{"id":{"repo_id":"uiuc","oai_identifier":"oai:www.ideals.illinois.edu:2142/82712"},"canonical_url":"https://search.dev.ndltd.org/etd/uiuc/oai:www.ideals.illinois.edu:2142/82712","repository":{"repo_id":"uiuc","name":"University of Illinois - Urbana-Champaign","base_url":"https://www.ideals.illinois.edu/oai-pmh"},"display":{"title":"Design of Sintered, Tough, Oxide Laminate and Fibrous Monolithic Composites","abstract":"Tough, oxide, laminated and fibrous monolithic composites were fabricated by using tape casting and co-extrusion technique, respectively. Mullite (3Al 2O3·2SiO2), alumina (Al2O 3), 50 vol% alumina · 50 vol% YAG (yttrium aluminum garnet, Y 3Al5O12) in situ composite, 50 vol% alumina · 50 vol% mullite in situ composite, zirconia (ZrO 2), and nickel aluminate (NiAl2O4) were used as matrix materials. Aluminum phosphate (AlPO4), alumina platelets, and 50 vol% alumina · 50 vol% leucite (KAlSi2O6) were chosen as high temperature applicable interphase materials. ICP (Inductively coupled plasma) data indicated no extensive decomposition of AlPO4 heat treated at 1600 and 1800°C. The AlPO4 worked as a stable, porous, weak, crack deflecting interphase material with three point bending strength of 1.5 MPa and 61% of theoretical density after heat treatment at 1600°C for 10h. The 50 vol% alumina · 50 vol% YAG in situ composite had a bending strength of 361 MPa after sintering at the condition of 1700°C/5h. A : B (C) : D (E) bimodal designs were proposed to increase the toughness of the laminated composites. 1 : 5 (6) : 12 (1) bimodal laminated composite had a bending strength and a work of fracture of 142 MPa and 0.51 KJ/m2, respectively. Fibrous monolithic composites with different interphase thickness and interphase composition were fabricated. 2-, 3- and mixed-layer fibrous monolithic composites were made.","abstract_html":"Tough, oxide, laminated and fibrous monolithic composites were fabricated by using tape casting and co-extrusion technique, respectively. Mullite (3Al 2O3·2SiO2), alumina (Al2O 3), 50 vol% alumina · 50 vol% YAG (yttrium aluminum garnet, Y 3Al5O12) in situ composite, 50 vol% alumina · 50 vol% mullite in situ composite, zirconia (ZrO 2), and nickel aluminate (NiAl2O4) were used as matrix materials. Aluminum phosphate (AlPO4), alumina platelets, and 50 vol% alumina · 50 vol% leucite (KAlSi2O6) were chosen as high temperature applicable interphase materials. ICP (Inductively coupled plasma) data indicated no extensive decomposition of AlPO4 heat treated at 1600 and 1800°C. The AlPO4 worked as a stable, porous, weak, crack deflecting interphase material with three point bending strength of 1.5 MPa and 61% of theoretical density after heat treatment at 1600°C for 10h. The 50 vol% alumina · 50 vol% YAG in situ composite had a bending strength of 361 MPa after sintering at the condition of 1700°C/5h. A : B (C) : D (E) bimodal designs were proposed to increase the toughness of the laminated composites. 1 : 5 (6) : 12 (1) bimodal laminated composite had a bending strength and a work of fracture of 142 MPa and 0.51 KJ/m2, respectively. Fibrous monolithic composites with different interphase thickness and interphase composition were fabricated. 2-, 3- and mixed-layer fibrous monolithic composites were made.","abstract_has_math":false,"creators":["Kim, Dong-Kyu"],"institution":"University of Illinois at Urbana-Champaign","degree_name":"Ph.D.","degree_level":"Dissertation","degree_discipline":"Materials Science and Engineering","degree_department":null,"school":null,"contributors":["Kriven, Waltraud M."],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2015,"date_issued":"2015-09-25T20:52:35Z","date_published":"2015-09-25T20:52:35Z","updated_at":"2026-07-22T22:26:18Z","subjects":["Engineering, Materials Science"],"languages":["eng"],"rights":[],"rights_urls":[],"identifier_entries":[{"key":"dc:identifier","label":"Identifier","values":["(MiAaPQ)AAI3044136"],"render_values":[{"text":"(MiAaPQ)AAI3044136","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/2142/82712","outbound_label":"Handle","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor","label":"Contributor","values":["Kriven, Waltraud M."]},{"key":"dc:creator","label":"Author","values":["Kim, Dong-Kyu"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date","label":"Dc Date","values":["2015-09-25T20:52:35Z","10000-01-01","2002"]},{"key":"dc:type","label":"Dc Type","values":["text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Materials Science and Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Dissertation"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Ph.D."