{"id":{"repo_id":"uiuc","oai_identifier":"oai:www.ideals.illinois.edu:2142/85933"},"canonical_url":"https://search.dev.ndltd.org/etd/uiuc/oai:www.ideals.illinois.edu:2142/85933","repository":{"repo_id":"uiuc","name":"University of Illinois - Urbana-Champaign","base_url":"https://www.ideals.illinois.edu/oai-pmh"},"display":{"title":"The Influence of Defect-Solute Interactions on Segregation of Au Implanted Into Binary Ni Alloys at Elevated Temperatures","abstract":"The diffusion behavior of solutes under irradiation in a Ni matrix have been investigated. The behavior of the solutes Si, Be, Ge, and Al were studied by directing a 300 keV Au$\\sp+$ beam at the material and observing the resultant profiles of the solutes. The implanted Au was also investigated in the same manner. The implantations were performed at various temperatures between 25 and 700$\\sp\\circ$C at a Au dose of $1.0\\times10\\sp{16}.$ Depletion of the existing solutes was observed in all cases and attributed to radiation-induced segregation effects attributable to fluxes of defects established by the irradiating beam. At elevated temperatures, the amount of Au retained in the target declined dramatically, losses that attributed to sputtering from a monolayer established at the surface by Gibbsian Segregation. Simulation of the implantations by a theoretical kinetic model was used to produce values for the important defect migration and binding parameters that are responsible for the most significant radiation effects. The derived parameters are in agreement with other published results and can be used to predict the general behavior of the solutes in the Ni system under irradiation.","abstract_html":"The diffusion behavior of solutes under irradiation in a Ni matrix have been investigated. The behavior of the solutes Si, Be, Ge, and Al were studied by directing a 300 keV Au$\\sp+$ beam at the material and observing the resultant profiles of the solutes. The implanted Au was also investigated in the same manner. The implantations were performed at various temperatures between 25 and 700$\\sp\\circ$C at a Au dose of $1.0\\times10\\sp{16}.$ Depletion of the existing solutes was observed in all cases and attributed to radiation-induced segregation effects attributable to fluxes of defects established by the irradiating beam. At elevated temperatures, the amount of Au retained in the target declined dramatically, losses that attributed to sputtering from a monolayer established at the surface by Gibbsian Segregation. Simulation of the implantations by a theoretical kinetic model was used to produce values for the important defect migration and binding parameters that are responsible for the most significant radiation effects. The derived parameters are in agreement with other published results and can be used to predict the general behavior of the solutes in the Ni system under irradiation.","abstract_has_math":true,"creators":["James, Michael Richard"],"institution":"University of Illinois at Urbana-Champaign","degree_name":"Ph.D.","degree_level":"Dissertation","degree_discipline":"Nuclear Engineering","degree_department":null,"school":null,"contributors":["Stubbins, James F."],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2015,"date_issued":"2015-09-28T14:51:19Z","date_published":"2015-09-28T14:51:19Z","updated_at":"2026-07-22T22:26:26Z","subjects":["Engineering, Nuclear"],"languages":["eng"],"rights":[],"rights_urls":[],"identifier_entries":[{"key":"dc:identifier","label":"Identifier","values":["(MiAaPQ)AAI9812642"],"render_values":[{"text":"(MiAaPQ)AAI9812642","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/2142/85933","outbound_label":"Handle","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor","label":"Contributor","values":["Stubbins, James F."]},{"key":"dc:creator","label":"Author","values":["James, Michael Richard"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date","label":"Dc Date","values":["2015-09-28T14:51:19Z","10000-01-01","1997"]},{"key":"dc:type","label":"Dc Type","values":["text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Nuclear Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Dissertation"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Ph.D."