{"id":{"repo_id":"uiuc","oai_identifier":"oai:www.ideals.illinois.edu:2142/85104"},"canonical_url":"https://search.dev.ndltd.org/etd/uiuc/oai:www.ideals.illinois.edu:2142/85104","repository":{"repo_id":"uiuc","name":"University of Illinois - Urbana-Champaign","base_url":"https://www.ideals.illinois.edu/oai-pmh"},"display":{"title":"Evaluation of Tungsten Hexachloride as a ROMP Active Catalyst Precursor for Self -Healing Polymers","abstract":"A drawback to current catalysts used in self-healing materials is the relatively low temperatures at which they deactivate. An advantage of WCl 6 is that the high melting temperature (Tm=275°C) allows for the use of the catalyst in higher temperature applications. Typical polymer and fiber reinforced plastic processing temperatures are 121 and 177°C. The ability of WCl6 catalyst to withstand these processing temperatures was probed. Several thermal analysis techniques were used to evaluate the activity of WCl6 after high temperature exposure. At both 121 and 177°C in an inert environment, the WCl6 retained sufficient activity for use as a ROMP precursor for self-healing applications. Mechanical evaluation through fracture experiments showed healing efficiencies as high as 92% if the processing and testing environment was carefully controlled.","abstract_html":"A drawback to current catalysts used in self-healing materials is the relatively low temperatures at which they deactivate. An advantage of WCl 6 is that the high melting temperature (Tm=275°C) allows for the use of the catalyst in higher temperature applications. Typical polymer and fiber reinforced plastic processing temperatures are 121 and 177°C. The ability of WCl6 catalyst to withstand these processing temperatures was probed. Several thermal analysis techniques were used to evaluate the activity of WCl6 after high temperature exposure. At both 121 and 177°C in an inert environment, the WCl6 retained sufficient activity for use as a ROMP precursor for self-healing applications. Mechanical evaluation through fracture experiments showed healing efficiencies as high as 92% if the processing and testing environment was carefully controlled.","abstract_has_math":false,"creators":["Kamphaus, Jason M."],"institution":"University of Illinois at Urbana-Champaign","degree_name":"Ph.D.","degree_level":"Dissertation","degree_discipline":"Aerospace Engineering","degree_department":null,"school":null,"contributors":["White, Scott R."],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2015,"date_issued":"2015-09-25T22:34:26Z","date_published":"2015-09-25T22:34:26Z","updated_at":"2026-07-22T22:26:24Z","subjects":["Engineering, Materials Science"],"languages":["eng"],"rights":[],"rights_urls":[],"identifier_entries":[{"key":"dc:identifier","label":"Identifier","values":["(MiAaPQ)AAI3290268"],"render_values":[{"text":"(MiAaPQ)AAI3290268","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/2142/85104","outbound_label":"Handle","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor","label":"Contributor","values":["White, Scott R."]},{"key":"dc:creator","label":"Author","values":["Kamphaus, Jason M."]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date","label":"Dc Date","values":["2015-09-25T22:34:26Z","10000-01-01","2007"]},{"key":"dc:type","label":"Dc Type","values":["text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Aerospace Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Dissertation"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Ph.D."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["University of Illinois at Urbana-Champaign"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Engineering, Materials Science"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["eng"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["http://hdl.handle.net/2142/85104","(MiAaPQ)AAI3290268"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["A drawback to current catalysts used in self-healing materials is the relatively low temperatures at which they deactivate. An advantage of WCl 6 is that the high melting temperature (Tm=275°C) allows for the use of the catalyst in higher temperature applications. Typical polymer and fiber reinforced plastic processing temperatures are 121 and 177°C. The ability of WCl6 catalyst to withstand these processing temperatures was probed. Several thermal analysis techniques were used to evaluate the activity of WCl6 after high temperature exposure. At both 121 and 177°C in an inert environment, the WCl6 retained sufficient activity for use as a ROMP precursor for self-healing applications. Mechanical evaluation through fracture experiments showed healing efficiencies as high as 92% if the processing and testing environment was carefully controlled.","Made available in DSpace on 2015-09-25T22:34:26Z (GMT). No. of bitstreams: 2 license.txt: 4848 bytes, checksum: 96035ab3f5e1c23cc7138a224ce498bd (MD5) 3290268.pdf: 3069195 bytes, checksum: 66e4ff3621c95fb644f1ee1ea4acd81c (MD5) Previous issue date: 2007","Embargo set by: Seth Robbins for item 86385 Lift date: Forever Reason: Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","U of I Only","140 p.","Thesis (Ph.D.)--University of Illinois at Urbana-Champaign, 2007."]},{"key":"dc:title","label":"Title","values":["Evaluation of Tungsten Hexachloride as a ROMP Active Catalyst Precursor for Self -Healing Polymers"]}]}],"canonical_facts":{"dc:contributor":["White, Scott R."],"dc:creator":["Kamphaus, Jason M."],"dc:date":["2015-09-25T22:34:26Z","10000-01-01","2007"],"dc:description":["A drawback to current catalysts used in self-healing materials is the relatively low temperatures at which they deactivate. An advantage of WCl 6 is that the high melting temperature (Tm=275°C) allows for the use of the catalyst in higher temperature applications. Typical polymer and fiber reinforced plastic processing temperatures are 121 and 177°C. The ability of WCl6 catalyst to withstand these processing temperatures was probed. Several thermal analysis techniques were used to evaluate the activity of WCl6 after high temperature exposure. At both 121 and 177°C in an inert environment, the WCl6 retained sufficient activity for use as a ROMP precursor for self-healing applications. Mechanical evaluation through fracture experiments showed healing efficiencies as high as 92% if the processing and testing environment was carefully controlled.","Made available in DSpace on 2015-09-25T22:34:26Z (GMT). No. of bitstreams: 2 license.txt: 4848 bytes, checksum: 96035ab3f5e1c23cc7138a224ce498bd (MD5) 3290268.pdf: 3069195 bytes, checksum: 66e4ff3621c95fb644f1ee1ea4acd81c (MD5) Previous issue date: 2007","Embargo set by: Seth Robbins for item 86385 Lift date: Forever Reason: Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","U of I Only","140 p.","Thesis (Ph.D.)--University of Illinois at Urbana-Champaign, 2007."],"dc:identifier":["http://hdl.handle.net/2142/85104","(MiAaPQ)AAI3290268"],"dc:language":["eng"],"dc:subject":["Engineering, Materials Science"],"dc:title":["Evaluation of Tungsten Hexachloride as a ROMP Active Catalyst Precursor for Self -Healing Polymers"],"dc:type":["text"],"thesis:degree_discipline":["Aerospace Engineering"],"thesis:degree_level":["Dissertation"],"thesis:degree_name":["Ph.D."],"thesis:institution_name":["University of Illinois at Urbana-Champaign"]},"updated_at":"2026-07-22T22:26:24Z"}