{"id":{"repo_id":"vt","oai_identifier":"oai:vtechworks.lib.vt.edu:10919/101225"},"canonical_url":"https://search.dev.ndltd.org/etd/vt/oai:vtechworks.lib.vt.edu:10919/101225","repository":{"repo_id":"vt","name":"Virginia Tech","base_url":"https://vtechworks.lib.vt.edu/oai/request"},"display":{"title":"An investigation of friction and wear mechanisms in selected thermoplastics","abstract":"These studies developed from Scanning Electron Microscope (SEM) observations of abrasive wear of a polymer disk sliding against metal asperity models. The investigator was unable to observe actual particle formation but did identify elastic and plastic deformation of the polymer, and a debris buildup and extrusion process occurring at the leading edge of the asperity. On the assumption that this process could lead to a surface fatigue condition, pin-on-disk wear trials were completed using a spherical steel ball sliding on polycarbonate, rigid PVC, and ultra-high molecular weight polyethylene specimens in dry and lubricated conditions. A delay in debris formation was observed in the rigid PVC and polycarbonate dry sliding trials. In each case a higher rate of friction force increase coincided with debris formation. No debris was produced in the ultra-high molecular weight polyethylene dry sliding trials, and the friction force trace was flat. An SEM analysis of the polycarbonate and rigid PVC wear tracks revealed pitting consistent with the Delamination Theory of wear. The effect of the lubricants was to significantly alter the form of the friction force traces, but not to eliminate wear in rigid PVC and polycarbonate. The results of the investigation, particularly the delay in wear debris generation, indicated that a fatigue wear mechanism appeared to exist in dry metal pin-on-polymer disk sliding systems. A qualitative wear model was developed to relate the in-situ SEM observations and the results of the pin-on-disk trials.","abstract_html":"These studies developed from Scanning Electron Microscope (SEM) observations of abrasive wear of a polymer disk sliding against metal asperity models. The investigator was unable to observe actual particle formation but did identify elastic and plastic deformation of the polymer, and a debris buildup and extrusion process occurring at the leading edge of the asperity. On the assumption that this process could lead to a surface fatigue condition, pin-on-disk wear trials were completed using a spherical steel ball sliding on polycarbonate, rigid PVC, and ultra-high molecular weight polyethylene specimens in dry and lubricated conditions. A delay in debris formation was observed in the rigid PVC and polycarbonate dry sliding trials. In each case a higher rate of friction force increase coincided with debris formation. No debris was produced in the ultra-high molecular weight polyethylene dry sliding trials, and the friction force trace was flat. An SEM analysis of the polycarbonate and rigid PVC wear tracks revealed pitting consistent with the Delamination Theory of wear. The effect of the lubricants was to significantly alter the form of the friction force traces, but not to eliminate wear in rigid PVC and polycarbonate. The results of the investigation, particularly the delay in wear debris generation, indicated that a fatigue wear mechanism appeared to exist in dry metal pin-on-polymer disk sliding systems. A qualitative wear model was developed to relate the in-situ SEM observations and the results of the pin-on-disk trials.","abstract_has_math":false,"creators":["Potter, Joseph R."],"institution":"Virginia Polytechnic Institute and State University","degree_name":"M.S.","degree_level":"masters","degree_discipline":"Mechanical Engineering","degree_department":"Mechanical Engineering","school":null,"contributors":[],"advisors":[],"committee_chairs":[],"committee_members":[],"year":1983,"date_issued":"1983","date_published":"1983","updated_at":"2026-07-22T22:20:05Z","subjects":[],"languages":["en"],"rights":["In Copyright"],"rights_urls":["http://rightsstatements.org/vocab/InC/1.0/"],"identifier_entries":[]},"links":{"outbound_url":"http://hdl.handle.net/10919/101225","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.department","label":"Department","values":["Mechanical Engineering"]},{"key":"dc:creator","label":"Author","values":["Potter, Joseph R."]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2020-12-14T16:34:54Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2020-12-14T16:34:54Z"]},{"key":"dc:date.issued","label":"Date","values":["1983"]},{"key":"dc:publisher","label":"Institution","values":["Virginia Polytechnic Institute and State University"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"dc:type.dcmitype","label":"Dc Type Dcmitype","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Mechanical Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["M.S."