{"id":{"repo_id":"unm","oai_identifier":"oai:digitalrepository.unm.edu:ce_etds-1066"},"canonical_url":"https://search.dev.ndltd.org/etd/unm/oai:digitalrepository.unm.edu:ce_etds-1066","repository":{"repo_id":"unm","name":"University of New Mexico","base_url":"https://digitalrepository.unm.edu/do/oai/"},"display":{"title":"Predicting failure behavior of polymeric and asphalt composites using damage models","abstract":"This study investigates the failure behavior of two types of composite materials using damage models within the framework of ABAQUS finite element software. The failure behavior of an IM7/977-2 carbon epoxy composite material subjected to a Mode I delamination is predicted using traction-separation and bulk material damage models that are based on disturbed state concept (DSC) principles. The models were validated by comparing the results to referenced laboratory testing performed on IM7/977-2 carbon epoxy composite. The damaged states associated with various stages of loading are presented in this study. This study also predicts the failure behavior of asphalt materials through the use of damage models using the principles of the DSC. Traction-separation crack response, damage initiation and damage evolution behavior are investigated by modeling pavement systems consisting of a hot mix asphalt (HMA) overlay above an existing HMA layer and subjected to an applied static wheel loading. Preexisting cracks located within the existing asphalt material are also considered. The extended finite element method (XFEM) was employed to model mesh-independent cracking. The finite element model was validated by comparing the results to indirect tensile laboratory testing and referenced direct tensile laboratory data-based results performed on asphalt samples. The validated model was then used to examine damage in a pavement system with and without preexisting cracks.","abstract_html":"This study investigates the failure behavior of two types of composite materials using damage models within the framework of ABAQUS finite element software. The failure behavior of an IM7/977-2 carbon epoxy composite material subjected to a Mode I delamination is predicted using traction-separation and bulk material damage models that are based on disturbed state concept (DSC) principles. The models were validated by comparing the results to referenced laboratory testing performed on IM7/977-2 carbon epoxy composite. The damaged states associated with various stages of loading are presented in this study. This study also predicts the failure behavior of asphalt materials through the use of damage models using the principles of the DSC. Traction-separation crack response, damage initiation and damage evolution behavior are investigated by modeling pavement systems consisting of a hot mix asphalt (HMA) overlay above an existing HMA layer and subjected to an applied static wheel loading. Preexisting cracks located within the existing asphalt material are also considered. The extended finite element method (XFEM) was employed to model mesh-independent cracking. The finite element model was validated by comparing the results to indirect tensile laboratory testing and referenced direct tensile laboratory data-based results performed on asphalt samples. The validated model was then used to examine damage in a pavement system with and without preexisting cracks.","abstract_has_math":false,"creators":["Vallejo, Meghan"],"institution":null,"degree_name":"Civil Engineering","degree_level":"Thesis","degree_discipline":"Civil Engineering","degree_department":null,"school":null,"contributors":["Tarefder, Rafiqul","Ng, Tang-Tat","Maji, Arup"],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2012,"date_issued":"2012-07-03T07:00:00Z","date_published":"2012-07-03T07:00:00Z","updated_at":"2026-07-24T05:26:55Z","subjects":["Polymeric composites--Fatigue--Computer simulation","Composite materials--Delamination--Computer simulation","Pavements","Asphalt--Cracking--Computer simulation","Pavements--Overlays--Cracking--Computer simulation","Finite element method."],"languages":["English"],"rights":[],"rights_urls":[],"identifier_entries":[{"key":"dc:identifier","label":"Identifier","values":["https://digitalrepository.unm.edu/ce_etds/65"],"render_values":[{"text":"https://digitalrepository.unm.edu/ce_etds/65","href":"https://digitalrepository.unm.edu/ce_etds/65","code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/1928/20793","outbound_label":"Handle","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor","label":"Contributor","values":["Tarefder, Rafiqul","Ng, Tang-Tat","Maji, Arup"]},{"key":"dc:creator","label":"Author","values":["Vallejo, Meghan"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"thesis:degree_discipline","label":"Discipline","values":["Civil Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Thesis","Masters"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Civil Engineering"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Polymeric composites--Fatigue--Computer simulation","Composite materials--Delamination--Computer simulation","Pavements","Asphalt--Cracking--Computer simulation","Pavements--Overlays--Cracking--Computer simulation","Finite element method."]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["English"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["http://hdl.handle.net/1928/20793","https://digitalrepository.unm.edu/ce_etds/65"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["This study investigates the failure behavior of two types of composite materials using damage models within the framework of ABAQUS finite element software. The failure behavior of an IM7/977-2 carbon epoxy composite material subjected to a Mode I delamination is predicted using traction-separation and bulk material damage models that are based on disturbed state concept (DSC) principles. The models were validated by comparing the results to referenced laboratory testing performed on IM7/977-2 carbon epoxy composite. The damaged states associated with various stages of loading are presented in this study. This study also predicts the failure behavior of asphalt materials through the use of damage models using the principles of the DSC. Traction-separation crack response, damage initiation and damage evolution behavior are investigated by modeling pavement systems consisting of a hot mix asphalt (HMA) overlay above an existing HMA layer and subjected to an applied static wheel loading. Preexisting cracks located within the existing asphalt material are also considered. The extended finite element method (XFEM) was employed to model mesh-independent cracking. The finite element model was validated by comparing the results to indirect tensile laboratory testing and referenced direct tensile laboratory data-based results performed on asphalt samples. The validated model was then used to examine damage in a pavement system with and without preexisting cracks."]},{"key":"dc:title","label":"Title","values":["Predicting failure behavior of polymeric and asphalt composites using damage models"]}]}],"canonical_facts":{"dc:contributor":["Tarefder, Rafiqul","Ng, Tang-Tat","Maji, Arup"],"dc:creator":["Vallejo, Meghan"],"dc:description.abstract":["This study investigates the failure behavior of two types of composite materials using damage models within the framework of ABAQUS finite element software. The failure behavior of an IM7/977-2 carbon epoxy composite material subjected to a Mode I delamination is predicted using traction-separation and bulk material damage models that are based on disturbed state concept (DSC) principles. The models were validated by comparing the results to referenced laboratory testing performed on IM7/977-2 carbon epoxy composite. The damaged states associated with various stages of loading are presented in this study. This study also predicts the failure behavior of asphalt materials through the use of damage models using the principles of the DSC. Traction-separation crack response, damage initiation and damage evolution behavior are investigated by modeling pavement systems consisting of a hot mix asphalt (HMA) overlay above an existing HMA layer and subjected to an applied static wheel loading. Preexisting cracks located within the existing asphalt material are also considered. The extended finite element method (XFEM) was employed to model mesh-independent cracking. The finite element model was validated by comparing the results to indirect tensile laboratory testing and referenced direct tensile laboratory data-based results performed on asphalt samples. The validated model was then used to examine damage in a pavement system with and without preexisting cracks."],"dc:identifier":["http://hdl.handle.net/1928/20793","https://digitalrepository.unm.edu/ce_etds/65"],"dc:language":["English"],"dc:subject":["Polymeric composites--Fatigue--Computer simulation","Composite materials--Delamination--Computer simulation","Pavements","Asphalt--Cracking--Computer simulation","Pavements--Overlays--Cracking--Computer simulation","Finite element method."],"dc:title":["Predicting failure behavior of polymeric and asphalt composites using damage models"],"thesis:degree_discipline":["Civil Engineering"],"thesis:degree_level":["Thesis","Masters"],"thesis:degree_name":["Civil Engineering"]},"updated_at":"2026-07-24T05:26:55Z"}