{"id":{"repo_id":"unlv","oai_identifier":"oai:oasis.library.unlv.edu:rtds-2231"},"canonical_url":"https://search.dev.ndltd.org/etd/unlv/oai:oasis.library.unlv.edu:rtds-2231","repository":{"repo_id":"unlv","name":"University of Nevada - Las Vegas","base_url":"https://oasis.library.unlv.edu/do/oai/"},"display":{"title":"Cobalt silicide characterization","abstract":"Decreasing feature sizes of advanced ULSI (Ultra large-scale integrated) devices are driven by a desire for improve device performance and an increase in the number of devices on a single wafer. Small feature sizes cause increased resistance, which leads to degraded device performances. Silicides can reduce sheet resistance on poly-silicon lines and shallow junctions. The mostly widely accepted silicide process, Titanium Silicide (TiSi2), was adopted because of its low resistivity. Major limitations of TiSi2 include an inability to form on narrow poly-lines and gate shorting. Cobalt silicide is an alternative to TiSi2 due to its scalability (down to 0.065 mum 2) while providing acceptable sheet resistance, better heat cycle immunity, and good junction leakage characteristics; Key factors to be considered for a silicide process are: junction leakage currents, film uniformity, junction spiking, void formation, sheet resistivity, thermal stability, and agglomeration. There are four process variables in this study: the first rapid thermal anneal (RTA) temperature and ramp rate, the Co and TiN removal time, and the second RTA temperature. (Abstract shortened by UMI.).","abstract_html":"Decreasing feature sizes of advanced ULSI (Ultra large-scale integrated) devices are driven by a desire for improve device performance and an increase in the number of devices on a single wafer. Small feature sizes cause increased resistance, which leads to degraded device performances. Silicides can reduce sheet resistance on poly-silicon lines and shallow junctions. The mostly widely accepted silicide process, Titanium Silicide (TiSi2), was adopted because of its low resistivity. Major limitations of TiSi2 include an inability to form on narrow poly-lines and gate shorting. Cobalt silicide is an alternative to TiSi2 due to its scalability (down to 0.065 mum 2) while providing acceptable sheet resistance, better heat cycle immunity, and good junction leakage characteristics; Key factors to be considered for a silicide process are: junction leakage currents, film uniformity, junction spiking, void formation, sheet resistivity, thermal stability, and agglomeration. There are four process variables in this study: the first rapid thermal anneal (RTA) temperature and ramp rate, the Co and TiN removal time, and the second RTA temperature. (Abstract shortened by UMI.).","abstract_has_math":false,"creators":["Alldredge, Donovan"],"institution":"University of Nevada, Las Vegas","degree_name":"Master of Science (MS)","degree_level":"Thesis","degree_discipline":"Electrical Engineering","degree_department":null,"school":null,"contributors":["Rama Venkat"],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2000,"date_issued":"2000-01-01T08:00:00Z","date_published":"2000-01-01T08:00:00Z","updated_at":"2026-07-24T05:25:18Z","subjects":[],"languages":["English"],"rights":["IN COPYRIGHT. For more information about this rights statement, please visit http://rightsstatements.org/vocab/InC/1.0/"],"rights_urls":[],"identifier_entries":[{"key":"dc:identifier","label":"Identifier","values":["https://oasis.library.unlv.edu/rtds/1232"],"render_values":[{"text":"https://oasis.library.unlv.edu/rtds/1232","href":"https://oasis.library.unlv.edu/rtds/1232","code":true}]}]},"links":{"outbound_url":"https://doi.org/10.25669/tmpc-27ba","outbound_label":"DOI","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor","label":"Contributor","values":["Rama Venkat"]},{"key":"dc:creator","label":"Author","values":["Alldredge, Donovan"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:publisher","label":"Institution","values":["University of Nevada, Las Vegas"]},{"key":"dc:type","label":"Dc Type","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Electrical Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Thesis"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science (MS)"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["English"]},{"key":"dc:rights","label":"Dc Rights","values":["IN COPYRIGHT. For more information about this rights statement, please visit http://rightsstatements.org/vocab/InC/1.0/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["10.25669/tmpc-27ba","https://oasis.library.unlv.edu/rtds/1232","https://oasis.library.unlv.edu/context/rtds/article/2231/viewcontent/uc.pdf"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["Decreasing feature sizes of advanced ULSI (Ultra large-scale integrated) devices are driven by a desire for improve device performance and an increase in the number of devices on a single wafer. Small feature sizes cause increased resistance, which leads to degraded device performances. Silicides can reduce sheet resistance on poly-silicon lines and shallow junctions. The mostly widely accepted silicide process, Titanium Silicide (TiSi2), was adopted because of its low resistivity. Major limitations of TiSi2 include an inability to form on narrow poly-lines and gate shorting. Cobalt silicide is an alternative to TiSi2 due to its scalability (down to 0.065 mum 2) while providing acceptable sheet resistance, better heat cycle immunity, and good junction leakage characteristics; Key factors to be considered for a silicide process are: junction leakage currents, film uniformity, junction spiking, void formation, sheet resistivity, thermal stability, and agglomeration. There are four process variables in this study: the first rapid thermal anneal (RTA) temperature and ramp rate, the Co and TiN removal time, and the second RTA temperature. (Abstract shortened by UMI.)."]},{"key":"dc:format","label":"Dc Format","values":["pdf"]},{"key":"dc:title","label":"Title","values":["Cobalt silicide characterization"]}]}],"canonical_facts":{"dc:contributor":["Rama Venkat"],"dc:creator":["Alldredge, Donovan"],"dc:description.abstract":["Decreasing feature sizes of advanced ULSI (Ultra large-scale integrated) devices are driven by a desire for improve device performance and an increase in the number of devices on a single wafer. Small feature sizes cause increased resistance, which leads to degraded device performances. Silicides can reduce sheet resistance on poly-silicon lines and shallow junctions. The mostly widely accepted silicide process, Titanium Silicide (TiSi2), was adopted because of its low resistivity. Major limitations of TiSi2 include an inability to form on narrow poly-lines and gate shorting. Cobalt silicide is an alternative to TiSi2 due to its scalability (down to 0.065 mum 2) while providing acceptable sheet resistance, better heat cycle immunity, and good junction leakage characteristics; Key factors to be considered for a silicide process are: junction leakage currents, film uniformity, junction spiking, void formation, sheet resistivity, thermal stability, and agglomeration. There are four process variables in this study: the first rapid thermal anneal (RTA) temperature and ramp rate, the Co and TiN removal time, and the second RTA temperature. (Abstract shortened by UMI.)."],"dc:format":["pdf"],"dc:identifier":["10.25669/tmpc-27ba","https://oasis.library.unlv.edu/rtds/1232","https://oasis.library.unlv.edu/context/rtds/article/2231/viewcontent/uc.pdf"],"dc:language":["English"],"dc:publisher":["University of Nevada, Las Vegas"],"dc:rights":["IN COPYRIGHT. For more information about this rights statement, please visit http://rightsstatements.org/vocab/InC/1.0/"],"dc:title":["Cobalt silicide characterization"],"dc:type":["Text"],"thesis:degree_discipline":["Electrical Engineering"],"thesis:degree_level":["Thesis"],"thesis:degree_name":["Master of Science (MS)"]},"updated_at":"2026-07-24T05:25:18Z"}