Preparation, Characterization, and Application of Molecular Ionic Composites for High Performance Batteries

A solid electrolyte is a crucial component of any solid state battery. Polymer gel electrolytes have received increasing attention in recent years due to their high ionic conductivity, flexibility, and improved safety. However, a general tradeoff usually exists between the mechanical properties and ionic conductivity in such materials. Molecular ionic composites (MICs) are a new type of rigid polymer gel electrolyte based on ionic liquids (ILs) and a double helical rigid-rod polyamide, poly(2,2′-disulfonyl-4,4′-benzidine terephthalamide) (PBDT). MICs have high ionic conductivity, high thermal and electrochemical stability, and widely tunable and high tensile modulus even at relatively low polymer content. MICs show great promise as solid electrolytes for solid state batteries. This dissertation describes the preparation and characterization of MIC electrolyte membranes. These transparent, flexible, and tough membranes are prepared through a convenient solvent casting process. A large variety of ILs, including both hydrophilic and hydrophobic examples, are suitable to prepare MIC electrolyte membranes by adjusting the solvents used in the casting process. The prepared membranes show a biphasic internal structure consisting of a PBDT-rich “bundle” phase and an IL-rich “puddle” (interconnected fluid) phase. Similar to the bulk MIC ingots prepared previously through an interfacial ion exchange process, the MIC membranes also have high ionic conductivity and tensile modulus at low polymer content. A MIC membrane composed of 1-butyl-1-methylpyrrolidinium bis(trifluoromethylsulfonyl)imide (Pyr₁₄TFSI), LiTFSI, and PBDT in a mass ratio of 8:1:1 is tested as a solid electrolyte for lithium metal batteries. This electrolyte membrane shows high ionic conductivity and high rigidity. The shear storage modulus of this MIC electrolyte membrane only decreases by 35% when heated to 200 °C from room temperature, suggesting great mechanical stability at high temperatures. The electrolyte membrane is successfully used as solid electrolyte for a Li/LiFePO₄ battery working over a large temperature range from 23 to 150 °C, and the discharge capacity retention of the cell is as high as 99% after 50 cycles at 150 °C. By replacing the IL in the MIC with a charge-neutral liquid, single-ion-conducting polymer gel electrolyte composed of PBDT and polyethylene glycol (PEG) oligomer are obtained. Similar to the MICs, these single-ion-conducting materials also have high Young’s modulus and biphasic internal structures. This study reveals that the counter ion (Li⁺ or Na⁺) of the PBDT has a major effect on both the ionic conductivity and modulus of the materials. Due to the stronger intermolecular interactions, LiPBDT-PEG demonstrates lower ionic conductivity but higher Young’s modulus. This dissertation also evaluates the viability of rigid PBDT as a polymer binder for electrodes. Aqueous solution-processed LiFePO₄ electrodes with only 3 wt% PBDT demonstrate stable cycling over 1000 cycles without obvious capacity decay, and the rate capacity of these aqueous solution-processed electrodes are comparable to the electrodes prepared with conventional poly(vinylidene difluoride) (PVDF) as the binder, suggesting PBDT can serve as a potential electrode binder for commercial applications.

Name thesis:degree_name

Doctor of Philosophy

Level thesis:degree_level

doctoral

Discipline thesis:degree_discipline

Macromolecular Science and Engineering

Department dc:contributor.department

Chemistry

Grantor dc:publisher

Virginia Tech

Year dc:date.issued

2021

Author dc:creator

• Yu, Deyang

Chair dc:contributor.committeechair

• Madsen, Louis A.

Committee members dc:contributor.committeemember

• Qiao, Rui
• Liu, Guoliang
• Schulz, Michael
• Lin, Feng

• polymer electrolyte
• ion gel
• solid state battery
• high temperature
• ionic liquid
• single-ion conducting
• electrode binder

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Dc Identifier Other

vt_gsexam:32763

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/106510