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Virginia Polytechnic Institute and State University"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["In Copyright"]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/10919/101225"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["These studies developed from Scanning Electron Microscope (SEM) observations of abrasive wear of a polymer disk sliding against metal asperity models. The investigator was unable to observe actual particle formation but did identify elastic and plastic deformation of the polymer, and a debris buildup and extrusion process occurring at the leading edge of the asperity. On the assumption that this process could lead to a surface fatigue condition, pin-on-disk wear trials were completed using a spherical steel ball sliding on polycarbonate, rigid PVC, and ultra-high molecular weight polyethylene specimens in dry and lubricated conditions. A delay in debris formation was observed in the rigid PVC and polycarbonate dry sliding trials. In each case a higher rate of friction force increase coincided with debris formation. No debris was produced in the ultra-high molecular weight polyethylene dry sliding trials, and the friction force trace was flat. An SEM analysis of the polycarbonate and rigid PVC wear tracks revealed pitting consistent with the Delamination Theory of wear. The effect of the lubricants was to significantly alter the form of the friction force traces, but not to eliminate wear in rigid PVC and polycarbonate. The results of the investigation, particularly the delay in wear debris generation, indicated that a fatigue wear mechanism appeared to exist in dry metal pin-on-polymer disk sliding systems. A qualitative wear model was developed to relate the in-situ SEM observations and the results of the pin-on-disk trials."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["M.S."]},{"key":"dc:format.mimetype","label":"Dc Format Mimetype","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["An investigation of friction and wear mechanisms in selected thermoplastics"]}]}],"canonical_facts":{"dc:contributor.department":["Mechanical Engineering"],"dc:creator":["Potter, Joseph R."],"dc:date.accessioned":["2020-12-14T16:34:54Z"],"dc:date.available":["2020-12-14T16:34:54Z"],"dc:date.issued":["1983"],"dc:description.abstract":["These studies developed from Scanning Electron Microscope (SEM) observations of abrasive wear of a polymer disk sliding against metal asperity models. The investigator was unable to observe actual particle formation but did identify elastic and plastic deformation of the polymer, and a debris buildup and extrusion process occurring at the leading edge of the asperity. On the assumption that this process could lead to a surface fatigue condition, pin-on-disk wear trials were completed using a spherical steel ball sliding on polycarbonate, rigid PVC, and ultra-high molecular weight polyethylene specimens in dry and lubricated conditions. A delay in debris formation was observed in the rigid PVC and polycarbonate dry sliding trials. In each case a higher rate of friction force increase coincided with debris formation. No debris was produced in the ultra-high molecular weight polyethylene dry sliding trials, and the friction force trace was flat. An SEM analysis of the polycarbonate and rigid PVC wear tracks revealed pitting consistent with the Delamination Theory of wear. The effect of the lubricants was to significantly alter the form of the friction force traces, but not to eliminate wear in rigid PVC and polycarbonate. The results of the investigation, particularly the delay in wear debris generation, indicated that a fatigue wear mechanism appeared to exist in dry metal pin-on-polymer disk sliding systems. A qualitative wear model was developed to relate the in-situ SEM observations and the results of the pin-on-disk trials."],"dc:description.degree":["M.S."],"dc:format.mimetype":["application/pdf"],"dc:identifier.uri":["http://hdl.handle.net/10919/101225"],"dc:language.iso":["en"],"dc:publisher":["Virginia Polytechnic Institute and State University"],"dc:rights":["In Copyright"],"dc:rights.uri":["http://rightsstatements.org/vocab/InC/1.0/"],"dc:title":["An investigation of friction and wear mechanisms in selected thermoplastics"],"dc:type":["Thesis"],"dc:type.dcmitype":["Text"],"thesis:degree_discipline":["Mechanical Engineering"],"thesis:degree_level":["masters"],"thesis:degree_name":["M.S."],"thesis:institution_name":["Virginia Polytechnic Institute and State University"]},"updated_at":"2026-07-22T22:20:05Z"}