Well-aligned DMS Zn1-xMnxO nanowires and nanorods were successfully synthesized in-situ using a chemical vapor deposition method. Low-dimensional nanostructures such as bowls and cages were deposited on a silicon surface downstream of the tube furnace. Variation of reaction temperature and Mn doping level were investigated on structure and properties of the as-grown nanomaterials. The as-grown nanowires and naorods are single crystalline wurtzite structure and possess a growth direction along the c axis. At 850 ºC, the most optimistic condition for ZnO crystal growth was obtained. At high reaction temperature 950ºC, Mn2+ were substitutionally doped into ZnO lattice, resulting in room-temperature ferromagnetic coupling with a saturated magnetization of 0.25emu/g. The ferromagnetic interaction is weakened, however, by larger concentration of Mn, due to the antiferromagnetic coupling of direct superexchange interaction between Mn2+. The well-aligned DMS 1-dimensional Mn doped ZnO nanostructures have great potential for application in spintronic nanodevices.
","abstract_html":"<p>Well-aligned DMS Zn1-xMnxO nanowires and nanorods were successfully synthesized in-situ using a chemical vapor deposition method. Low-dimensional nanostructures such as bowls and cages were deposited on a silicon surface downstream of the tube furnace. Variation of reaction temperature and Mn doping level were investigated on structure and properties of the as-grown nanomaterials. The as-grown nanowires and naorods are single crystalline wurtzite structure and possess a growth direction along the c axis. At 850 ºC, the most optimistic condition for ZnO crystal growth was obtained. At high reaction temperature 950ºC, Mn2+ were substitutionally doped into ZnO lattice, resulting in room-temperature ferromagnetic coupling with a saturated magnetization of 0.25emu/g. The ferromagnetic interaction is weakened, however, by larger concentration of Mn, due to the antiferromagnetic coupling of direct superexchange interaction between Mn2+. The well-aligned DMS 1-dimensional Mn doped ZnO nanostructures have great potential for application in spintronic nanodevices.</p>","abstract_has_math":false,"creators":["Liu, Jingjing"],"institution":null,"degree_name":"M.S.","degree_level":"Thesis","degree_discipline":"Physics","degree_department":null,"school":null,"contributors":["Zhou, Weilie; Stokes, Kevin","Tang, Jinke"],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2006,"date_issued":"2006-08-09T07:00:00Z","date_published":"2006-08-09T07:00:00Z","updated_at":"2026-07-24T05:28:16Z","subjects":[],"languages":[],"rights":[],"rights_urls":[],"identifier_entries":[]},"links":{"outbound_url":"https://scholarworks.uno.edu/td/426","outbound_label":"Repository record","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor","label":"Contributor","values":["Zhou, Weilie; Stokes, Kevin","Tang, Jinke"]},{"key":"dc:creator","label":"Author","values":["Liu, Jingjing"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"thesis:degree_discipline","label":"Discipline","values":["Physics"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Thesis"]},{"key":"thesis:degree_name","label":"Degree Name","values":["M.S."]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["https://scholarworks.uno.edu/td/426"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["Well-aligned DMS Zn1-xMnxO nanowires and nanorods were successfully synthesized in-situ using a chemical vapor deposition method. Low-dimensional nanostructures such as bowls and cages were deposited on a silicon surface downstream of the tube furnace. Variation of reaction temperature and Mn doping level were investigated on structure and properties of the as-grown nanomaterials. The as-grown nanowires and naorods are single crystalline wurtzite structure and possess a growth direction along the c axis. At 850 ºC, the most optimistic condition for ZnO crystal growth was obtained. At high reaction temperature 950ºC, Mn2+ were substitutionally doped into ZnO lattice, resulting in room-temperature ferromagnetic coupling with a saturated magnetization of 0.25emu/g. The ferromagnetic interaction is weakened, however, by larger concentration of Mn, due to the antiferromagnetic coupling of direct superexchange interaction between Mn2+. The well-aligned DMS 1-dimensional Mn doped ZnO nanostructures have great potential for application in spintronic nanodevices.
"]},{"key":"dc:title","label":"Title","values":["Diluted Magnetic Semiconductor Nanomaterials Fabrication by a Chemical Vapor Deposition Method"]}]}],"canonical_facts":{"dc:contributor":["Zhou, Weilie; Stokes, Kevin","Tang, Jinke"],"dc:creator":["Liu, Jingjing"],"dc:description.abstract":["Well-aligned DMS Zn1-xMnxO nanowires and nanorods were successfully synthesized in-situ using a chemical vapor deposition method. Low-dimensional nanostructures such as bowls and cages were deposited on a silicon surface downstream of the tube furnace. Variation of reaction temperature and Mn doping level were investigated on structure and properties of the as-grown nanomaterials. The as-grown nanowires and naorods are single crystalline wurtzite structure and possess a growth direction along the c axis. At 850 ºC, the most optimistic condition for ZnO crystal growth was obtained. At high reaction temperature 950ºC, Mn2+ were substitutionally doped into ZnO lattice, resulting in room-temperature ferromagnetic coupling with a saturated magnetization of 0.25emu/g. The ferromagnetic interaction is weakened, however, by larger concentration of Mn, due to the antiferromagnetic coupling of direct superexchange interaction between Mn2+. The well-aligned DMS 1-dimensional Mn doped ZnO nanostructures have great potential for application in spintronic nanodevices.
"],"dc:identifier":["https://scholarworks.uno.edu/td/426"],"dc:title":["Diluted Magnetic Semiconductor Nanomaterials Fabrication by a Chemical Vapor Deposition Method"],"thesis:degree_discipline":["Physics"],"thesis:degree_level":["Thesis"],"thesis:degree_name":["M.S."]},"updated_at":"2026-07-24T05:28:16Z"}