A Novel Process for GeSi Thin Film Synthesis

A unique process of fabricating a strained layer GexSi1-x on insulator is demonstrated. Such strained heterostructures are useful in the fabrication of high-mobility transistors. This technique incorporates well-established silicon processing technology e.g., ion implantation and thermal oxidation. A dilute GeSi layer is initially formed by implanting Ge+ into a silicon-on-insulator (SOI) substrate. Thermal oxidation segregates the Ge at the growing oxide interface to form a distinct GexSi1-x thin-film with a composition that can be tailored by controlling the oxidation parameters (e.g. temperature and oxidation ambient). In addition, the film thickness can be controlled by implantation fluence, which is important since the film forms pseudomorphically below 2×1016 Ge/cm2. Continued oxidation consumes the underlying Si leaving the strained GeSi film encapsulated by the two oxide layers, i.e. the top thermal oxide and the buried oxide. Removal of the thermal oxide by a dilute HF etch completes the process. Strain relaxation can be achieved by either of two methods. One involves vacancy injection by ion implantation to introduce sufficient open-volume within the film to compensate for the compressive strain. The other depends upon the formation of GeO2. If Ge is oxidized in the absence of Si, it evaporates as GeO(g) resulting in spontaneous relaxation within the strained film. Conditions under which this occurs have been discussed along with elaborated results of oxidation kinetics of Ge-ion implanted silicon. Rutherford backscattering spectrometry (RBS), ion channeling, Raman spectroscopy and scanning electron microscopy (SEM) were used as the characterization techniques.

Grantor dc:publisher

University of North Texas

Year dc:date

2007

Author dc:creator

• Hossain, Khalid

Contributors dc:contributor

• McDaniel, Floyd D.
• Holland, Orin Wayne
• Duggan, Jerome L.
• Weathers, Duncan L.
• Golding, Terry

• succession planning
• ion implantation
• oxidation kinetics
• scanning electron microscopy
• Thin films.
• Ion implantation.
• Silicon oxide.

Statement dc:rights

• Public
• Copyright
• Hossain, Khalid
• Copyright is held by the author, unless otherwise noted. All rights reserved.

Language dc:language

English

Identifier

oclc: 229356919
https://digital.library.unt.edu/ark:/67531/metadc5167/
ark: ark:/67531/metadc5167

OAI identifier oai:identifier

info:ark/67531/metadc5167