engineers determine if a CFRP retrofit solution is applicable in a given environmental setting and appropriate for the level of deterioration of the structure.

Name thesis:degree_name

Doctor of Philosophy

Level thesis:degree_level

doctoral

Discipline thesis:degree_discipline

Civil Engineering

Department dc:contributor.department

Civil and Environmental Engineering

Grantor dc:publisher

Virginia Tech

Year dc:date.issued

2023

Author dc:creator

• Yu-Shan, Abril Victoria

Chairs dc:contributor.committeechair

• Eatherton, Matthew R.
• Hebdon, Matthew Hardy

Committee members dc:contributor.committeemember

• Case, Scott W.
• Shakiba, Maryam

• CFRP
• Steel
• Corrosion
• Surface Roughness
• Environmental Exposure

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Language dc:language.iso

en

Dc Identifier Other

vt_gsexam:36033

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/113176