{"id":{"repo_id":"uiuc","oai_identifier":"oai:www.ideals.illinois.edu:2142/49705"},"canonical_url":"https://search.dev.ndltd.org/etd/uiuc/oai:www.ideals.illinois.edu:2142/49705","repository":{"repo_id":"uiuc","name":"University of Illinois - Urbana-Champaign","base_url":"https://www.ideals.illinois.edu/oai-pmh"},"display":{"title":"Photoactivity of titanium dioxide films with controlled orientation","abstract":"Photocatalysis is being explored as a possible alternative to current disinfection treatment methods. Switching to photocatalysis could remove issues with disinfection byproducts and lower the operating costs. However, the activity of photocatalysts is too low to be used commercially. The most common photocatalyst is titanium dioxide, and while the activity of titanium dioxide is high when compared to other photocatalysts, improvements need to be made before commercialization. Increasing the activity of TiO2 can be done in a variety of methods, but this dissertation will focus only on a single method. Previous research has found that TiO2 has a range of activities based on the different phases and orientations. Many groups are focusing on growing crystals that are mainly covered with the most active facet. However, photocatalysis is about balancing reactions, and combining the most active oxidation site with poor reduction site will lower the activity. It is believe that by combining a site that is good for oxidation with a site that is good for reduction can outperform a catalyst with random orientations or even those with the expression of a single orientation. Controlling the phase and orientation of the titanium dioxide will be done by depositing TiO2 onto patterned substrates. The patterns were created through block copolymer lithography, providing sub-50 nm features over the surface of the substrate. The pattern will then be expressed through the film, creating a film that has controlled texture based upon the size scale of the patterned surface. These films will then be characterized by measuring the photoactivity through methylene blue degradation experiments. In addition to the textured films, an experiment was carried out in effort to help identify and quantify reactivity of different orientations of TiO2. This was done by photodepositing metal ions onto different TiO2 films and measuring the metal deposition over time. These experiments showed the range in activities for oxidation and reduction reactions for the phases and orientations tested.","abstract_html":"Photocatalysis is being explored as a possible alternative to current disinfection treatment methods. Switching to photocatalysis could remove issues with disinfection byproducts and lower the operating costs. However, the activity of photocatalysts is too low to be used commercially. The most common photocatalyst is titanium dioxide, and while the activity of titanium dioxide is high when compared to other photocatalysts, improvements need to be made before commercialization. Increasing the activity of TiO2 can be done in a variety of methods, but this dissertation will focus only on a single method. Previous research has found that TiO2 has a range of activities based on the different phases and orientations. Many groups are focusing on growing crystals that are mainly covered with the most active facet. However, photocatalysis is about balancing reactions, and combining the most active oxidation site with poor reduction site will lower the activity. It is believe that by combining a site that is good for oxidation with a site that is good for reduction can outperform a catalyst with random orientations or even those with the expression of a single orientation. Controlling the phase and orientation of the titanium dioxide will be done by depositing TiO2 onto patterned substrates. The patterns were created through block copolymer lithography, providing sub-50 nm features over the surface of the substrate. The pattern will then be expressed through the film, creating a film that has controlled texture based upon the size scale of the patterned surface. These films will then be characterized by measuring the photoactivity through methylene blue degradation experiments. In addition to the textured films, an experiment was carried out in effort to help identify and quantify reactivity of different orientations of TiO2. This was done by photodepositing metal ions onto different TiO2 films and measuring the metal deposition over time. These experiments showed the range in activities for oxidation and reduction reactions for the phases and orientations