{"id":{"repo_id":"uiuc","oai_identifier":"oai:www.ideals.illinois.edu:2142/71827"},"canonical_url":"https://search.dev.ndltd.org/etd/uiuc/oai:www.ideals.illinois.edu:2142/71827","repository":{"repo_id":"uiuc","name":"University of Illinois - Urbana-Champaign","base_url":"https://www.ideals.illinois.edu/oai-pmh"},"display":{"title":"Dynamic Compaction of Rapidly Solidified Nickel-Base Superalloys (Rapid Solidification, Powder Metallurgy, Hot Isostatic Pressing, Consolidation, Precipitation)","abstract":"Rapid solidification of an experimental nickel-base superalloy was achieved using centrifugal atomization, chill-block melt-spinning and laser surface melting. Transmission electron microscopy was utilized to characterize the various microstructures obtained in terms of growth morphology, segregation profiles, (gamma)' size and distribution of secondary hardening phases. The response of melt-spun ribbon to thermal treatment was determined and utilized to evaluate the microstructures observed in consolidated material.","abstract_html":"Rapid solidification of an experimental nickel-base superalloy was achieved using centrifugal atomization, chill-block melt-spinning and laser surface melting. Transmission electron microscopy was utilized to characterize the various microstructures obtained in terms of growth morphology, segregation profiles, (gamma)' size and distribution of secondary hardening phases. The response of melt-spun ribbon to thermal treatment was determined and utilized to evaluate the microstructures observed in consolidated material.","abstract_has_math":false,"creators":["Hales, Stephen John"],"institution":"University of Illinois at Urbana-Champaign","degree_name":"Ph.D.","degree_level":"Dissertation","degree_discipline":"Metallurgical Engineering","degree_department":null,"school":null,"contributors":[],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2014,"date_issued":"2014-12-16T20:52:04Z","date_published":"2014-12-16T20:52:04Z","updated_at":"2026-07-22T22:26:05Z","subjects":["Engineering, Metallurgy"],"languages":[],"rights":[],"rights_urls":[],"identifier_entries":[{"key":"dc:identifier","label":"Identifier","values":["(UMI)AAI8610931"],"render_values":[{"text":"(UMI)AAI8610931","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/2142/71827","outbound_label":"Handle","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:creator","label":"Author","values":["Hales, Stephen John"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date","label":"Dc Date","values":["2014-12-16T20:52:04Z","10000-01-01","1986"]},{"key":"dc:type","label":"Dc Type","values":["text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Metallurgical Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Dissertation"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Ph.D."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["University of Illinois at Urbana-Champaign"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Engineering, Metallurgy"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["http://hdl.handle.net/2142/71827","(UMI)AAI8610931"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["Rapid solidification of an experimental nickel-base superalloy was achieved using centrifugal atomization, chill-block melt-spinning and laser surface melting. Transmission electron microscopy was utilized to characterize the various microstructures obtained in terms of growth morphology, segregation profiles, (gamma)' size and distribution of secondary hardening phases. The response of melt-spun ribbon to thermal treatment was determined and utilized to evaluate the microstructures observed in consolidated material.","Rapidly solidified particulate was consolidated using both hot isostatic pressing and dynamic powder compaction. Studies were conducted to establish the way in which rapidly solidified microstructures had changed during each process, particularly with respect to possible interparticle bonding mechanisms. Mechanical tests performed on the hot isostatically pressed material established the integrity of this bonding. In addition, the dynamically compacted material was exposed to various elevated temperatures to determine the stability of the microstructure. The resultant recrystallized microstructure was evaluated in terms of the suitability of the material for intermediate temperature applications.","Made available in DSpace on 2014-12-16T20:52:04Z (GMT). No. of bitstreams: 1 8610931.pdf: 6673446 bytes, checksum: 1f53b9a7cabf746289c59f1e2ad94163 (MD5) Previous issue date: 1986","Embargo set by: Seth Robbins for item 71993 Lift date: Forever Reason: Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","U of I Only","170 p.","Thesis (Ph.D.)--University of Illinois at Urbana-Champaign, 1986."]},{"key":"dc:title","label":"Title","values":["Dynamic Compaction of Rapidly Solidified Nickel-Base Superalloys (Rapid Solidification, Powder Metallurgy, Hot Isostatic Pressing, Consolidation, Precipitation)"]}]}],"canonical_facts":{"dc:creator":["Hales, Stephen John"],"dc:date":["2014-12-16T20:52:04Z","10000-01-01","1986"],"dc:description":["Rapid solidification of an experimental nickel-base superalloy was achieved using centrifugal atomization, chill-block melt-spinning and laser surface melting. Transmission electron microscopy was utilized to characterize the various microstructures obtained in terms of growth morphology, segregation profiles, (gamma)' size and distribution of secondary hardening phases. The response of melt-spun ribbon to thermal treatment was determined and utilized to evaluate the microstructures observed in consolidated material.","Rapidly solidified particulate was consolidated using both hot isostatic pressing and dynamic powder compaction. Studies were conducted to establish the way in which rapidly solidified microstructures had changed during each process, particularly with respect to possible interparticle bonding mechanisms. Mechanical tests performed on the hot isostatically pressed material established the integrity of this bonding. In addition, the dynamically compacted material was exposed to various elevated temperatures to determine the stability of the microstructure. The resultant recrystallized microstructure was evaluated in terms of the suitability of the material for intermediate temperature applications.","Made available in DSpace on 2014-12-16T20:52:04Z (GMT). No. of bitstreams: 1 8610931.pdf: 6673446 bytes, checksum: 1f53b9a7cabf746289c59f1e2ad94163 (MD5) Previous issue date: 1986","Embargo set by: Seth Robbins for item 71993 Lift date: Forever Reason: Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","U of I Only","170 p.","Thesis (Ph.D.)--University of Illinois at Urbana-Champaign, 1986."],"dc:identifier":["http://hdl.handle.net/2142/71827","(UMI)AAI8610931"],"dc:subject":["Engineering, Metallurgy"],"dc:title":["Dynamic Compaction of Rapidly Solidified Nickel-Base Superalloys (Rapid Solidification, Powder Metallurgy, Hot Isostatic Pressing, Consolidation, Precipitation)"],"dc:type":["text"],"thesis:degree_discipline":["Metallurgical Engineering"],"thesis:degree_level":["Dissertation"],"thesis:degree_name":["Ph.D."],"thesis:institution_name":["University of Illinois at Urbana-Champaign"]},"updated_at":"2026-07-22T22:26:05Z"}