{"id":{"repo_id":"uiuc","oai_identifier":"oai:www.ideals.illinois.edu:2142/71706"},"canonical_url":"https://search.dev.ndltd.org/etd/uiuc/oai:www.ideals.illinois.edu:2142/71706","repository":{"repo_id":"uiuc","name":"University of Illinois - Urbana-Champaign","base_url":"https://www.ideals.illinois.edu/oai-pmh"},"display":{"title":"The Effect of Hydrogen on The Microstructure of Silicon-Carbide","abstract":"The effect of hydrogenation on the microstructure of a pressureless sintered silicon carbide was studied. Samples which were annealed in a 40:60 mole % H(,2):Ar atmosphere at 1400(DEGREES)C for 50 hours were microstructurally compared with unannealed samples and samples that had been annealed in a similar manner but using an argon atmosphere. The results were also compared with microstructural results obtained from in situ studies using both hydrogen and argon atmospheres. These results were compared with a thermodynamic model which was constructed using a free energy minimization technique.","abstract_html":"The effect of hydrogenation on the microstructure of a pressureless sintered silicon carbide was studied. Samples which were annealed in a 40:60 mole % H(,2):Ar atmosphere at 1400(DEGREES)C for 50 hours were microstructurally compared with unannealed samples and samples that had been annealed in a similar manner but using an argon atmosphere. The results were also compared with microstructural results obtained from in situ studies using both hydrogen and argon atmospheres. These results were compared with a thermodynamic model which was constructed using a free energy minimization technique.","abstract_has_math":false,"creators":["Fischman, Gary Scott"],"institution":"University of Illinois at Urbana-Champaign","degree_name":"Ph.D.","degree_level":"Dissertation","degree_discipline":"Ceramics Engineering","degree_department":null,"school":null,"contributors":[],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2014,"date_issued":"2014-12-16T19:16:57Z","date_published":"2014-12-16T19:16:57Z","updated_at":"2026-07-22T22:26:05Z","subjects":["Engineering, Materials Science"],"languages":[],"rights":[],"rights_urls":[],"identifier_entries":[{"key":"dc:identifier","label":"Identifier","values":["(UMI)AAI8521764"],"render_values":[{"text":"(UMI)AAI8521764","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/2142/71706","outbound_label":"Handle","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:creator","label":"Author","values":["Fischman, Gary Scott"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date","label":"Dc Date","values":["2014-12-16T19:16:57Z","10000-01-01","1985"]},{"key":"dc:type","label":"Dc Type","values":["text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Ceramics Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Dissertation"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Ph.D."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["University of Illinois at Urbana-Champaign"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Engineering, Materials Science"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["http://hdl.handle.net/2142/71706","(UMI)AAI8521764"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["The effect of hydrogenation on the microstructure of a pressureless sintered silicon carbide was studied. Samples which were annealed in a 40:60 mole % H(,2):Ar atmosphere at 1400(DEGREES)C for 50 hours were microstructurally compared with unannealed samples and samples that had been annealed in a similar manner but using an argon atmosphere. The results were also compared with microstructural results obtained from in situ studies using both hydrogen and argon atmospheres. These results were compared with a thermodynamic model which was constructed using a free energy minimization technique.","The observed effects of hydrogenation were surface decarburization and amorphization throughout the silicon carbide material. Other observations include the thermally induced growth of microcrystalline silicon and accelerated amorphization around the silicon microcrystals in samples used in hydrogen in situ studies. An analysis of the microstructure of the reference material was also performed.","Made available in DSpace on 2014-12-16T19:16:57Z (GMT). No. of bitstreams: 1 8521764.pdf: 4914237 bytes, checksum: 27b1bc6f7b13a3fb2171e144a9e60a7c (MD5) Previous issue date: 1985","Embargo set by: Seth Robbins for item 71872 Lift date: Forever Reason: Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","U of I Only","233 p.","Thesis (Ph.D.)--University of Illinois at Urbana-Champaign, 1985."]},{"key":"dc:title","label":"Title","values":["The Effect of Hydrogen on The Microstructure of Silicon-Carbide"]}]}],"canonical_facts":{"dc:creator":["Fischman, Gary Scott"],"dc:date":["2014-12-16T19:16:57Z","10000-01-01","1985"],"dc:description":["The effect of hydrogenation on the microstructure of a pressureless sintered silicon carbide was studied. Samples which were annealed in a 40:60 mole % H(,2):Ar atmosphere at 1400(DEGREES)C for 50 hours were microstructurally compared with unannealed samples and samples that had been annealed in a similar manner but using an argon atmosphere. The results were also compared with microstructural results obtained from in situ studies using both hydrogen and argon atmospheres. These results were compared with a thermodynamic model which was constructed using a free energy minimization technique.","The observed effects of hydrogenation were surface decarburization and amorphization throughout the silicon carbide material. Other observations include the thermally induced growth of microcrystalline silicon and accelerated amorphization around the silicon microcrystals in samples used in hydrogen in situ studies. An analysis of the microstructure of the reference material was also performed.","Made available in DSpace on 2014-12-16T19:16:57Z (GMT). No. of bitstreams: 1 8521764.pdf: 4914237 bytes, checksum: 27b1bc6f7b13a3fb2171e144a9e60a7c (MD5) Previous issue date: 1985","Embargo set by: Seth Robbins for item 71872 Lift date: Forever Reason: Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs","U of I Only","233 p.","Thesis (Ph.D.)--University of Illinois at Urbana-Champaign, 1985."],"dc:identifier":["http://hdl.handle.net/2142/71706","(UMI)AAI8521764"],"dc:subject":["Engineering, Materials Science"],"dc:title":["The Effect of Hydrogen on The Microstructure of Silicon-Carbide"],"dc:type":["text"],"thesis:degree_discipline":["Ceramics Engineering"],"thesis:degree_level":["Dissertation"],"thesis:degree_name":["Ph.D."],"thesis:institution_name":["University of Illinois at Urbana-Champaign"]},"updated_at":"2026-07-22T22:26:05Z"}