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["University of Illinois at Urbana-Champaign"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Engineering, Nuclear"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["eng"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["http://hdl.handle.net/2142/85933","(MiAaPQ)AAI9812642"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["The diffusion behavior of solutes under irradiation in a Ni matrix have been investigated. The behavior of the solutes Si, Be, Ge, and Al were studied by directing a 300 keV Au$\\sp+$ beam at the material and observing the resultant profiles of the solutes. The implanted Au was also investigated in the same manner. The implantations were performed at various temperatures between 25 and 700$\\sp\\circ$C at a Au dose of $1.0\\times10\\sp{16}.$ Depletion of the existing solutes was observed in all cases and attributed to radiation-induced segregation effects attributable to fluxes of defects established by the irradiating beam. At elevated temperatures, the amount of Au retained in the target declined dramatically, losses that attributed to sputtering from a monolayer established at the surface by Gibbsian Segregation. Simulation of the implantations by a theoretical kinetic model was used to produce values for the important defect migration and binding parameters that are responsible for the most significant radiation effects. The derived parameters are in agreement with other published results and can be used to predict the general behavior of the solutes in the Ni system under irradiation.","Made available in DSpace on 2015-09-28T14:51:19Z (GMT). No. of bitstreams: 2 license.txt: 4848 bytes, checksum: 96035ab3f5e1c23cc7138a224ce498bd (MD5) 9812642.pdf: 4016950 bytes, checksum: 90ff59c9e21aefadd95fdf7b8c15c7ed (MD5) Previous issue date: 1997","Embargo set by: Seth Robbins for item 87214 Lift date: Forever Reason: Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","U of I Only","178 p.","Thesis (Ph.D.)--University of Illinois at Urbana-Champaign, 1997."]},{"key":"dc:title","label":"Title","values":["The Influence of Defect-Solute Interactions on Segregation of Au Implanted Into Binary Ni Alloys at Elevated Temperatures"]}]}],"canonical_facts":{"dc:contributor":["Stubbins, James F."],"dc:creator":["James, Michael Richard"],"dc:date":["2015-09-28T14:51:19Z","10000-01-01","1997"],"dc:description":["The diffusion behavior of solutes under irradiation in a Ni matrix have been investigated. The behavior of the solutes Si, Be, Ge, and Al were studied by directing a 300 keV Au$\\sp+$ beam at the material and observing the resultant profiles of the solutes. The implanted Au was also investigated in the same manner. The implantations were performed at various temperatures between 25 and 700$\\sp\\circ$C at a Au dose of $1.0\\times10\\sp{16}.$ Depletion of the existing solutes was observed in all cases and attributed to radiation-induced segregation effects attributable to fluxes of defects established by the irradiating beam. At elevated temperatures, the amount of Au retained in the target declined dramatically, losses that attributed to sputtering from a monolayer established at the surface by Gibbsian Segregation. Simulation of the implantations by a theoretical kinetic model was used to produce values for the important defect migration and binding parameters that are responsible for the most significant radiation effects. The derived parameters are in agreement with other published results and can be used to predict the general behavior of the solutes in the Ni system under irradiation.","Made available in DSpace on 2015-09-28T14:51:19Z (GMT). No. of bitstreams: 2 license.txt: 4848 bytes, checksum: 96035ab3f5e1c23cc7138a224ce498bd (MD5) 9812642.pdf: 4016950 bytes, checksum: 90ff59c9e21aefadd95fdf7b8c15c7ed (MD5) Previous issue date: 1997","Embargo set by: Seth Robbins for item 87214 Lift date: Forever Reason: Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","U of I Only","178 p.","Thesis (Ph.D.)--University of Illinois at Urbana-Champaign, 1997."],"dc:identifier":["http://hdl.handle.net/2142/85933","(MiAaPQ)AAI9812642"],"dc:language":["eng"],"dc:subject":["Engineering, Nuclear"],"dc:title":["The Influence of Defect-Solute Interactions on Segregation of Au Implanted Into Binary Ni Alloys at Elevated Temperatures"],"dc:type":["text"],"thesis:degree_discipline":["Nuclear Engineering"],"thesis:degree_level":["Dissertation"],"thesis:degree_name":["Ph.D."],"thesis:institution_name":["University of Illinois at Urbana-Champaign"]},"updated_at":"2026-07-22T22:26:26Z"}