tested.","abstract_has_math":false,"creators":["Jensen, Cody"],"institution":"University of Illinois at Urbana-Champaign","degree_name":"Ph.D.","degree_level":"Dissertation","degree_discipline":"Chemical Engineering","degree_department":null,"school":null,"contributors":["Cahill, David G.","Yang, Hong","Seebauer, Edmund G.","Flaherty, David W."],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2014,"date_issued":"2014-05-30T17:05:42Z","date_published":"2014-05-30T17:05:42Z","updated_at":"2026-07-22T22:25:38Z","subjects":["titanium dioxide","TiO2","photocatalysis","photodegradation","thin film","sputter deposition","self-assembly"],"languages":["en"],"rights":["Copyright 2014 Cody Jensen"],"rights_urls":[],"identifier_entries":[]},"links":{"outbound_url":"http://hdl.handle.net/2142/49705","outbound_label":"Handle","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor","label":"Contributor","values":["Cahill, David G.","Yang, Hong","Seebauer, Edmund G.","Flaherty, David W."]},{"key":"dc:creator","label":"Author","values":["Jensen, Cody"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date","label":"Dc Date","values":["2014-05-30T17:05:42Z","2016-09-22T20:59:22Z","2014-05"]},{"key":"dc:type","label":"Dc Type","values":["text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Chemical Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Dissertation"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Ph.D."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["University of Illinois at Urbana-Champaign"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["titanium dioxide","TiO2","photocatalysis","photodegradation","thin film","sputter deposition","self-assembly"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["Copyright 2014 Cody Jensen"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["http://hdl.handle.net/2142/49705"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["Photocatalysis is being explored as a possible alternative to current disinfection treatment methods. Switching to photocatalysis could remove issues with disinfection byproducts and lower the operating costs. However, the activity of photocatalysts is too low to be used commercially. The most common photocatalyst is titanium dioxide, and while the activity of titanium dioxide is high when compared to other photocatalysts, improvements need to be made before commercialization. Increasing the activity of TiO2 can be done in a variety of methods, but this dissertation will focus only on a single method. Previous research has found that TiO2 has a range of activities based on the different phases and orientations. Many groups are focusing on growing crystals that are mainly covered with the most active facet. However, photocatalysis is about balancing reactions, and combining the most active oxidation site with poor reduction site will lower the activity. It is believe that by combining a site that is good for oxidation with a site that is good for reduction can outperform a catalyst with random orientations or even those with the expression of a single orientation. Controlling the phase and orientation of the titanium dioxide will be done by depositing TiO2 onto patterned substrates. The patterns were created through block copolymer lithography, providing sub-50 nm features over the surface of the substrate. The pattern will then be expressed through the film, creating a film that has controlled texture based upon the size scale of the patterned surface. These films will then be characterized by measuring the photoactivity through methylene blue degradation experiments. In addition to the textured films, an experiment was carried out in effort to help identify and quantify reactivity of different orientations of TiO2. This was done by photodepositing metal ions onto different TiO2 films and measuring the metal deposition over time. These experiments showed the range in activities for oxidation and reduction reactions for the phases and orientations tested.","Item withdrawn by Laura Spradlin (lspradl2@illinois.edu) on 2014-04-09T14:57:10Z Item was in collections: University of Illinois Theses & Dissertations (ID: 1) No. of bitstreams: 2 Jensen_Cody.docx: 4449942 bytes, checksum: f2b5138fb42936cbe8a0edf7fc7356e9 (MD5) Jensen_Cody.pdf: 2737308 bytes, checksum: 2478aef270dd2ad23f024b1a44c1161b (MD5)","Made available in DSpace on 2014-05-30T17:05:42Z (GMT). No. of bitstreams: 3 Cody_Jensen.pdf: 2737121 bytes, checksum: d1e0079be69f8abc1f3b4c10d026efff (MD5) Jensen_Cody.docx: 4453376 bytes, checksum: fd058b4dc4c48e09bb8fc5e75f4a301f (MD5) license.txt: 4061 bytes, checksum: 8491e89851318a7865b2d380695d9e9e (MD5)","Restriction data tranferred 2014-07-01T11:38:50-05:00 Original Data Group with Access UIUC Users [automated] Release Date: 2016-05-30 12:09:03 UTC Reason: Author requested U of Illinois access only (OA after 2yrs) in Vireo ETD system","Item marked as restricted to the 'UIUC Users [automated]' Group (id=2) by Seth Robbins (robbins.sd@gmail.com) on 2014-05-30T17:09:45Z Item is restricted until 2016-05-30T17:09:03Z","U of I Only Restriction Lifted for Item 49756 on 2016-09-22T20:59:22Z."]