Non-Covalent Interactions in Polymeric Materials: From Ionomers to Polymer Blends

Conventional studies of ionomers have focused on ionomers bearing monovalent carboxylate or sulfonate pendant ions. There are relatively fewer studies on ionomers containing multivalent pendant ions, such as divalent phosphonate. In this dissertation, poly(ethylene terephthalate) (PET) and polystyrene ionomers with divalent phosphonate pendant ions have been synthesized, and the influence of divalent phosphonate pendant ions on the structure-morphology-property relationship has been compared to the ionomers with monovalent sulfonate pendant ions. The phosphonate groups generated a stronger physically crosslinked network in phosphonated ionomers as compared to sulfonated analogues. Higher plateau modulus, longer relaxation time, and significantly higher zero-shear viscosity were noted for phosphonated ionomers by a dynamic melt rheology study. Compared to the ionic aggregates generated from sulfonate groups, larger ionic aggregates with associated phosphonate groups have been observed. Furthermore, phosphonated ionomers displayed significantly higher glass transition temperatures than sulfonated ionomers. Ionomers have proven to be attractive, interfacially active compatibilizers for a number of polymer blend systems because of specific interactions that may develop between the ionic groups and complementary functional groups on other polar polymers within the blends. The successful compatibilization of polyester/polyamide blends (prepared by solution mixing and melt blending methods) using phosphonated PET ionomers as a minor-component compatibilizer has been demonstrated. The phase-separated polyamide domain dimension decreased with increasing mol % phosphonated monomers and this decrease was attributed to the specific interactions between the ionic phosphonate groups on the polyester ionomer and the amide linkages of polyamide. More importantly, the divalent phosphonate pendant ions are more effective at compatibilizing polyester/polyamide blends in comparison to the monovalent sulfonate pendant ions. Phosphonated PET ionomer-compatibilized polyester/polyamide blends required 6 times fewer ionic monomers to achieve domain dimension < 1 μm as compared to sulfonated PET-containing blends. Deep eutectic solvents (DES) have been reported to be the next generation solvents due to the superior biocompatibility, biodegradability, and sustainability as compared to ionic liquids. Two types of deep eutectic solvents, choline chloride : malic acid (ChCl:MA) and L-arginine : levulinic acid (Arg:LA), have been demonstrated as effective plasticizers for poly(vinyl alcohol) (PVOH) films. The plasticization effects on the properties of PVOH films were evidenced by lower crystallizability and improved film ductility. In addition, ChCl:MA deep eutectic solvent was more effective in plasticizing PVOH as compared to propylene glycol, one of the most widely studied alcohol-type plasticizers. From an applied perspective, DES-plasticized PVOH film is a promising candidate in the packaging market of heath-related products.

Name thesis:degree_name

Doctor of Philosophy

Level thesis:degree_level

doctoral

Discipline thesis:degree_discipline

Chemistry

Department dc:contributor.department

Chemistry

Grantor dc:publisher

Virginia Tech

Year dc:date.issued

2019

Author dc:creator

• Ju, Lin

Chair dc:contributor.committeechair

• Moore, Robert Bowen

Committee members dc:contributor.committeemember

• Long, Timothy E.
• Bortner, Michael J.
• Matson, John B.

• phosphonated ionomers
• compatibilization of polymer blends
• plasticization of poly(vinyl alcohol)
• deep eutectic solvent
• structure-morphology-property relationship

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Dc Identifier Other

vt_gsexam:22207

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/102651