{"id":{"repo_id":"uiuc","oai_identifier":"oai:www.ideals.illinois.edu:2142/82754"},"canonical_url":"https://search.dev.ndltd.org/etd/uiuc/oai:www.ideals.illinois.edu:2142/82754","repository":{"repo_id":"uiuc","name":"University of Illinois - Urbana-Champaign","base_url":"https://www.ideals.illinois.edu/oai-pmh"},"display":{"title":"Modeling Interfacial Slag Layer Phenomena in the Shell /Mold Gap in Continuous Casting of Steel","abstract":"The model was also applied to interpret the crystallization behavior of slag. A mechanism for the formation of this crystalline layer was proposed that combined the effects of a shift in the viscosity curve, a decrease in the liquid slag conductivity due to partial crystallization, and an increase in the solid slag layer. When the shear stress exceeds the slag shear strength before the axial stress accumulates to the fracture strength, the slag could shear longitudinally inside the layers.","abstract_html":"The model was also applied to interpret the crystallization behavior of slag. A mechanism for the formation of this crystalline layer was proposed that combined the effects of a shift in the viscosity curve, a decrease in the liquid slag conductivity due to partial crystallization, and an increase in the solid slag layer. When the shear stress exceeds the slag shear strength before the axial stress accumulates to the fracture strength, the slag could shear longitudinally inside the layers.","abstract_has_math":false,"creators":["Meng, Ya"],"institution":"University of Illinois at Urbana-Champaign","degree_name":"Ph.D.","degree_level":"Dissertation","degree_discipline":"Materials Science and Engineering","degree_department":null,"school":null,"contributors":["Thomas, Brian G."],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2015,"date_issued":"2015-09-25T20:52:51Z","date_published":"2015-09-25T20:52:51Z","updated_at":"2026-07-22T22:26:18Z","subjects":["Engineering, Metallurgy"],"languages":["eng"],"rights":[],"rights_urls":[],"identifier_entries":[{"key":"dc:identifier","label":"Identifier","values":["(MiAaPQ)AAI3153381"],"render_values":[{"text":"(MiAaPQ)AAI3153381","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/2142/82754","outbound_label":"Handle","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor","label":"Contributor","values":["Thomas, Brian G."]},{"key":"dc:creator","label":"Author","values":["Meng, Ya"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date","label":"Dc Date","values":["2015-09-25T20:52:51Z","10000-01-01","2004"]},{"key":"dc:type","label":"Dc Type","values":["text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Materials Science and Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Dissertation"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Ph.D."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["University of Illinois at Urbana-Champaign"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Engineering, Metallurgy"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["eng"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["http://hdl.handle.net/2142/82754","(MiAaPQ)AAI3153381"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["The model was also applied to interpret the crystallization behavior of slag. A mechanism for the formation of this crystalline layer was proposed that combined the effects of a shift in the viscosity curve, a decrease in the liquid slag conductivity due to partial crystallization, and an increase in the solid slag layer. When the shear stress exceeds the slag shear strength before the axial stress accumulates to the fracture strength, the slag could shear longitudinally inside the layers.","Made available in DSpace on 2015-09-25T20:52:51Z (GMT). No. of bitstreams: 2 license.txt: 4848 bytes, checksum: 96035ab3f5e1c23cc7138a224ce498bd (MD5) 3153381.pdf: 9833324 bytes, checksum: 05eec7aaebe8078e06152fbe097a930a (MD5) Previous issue date: 2004","Embargo set by: Seth Robbins for item 84035 Lift date: Forever Reason: Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","U of I Only","212 p.","Thesis (Ph.D.)--University of Illinois at Urbana-Champaign, 2004."]},{"key":"dc:title","label":"Title","values":["Modeling Interfacial Slag Layer Phenomena in the Shell /Mold Gap in Continuous Casting of Steel"]}]}],"canonical_facts":{"dc:contributor":["Thomas, Brian G."],"dc:creator":["Meng, Ya"],"dc:date":["2015-09-25T20:52:51Z","10000-01-01","2004"],"dc:description":["The model was also applied to interpret the crystallization behavior of slag. A mechanism for the formation of this crystalline layer was proposed that combined the effects of a shift in the viscosity curve, a decrease in the liquid slag conductivity due to partial crystallization, and an increase in the solid slag layer. When the shear stress exceeds the slag shear strength before the axial stress accumulates to the fracture strength, the slag could shear longitudinally inside the layers.","Made available in DSpace on 2015-09-25T20:52:51Z (GMT). No. of bitstreams: 2 license.txt: 4848 bytes, checksum: 96035ab3f5e1c23cc7138a224ce498bd (MD5) 3153381.pdf: 9833324 bytes, checksum: 05eec7aaebe8078e06152fbe097a930a (MD5) Previous issue date: 2004","Embargo set by: Seth Robbins for item 84035 Lift date: Forever Reason: Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","U of I Only","212 p.","Thesis (Ph.D.)--University of Illinois at Urbana-Champaign, 2004."],"dc:identifier":["http://hdl.handle.net/2142/82754","(MiAaPQ)AAI3153381"],"dc:language":["eng"],"dc:subject":["Engineering, Metallurgy"],"dc:title":["Modeling Interfacial Slag Layer Phenomena in the Shell /Mold Gap in Continuous Casting of Steel"],"dc:type":["text"],"thesis:degree_discipline":["Materials Science and Engineering"],"thesis:degree_level":["Dissertation"],"thesis:degree_name":["Ph.D."],"thesis:institution_name":["University of Illinois at Urbana-Champaign"]},"updated_at":"2026-07-22T22:26:18Z"}