{"id":{"repo_id":"unf","oai_identifier":"oai:digitalcommons.unf.edu:etd-1553"},"canonical_url":"https://search.dev.ndltd.org/etd/unf/oai:digitalcommons.unf.edu:etd-1553","repository":{"repo_id":"unf","name":"University of North Florida","base_url":"https://digitalcommons.unf.edu/do/oai/"},"display":{"title":"The Effect of Surface Corrosion Damage on the Fatigue Life of Extruded Aluminum Alloy 6061-T6","abstract":"Aluminum alloy 6061-T6 is a common engineering material used in aerospace, automotive, structural applications. Despite its wide use, little has been published about the effects of damage from surface corrosion on its fatigue life. An investigation was performed where 6061-T6 extrusions were exposed to a 3.5% NaCl solution at pH 2 for 2 days and 24 days. The length of time and pH were chosen in order to create distinct surface flaws. The effect of these flaws on the fatigue life was then investigated and analyzed using scanning electron microscopy (SEM) and Weibull statistics. It was determined that samples corroded for both 2-days and 24-days exhibit fatigue lives that can be described using a 3-parameter Weibull distribution. The result of which was the determination of a threshold value for fatigue as well a general understanding of flaw geometry.","abstract_html":"Aluminum alloy 6061-T6 is a common engineering material used in aerospace, automotive, structural applications. Despite its wide use, little has been published about the effects of damage from surface corrosion on its fatigue life. An investigation was performed where 6061-T6 extrusions were exposed to a 3.5% NaCl solution at pH 2 for 2 days and 24 days. The length of time and pH were chosen in order to create distinct surface flaws. The effect of these flaws on the fatigue life was then investigated and analyzed using scanning electron microscopy (SEM) and Weibull statistics. It was determined that samples corroded for both 2-days and 24-days exhibit fatigue lives that can be described using a 3-parameter Weibull distribution. The result of which was the determination of a threshold value for fatigue as well a general understanding of flaw geometry.","abstract_has_math":false,"creators":["Weber, Matthew"],"institution":"UNF Digital Commons","degree_name":null,"degree_level":null,"degree_discipline":null,"degree_department":null,"school":null,"contributors":[],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2014,"date_issued":"2014-01-01T08:00:00Z","date_published":"2014-01-01T08:00:00Z","updated_at":"2026-07-24T05:21:49Z","subjects":["Thesis; University of North Florida; UNF; Dissertations; Academic -- UNF -- Master of Science in Mechanical Engineering; Dissertations; Academic -- UNF -- Engineering; Corrosion; Fatigue; Aluminum Alloy 6061-T6","Other Mechanical Engineering","Structural Materials"],"languages":[],"rights":[],"rights_urls":[],"identifier_entries":[]},"links":{"outbound_url":"https://digitalcommons.unf.edu/etd/524","outbound_label":"Repository record","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:creator","label":"Author","values":["Weber, Matthew"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date","label":"Dc Date","values":["2014-01-01T08:00:00Z"]},{"key":"dc:publisher","label":"Institution","values":["UNF Digital Commons"]},{"key":"dc:type","label":"Dc Type","values":["thesis"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Thesis; University of North Florida; UNF; Dissertations; Academic -- UNF -- Master of Science in Mechanical Engineering; Dissertations; Academic -- UNF -- Engineering; Corrosion; Fatigue; Aluminum Alloy 6061-T6","Other Mechanical Engineering","Structural Materials"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["https://digitalcommons.unf.edu/etd/524","https://digitalcommons.unf.edu/context/etd/article/1553/viewcontent/ETD1195PA.pdf"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["Aluminum alloy 6061-T6 is a common engineering material used in aerospace, automotive, structural applications. Despite its wide use, little has been published about the effects of damage from surface corrosion on its fatigue life. An investigation was performed where 6061-T6 extrusions were exposed to a 3.5% NaCl solution at pH 2 for 2 days and 24 days. The length of time and pH were chosen in order to create distinct surface flaws. The effect of these flaws on the fatigue life was then investigated and analyzed using scanning electron microscopy (SEM) and Weibull statistics. It was determined that samples corroded for both 2-days and 24-days exhibit fatigue lives that can be described using a 3-parameter Weibull distribution. The result of which was the determination of a threshold value for fatigue as well a general understanding of flaw geometry."]},{"key":"dc:format","label":"Dc Format","values":["application/pdf"]},{"key":"dc:source","label":"Dc Source","values":["UNF Graduate Theses and Dissertations"]},{"key":"dc:title","label":"Title","values":["The Effect of Surface Corrosion Damage on the Fatigue Life of Extruded Aluminum Alloy 6061-T6"]}]}],"canonical_facts":{"dc:creator":["Weber, Matthew"],"dc:date":["2014-01-01T08:00:00Z"],"dc:description":["Aluminum alloy 6061-T6 is a common engineering material used in aerospace, automotive, structural applications. Despite its wide use, little has been published about the effects of damage from surface corrosion on its fatigue life. An investigation was performed where 6061-T6 extrusions were exposed to a 3.5% NaCl solution at pH 2 for 2 days and 24 days. The length of time and pH were chosen in order to create distinct surface flaws. The effect of these flaws on the fatigue life was then investigated and analyzed using scanning electron microscopy (SEM) and Weibull statistics. It was determined that samples corroded for both 2-days and 24-days exhibit fatigue lives that can be described using a 3-parameter Weibull distribution. The result of which was the determination of a threshold value for fatigue as well a general understanding of flaw geometry."],"dc:format":["application/pdf"],"dc:identifier":["https://digitalcommons.unf.edu/etd/524","https://digitalcommons.unf.edu/context/etd/article/1553/viewcontent/ETD1195PA.pdf"],"dc:publisher":["UNF Digital Commons"],"dc:source":["UNF Graduate Theses and Dissertations"],"dc:subject":["Thesis; University of North Florida; UNF; Dissertations; Academic -- UNF -- Master of Science in Mechanical Engineering; Dissertations; Academic -- UNF -- Engineering; Corrosion; Fatigue; Aluminum Alloy 6061-T6","Other Mechanical Engineering","Structural Materials"],"dc:title":["The Effect of Surface Corrosion Damage on the Fatigue Life of Extruded Aluminum Alloy 6061-T6"],"dc:type":["thesis"]},"updated_at":"2026-07-24T05:21:49Z"}