},{"key":"dc:title","label":"Title","values":["Photoactivity of titanium dioxide films with controlled orientation"]}]}],"canonical_facts":{"dc:contributor":["Cahill, David G.","Yang, Hong","Seebauer, Edmund G.","Flaherty, David W."],"dc:creator":["Jensen, Cody"],"dc:date":["2014-05-30T17:05:42Z","2016-09-22T20:59:22Z","2014-05"],"dc:description":["Photocatalysis is being explored as a possible alternative to current disinfection treatment methods. Switching to photocatalysis could remove issues with disinfection byproducts and lower the operating costs. However, the activity of photocatalysts is too low to be used commercially. The most common photocatalyst is titanium dioxide, and while the activity of titanium dioxide is high when compared to other photocatalysts, improvements need to be made before commercialization. Increasing the activity of TiO2 can be done in a variety of methods, but this dissertation will focus only on a single method. Previous research has found that TiO2 has a range of activities based on the different phases and orientations. Many groups are focusing on growing crystals that are mainly covered with the most active facet. However, photocatalysis is about balancing reactions, and combining the most active oxidation site with poor reduction site will lower the activity. It is believe that by combining a site that is good for oxidation with a site that is good for reduction can outperform a catalyst with random orientations or even those with the expression of a single orientation. Controlling the phase and orientation of the titanium dioxide will be done by depositing TiO2 onto patterned substrates. The patterns were created through block copolymer lithography, providing sub-50 nm features over the surface of the substrate. The pattern will then be expressed through the film, creating a film that has controlled texture based upon the size scale of the patterned surface. These films will then be characterized by measuring the photoactivity through methylene blue degradation experiments. In addition to the textured films, an experiment was carried out in effort to help identify and quantify reactivity of different orientations of TiO2. This was done by photodepositing metal ions onto different TiO2 films and measuring the metal deposition over time. These experiments showed the range in activities for oxidation and reduction reactions for the phases and orientations tested.","Item withdrawn by Laura Spradlin (lspradl2@illinois.edu) on 2014-04-09T14:57:10Z Item was in collections: University of Illinois Theses & Dissertations (ID: 1) No. of bitstreams: 2 Jensen_Cody.docx: 4449942 bytes, checksum: f2b5138fb42936cbe8a0edf7fc7356e9 (MD5) Jensen_Cody.pdf: 2737308 bytes, checksum: 2478aef270dd2ad23f024b1a44c1161b (MD5)","Made available in DSpace on 2014-05-30T17:05:42Z (GMT). No. of bitstreams: 3 Cody_Jensen.pdf: 2737121 bytes, checksum: d1e0079be69f8abc1f3b4c10d026efff (MD5) Jensen_Cody.docx: 4453376 bytes, checksum: fd058b4dc4c48e09bb8fc5e75f4a301f (MD5) license.txt: 4061 bytes, checksum: 8491e89851318a7865b2d380695d9e9e (MD5)","Restriction data tranferred 2014-07-01T11:38:50-05:00 Original Data Group with Access UIUC Users [automated] Release Date: 2016-05-30 12:09:03 UTC Reason: Author requested U of Illinois access only (OA after 2yrs) in Vireo ETD system","Item marked as restricted to the 'UIUC Users [automated]' Group (id=2) by Seth Robbins (robbins.sd@gmail.com) on 2014-05-30T17:09:45Z Item is restricted until 2016-05-30T17:09:03Z","U of I Only Restriction Lifted for Item 49756 on 2016-09-22T20:59:22Z."],"dc:identifier":["http://hdl.handle.net/2142/49705"],"dc:language":["en"],"dc:rights":["Copyright 2014 Cody Jensen"],"dc:subject":["titanium dioxide","TiO2","photocatalysis","photodegradation","thin film","sputter deposition","self-assembly"],"dc:title":["Photoactivity of titanium dioxide films with controlled orientation"],"dc:type":["text"],"thesis:degree_discipline":["Chemical Engineering"],"thesis:degree_level":["Dissertation"],"thesis:degree_name":["Ph.D."],"thesis:institution_name":["University of Illinois at Urbana-Champaign"]},"updated_at":"2026-07-22T22:25:38Z"}