Formation of Ti₃Al and its embrittling effects on titanium-aluminum alloys

The formation of Ti₃Al and its embrittling characteristics have been investigated in Ti-Al binary alloys up to 9.0 weight percent aluminum. The investigating tools were optical metallography, the Brown-type stress corrosion test and the Charpy V-notch Impact test. Segregated microstructures resulting from annealing in the (α+β) region were found to be extremely difficult to homogenize below the α-transus and could possibly explain the two-phase regions reported by many investigators. Sea-water stress corrosion tests reveal that a Widmanstatten structure is susceptible to stress corrosion cracking after aging for two hours at 1100°F. Much longer annealing times are required to produce susceptibility in equiaxed α-grains resulting from annealing in the (α+β) region. Toughness is less affected as a result of aging a Widmanstatten structure than an equiaxed structure, although the reduction is significant in both cases.

Name thesis:degree_name

M.S.

Level thesis:degree_level

masters

Discipline thesis:degree_discipline

Metallurgical Engineering

Department dc:contributor.department

Metallurgical Engineering

Grantor dc:publisher

Virginia Polytechnic Institute

Year dc:date.issued

1967

Author dc:creator

• Brauer, Frank Edward

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Language dc:language.iso

en

Handle dc:identifier.uri

http://hdl.handle.net/10919/106209

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/106209