{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/106179"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/106179","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"Use of acoustic emission to study deformation of mild steel in hydrogen and nitrogen environments","abstract":"Acoustic emission activity resulting from plastic deformation of mild steel disks that were clamped and then pressurized from one side with either hydrogen or nitrogen was recorded and analyzed. It was found that during monotonic pressurization of disks in nitrogen gas, more cumulative counts were recorded than for similar disks pressurized in hydrogen gas. Possible signatures of the \"births\" of cracks were observed during hydrogen pressurization of disks that typically failed by leaking. The records of the nitrogen tests show very high energy and high count events occurring early in the deformation process. These events are believed to be the result of the breaking away of near-surface dislocations that had been pinned by nitrogen. The disks tested in nitrogen typically failed by bursting (ductile failure) while those tested in hydrogen typically failed by leaking (\"brittle\" failure).","abstract_html":"Acoustic emission activity resulting from plastic deformation of mild steel disks that were clamped and then pressurized from one side with either hydrogen or nitrogen was recorded and analyzed. It was found that during monotonic pressurization of disks in nitrogen gas, more cumulative counts were recorded than for similar disks pressurized in hydrogen gas. Possible signatures of the "births" of cracks were observed during hydrogen pressurization of disks that typically failed by leaking. The records of the nitrogen tests show very high energy and high count events occurring early in the deformation process. These events are believed to be the result of the breaking away of near-surface dislocations that had been pinned by nitrogen. The disks tested in nitrogen typically failed by bursting (ductile failure) while those tested in hydrogen typically failed by leaking ("brittle" failure).","abstract_has_math":false,"creators":["Fanning, John C."],"institution":"Virginia Polytechnic Institute and State University","degree_name":"M.S.","degree_level":"masters","degree_discipline":"Materials Engineering","degree_department":"Materials Engineering","school":null,"contributors":[],"advisors":[],"committee_chairs":[],"committee_members":[],"year":1987,"date_issued":"1987","date_published":"1987","updated_at":"2026-07-22T22:18:53Z","subjects":[],"languages":["en"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[]},"links":{"outbound_url":"http://hdl.handle.net/10919/106179","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.department","label":"Department","values":["Materials Engineering"]},{"key":"dc:creator","label":"Author","values":["Fanning, John C."]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2021-10-26T20:10:28Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2021-10-26T20:10:28Z"]},{"key":"dc:date.issued","label":"Date","values":["1987"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Polytechnic Institute and State University"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Materials Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["M.S."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/106179"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["Acoustic emission activity resulting from plastic deformation of mild steel disks that were clamped and then pressurized from one side with either hydrogen or nitrogen was recorded and analyzed. It was found that during monotonic pressurization of disks in nitrogen gas, more cumulative counts were recorded than for similar disks pressurized in hydrogen gas. Possible signatures of the \"births\" of cracks were observed during hydrogen pressurization of disks that typically failed by leaking. The records of the nitrogen tests show very high energy and high count events occurring early in the deformation process. These events are believed to be the result of the breaking away of near-surface dislocations that had been pinned by nitrogen. The disks tested in nitrogen typically failed by bursting (ductile failure) while those tested in hydrogen typically failed by leaking (\"brittle\" failure)."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["M.S."]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["Use of acoustic emission to study deformation of mild steel in hydrogen and nitrogen environments"]}]}],"canonical_facts":{"dc:contributor.department":["Materials Engineering"],"dc:creator":["Fanning, John C."],"dc:date.accessioned":["2021-10-26T20:10:28Z"],"dc:date.available":["2021-10-26T20:10:28Z"],"dc:date.issued":["1987"],"dc:description.abstract":["Acoustic emission activity resulting from plastic deformation of mild steel disks that were clamped and then pressurized from one side with either hydrogen or nitrogen was recorded and analyzed. It was found that during monotonic pressurization of disks in nitrogen gas, more cumulative counts were recorded than for similar disks pressurized in hydrogen gas. Possible signatures of the \"births\" of cracks were observed during hydrogen pressurization of disks that typically failed by leaking. The records of the nitrogen tests show very high energy and high count events occurring early in the deformation process. These events are believed to be the result of the breaking away of near-surface dislocations that had been pinned by nitrogen. The disks tested in nitrogen typically failed by bursting (ductile failure) while those tested in hydrogen typically failed by leaking (\"brittle\" failure)."],"dc:description.degree":["M.S."],"dc:format.mimetype":["application/pdf"],"dc:identifier.uri":["http://hdl.handle.net/10919/106179"],"dc:language.iso":["en"],"dc:publisher":["Virginia Polytechnic Institute and State University"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:title":["Use of acoustic emission to study deformation of mild steel in hydrogen and nitrogen environments"],"dc:type":["Thesis"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Materials Engineering"],"thesis:degree_level":["masters"],"thesis:degree_name":["M.S."],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:18:53Z"}