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["University of Illinois at Urbana-Champaign"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Engineering, Materials Science"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["eng"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["http://hdl.handle.net/2142/82712","(MiAaPQ)AAI3044136"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["Tough, oxide, laminated and fibrous monolithic composites were fabricated by using tape casting and co-extrusion technique, respectively. Mullite (3Al 2O3·2SiO2), alumina (Al2O 3), 50 vol% alumina · 50 vol% YAG (yttrium aluminum garnet, Y 3Al5O12) in situ composite, 50 vol% alumina · 50 vol% mullite in situ composite, zirconia (ZrO 2), and nickel aluminate (NiAl2O4) were used as matrix materials. Aluminum phosphate (AlPO4), alumina platelets, and 50 vol% alumina · 50 vol% leucite (KAlSi2O6) were chosen as high temperature applicable interphase materials. ICP (Inductively coupled plasma) data indicated no extensive decomposition of AlPO4 heat treated at 1600 and 1800°C. The AlPO4 worked as a stable, porous, weak, crack deflecting interphase material with three point bending strength of 1.5 MPa and 61% of theoretical density after heat treatment at 1600°C for 10h. The 50 vol% alumina · 50 vol% YAG in situ composite had a bending strength of 361 MPa after sintering at the condition of 1700°C/5h. A : B (C) : D (E) bimodal designs were proposed to increase the toughness of the laminated composites. 1 : 5 (6) : 12 (1) bimodal laminated composite had a bending strength and a work of fracture of 142 MPa and 0.51 KJ/m2, respectively. Fibrous monolithic composites with different interphase thickness and interphase composition were fabricated. 2-, 3- and mixed-layer fibrous monolithic composites were made.","Made available in DSpace on 2015-09-25T20:52:35Z (GMT). No. of bitstreams: 2 license.txt: 4848 bytes, checksum: 96035ab3f5e1c23cc7138a224ce498bd (MD5) 3044136.pdf: 7538919 bytes, checksum: e89421d0deae4289a31d88eb11b8c259 (MD5) Previous issue date: 2002","Embargo set by: Seth Robbins for item 83993 Lift date: Forever Reason: Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","U of I Only","200 p.","Thesis (Ph.D.)--University of Illinois at Urbana-Champaign, 2002."]},{"key":"dc:title","label":"Title","values":["Design of Sintered, Tough, Oxide Laminate and Fibrous Monolithic Composites"]}]}],"canonical_facts":{"dc:contributor":["Kriven, Waltraud M."],"dc:creator":["Kim, Dong-Kyu"],"dc:date":["2015-09-25T20:52:35Z","10000-01-01","2002"],"dc:description":["Tough, oxide, laminated and fibrous monolithic composites were fabricated by using tape casting and co-extrusion technique, respectively. Mullite (3Al 2O3·2SiO2), alumina (Al2O 3), 50 vol% alumina · 50 vol% YAG (yttrium aluminum garnet, Y 3Al5O12) in situ composite, 50 vol% alumina · 50 vol% mullite in situ composite, zirconia (ZrO 2), and nickel aluminate (NiAl2O4) were used as matrix materials. Aluminum phosphate (AlPO4), alumina platelets, and 50 vol% alumina · 50 vol% leucite (KAlSi2O6) were chosen as high temperature applicable interphase materials. ICP (Inductively coupled plasma) data indicated no extensive decomposition of AlPO4 heat treated at 1600 and 1800°C. The AlPO4 worked as a stable, porous, weak, crack deflecting interphase material with three point bending strength of 1.5 MPa and 61% of theoretical density after heat treatment at 1600°C for 10h. The 50 vol% alumina · 50 vol% YAG in situ composite had a bending strength of 361 MPa after sintering at the condition of 1700°C/5h. A : B (C) : D (E) bimodal designs were proposed to increase the toughness of the laminated composites. 1 : 5 (6) : 12 (1) bimodal laminated composite had a bending strength and a work of fracture of 142 MPa and 0.51 KJ/m2, respectively. Fibrous monolithic composites with different interphase thickness and interphase composition were fabricated. 2-, 3- and mixed-layer fibrous monolithic composites were made.","Made available in DSpace on 2015-09-25T20:52:35Z (GMT). No. of bitstreams: 2 license.txt: 4848 bytes, checksum: 96035ab3f5e1c23cc7138a224ce498bd (MD5) 3044136.pdf: 7538919 bytes, checksum: e89421d0deae4289a31d88eb11b8c259 (MD5) Previous issue date: 2002","Embargo set by: Seth Robbins for item 83993 Lift date: Forever Reason: Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","U of I Only","200 p.","Thesis (Ph.D.)--University of Illinois at Urbana-Champaign, 2002."],"dc:identifier":["http://hdl.handle.net/2142/82712","(MiAaPQ)AAI3044136"],"dc:language":["eng"],"dc:subject":["Engineering, Materials Science"],"dc:title":["Design of Sintered, Tough, Oxide Laminate and Fibrous Monolithic Composites"],"dc:type":["text"],"thesis:degree_discipline":["Materials Science and Engineering"],"thesis:degree_level":["Dissertation"],"thesis:degree_name":["Ph.D."],"thesis:institution_name":["University of Illinois at Urbana-Champaign"]},"updated_at":"2026-07-22T22:26:18Z"}