{"id":{"repo_id":"uiuc","oai_identifier":"oai:www.ideals.illinois.edu:2142/45615"},"canonical_url":"https://search.dev.ndltd.org/etd/uiuc/oai:www.ideals.illinois.edu:2142/45615","repository":{"repo_id":"uiuc","name":"University of Illinois - Urbana-Champaign","base_url":"https://www.ideals.illinois.edu/oai-pmh"},"display":{"title":"Molecularly thin rheological and contact interfaces","abstract":"A molecularly thin lubricant layer (of the order of 1-2 nanometers thick) has been shown to provide bearing forces at the interface between contacting solid surfaces under light loads and high shear rates. This phenomenon is important, for example, in the head-disk contact in magnetic storage hard disk drives to ensure that some of the contact is sustained by the lubricant layer and thus avoiding damage of the solid surfaces. The magnitude of the normal and tangential bearing forces that the lubricant layer can provide depends on temperature, viscosity of the lubricant, sliding velocity and radius of gyration of the lubricant molecules. This study shows that viscosity has the greatest effect on the load bearing capacity of the molecularly thin lubricant. Thus, by controlling the flash temperature and the ratio of molecularly thin lubricant-to-bulk viscosity, the bearing load carrying capacity of the layer can be controlled. This would allow for the contact to be sustained within the mobile lubricant layer, avoiding solid contact so as to protect the diamond-like carbon coating, and thus reduce wear and potential catastrophic failures. Another part of the thesis is the work on nano-tribological behavior of Hafnium-Diboride thin films. Dense, hard nanocrystalline films of HfBN and multilayer ones of HfB2/HfBN compositions having thickness in the range of 100-600 nm were deposited using chemical vapor deposition (CVD) technique. The roughness values of HfBN film is extremely small, with a value of 5.38-7.63 nm so it is compatible for use as a very smooth surface such as in microscale miniature systems. Nano-indentation and nano-scratch experiments were done to investigate friction and wear behavior of the films. HfBN exhibited lower coefficient of friction (COF) compared to the multilayer HfB2/HfBN. The amorphous as-deposited films were subjected to annealing at 700 oC in order to study their mechanical properties in the post-treatment conditions. In comparison to as-deposited films the annealed films possessed lower COF (COF 0.02 lower). The overall response of the annealed HfBN is outstanding making it compatible for wear resistant, very low roughness coating.","abstract_html":"A molecularly thin lubricant layer (of the order of 1-2 nanometers thick) has been shown to provide bearing forces at the interface between contacting solid surfaces under light loads and high shear rates. This phenomenon is important, for example, in the head-disk contact in magnetic storage hard disk drives to ensure that some of the contact is sustained by the lubricant layer and thus avoiding damage of the solid surfaces. The magnitude of the normal and tangential bearing forces that the lubricant layer can provide depends on temperature, viscosity of the lubricant, sliding velocity and radius of gyration of the lubricant molecules. This study shows that viscosity has the greatest effect on the load bearing capacity of the molecularly thin lubricant. Thus, by controlling the flash temperature and the ratio of molecularly thin lubricant-to-bulk viscosity, the bearing load carrying capacity of the layer can be controlled. This would allow for the contact to be sustained within the mobile lubricant layer, avoiding solid contact so as to protect the diamond-like carbon coating, and thus reduce wear and potential catastrophic failures. Another part of the thesis is the work on nano-tribological behavior of Hafnium-Diboride thin films. Dense, hard nanocrystalline films of HfBN and multilayer ones of HfB2/HfBN compositions having thickness in the range of 100-600 nm were deposited using chemical vapor deposition (CVD) technique. The roughness values of HfBN film is extremely small, with a value of 5.38-7.63 nm so it is compatible for use as a very smooth surface such as in microscale miniature systems. Nano-indentation and nano-scratch experiments were done to investigate friction and wear behavior of the films. HfBN exhibited lower coefficient of friction (COF) compared to the multilayer HfB2/HfBN. The amorphous as-deposited films were subjected to annealing at 700 oC in order to study their mechanical properties in the post-treatment conditions. In comparison to as-deposited films the annealed films possessed lower COF (COF 0.02 lower). The overall response of the annealed HfBN is outstanding making it compatible for wear resistant, very low roughness coating.","abstract_has_math":false,"creators":["Chowdhury, Shahla"],"institution":"University of Illinois at Urbana-Champaign","degree_name":"M.S.","degree_level":"Thesis","degree_discipline":"Theoretical & Applied Mechans","degree_department":null,"school":null,"contributors":["Polycarpou, Andreas A."],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2013,"date_issued":"2013-08-22T16:55:30Z","date_published":"2013-08-22T16:55:30Z","updated_at":"2026-07-22T22:25:36Z","subjects":["Molecularly thin lubricant","Hard disk drive","Coating"],"languages":["en"],"rights":["Copyright reserved by Shahla Chowdhury"],"rights_urls":[],"identifier_entries":[]},"links":{"outbound_url":"http://hdl.handle.net/2142/45615","outbound_label":"Handle","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor","label":"Contributor","values":["Polycarpou, Andreas A."]},{"key":"dc:creator","label":"Author","values":["Chowdhury, Shahla"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date","label":"Dc Date","values":["2013-08-22T16:55:30Z","2015-08-22T10:00:33Z","2013-08"]},{"key":"dc:type","label":"Dc Type","values":["text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Theoretical & Applied Mechans"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Thesis"]},{"key":"thesis:degree_name","label":"Degree Name","values":["M.S."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["University of Illinois at Urbana-Champaign"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Molecularly thin lubricant","Hard disk drive","Coating"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["Copyright reserved by Shahla Chowdhury"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["http://hdl.handle.net/2142/45615"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["A molecularly thin lubricant layer (of the order of 1-2 nanometers thick) has been shown to provide bearing forces at the interface between contacting solid surfaces under light loads and high shear rates. This phenomenon is important, for example, in the head-disk contact in magnetic storage hard disk drives to ensure that some of the contact is sustained by the lubricant layer and thus avoiding damage of the solid surfaces. The magnitude of the normal and tangential bearing forces that the lubricant layer can provide depends on temperature, viscosity of the lubricant, sliding velocity and radius of gyration of the lubricant molecules. This study shows that viscosity has the greatest effect on the load bearing capacity of the molecularly thin lubricant. Thus, by controlling the flash temperature and the ratio of molecularly thin lubricant-to-bulk viscosity, the bearing load carrying capacity of the layer can be controlled. This would allow for the contact to be sustained within the mobile lubricant layer, avoiding solid contact so as to protect the diamond-like carbon coating, and thus reduce wear and potential catastrophic failures. Another part of the thesis is the work on nano-tribological behavior of Hafnium-Diboride thin films. Dense, hard nanocrystalline films of HfBN and multilayer ones of HfB2/HfBN compositions having thickness in the range of 100-600 nm were deposited using chemical vapor deposition (CVD) technique. The roughness values of HfBN film is extremely small, with a value of 5.38-7.63 nm so it is compatible for use as a very smooth surface such as in microscale miniature systems. Nano-indentation and nano-scratch experiments were done to investigate friction and wear behavior of the films. HfBN exhibited lower coefficient of friction (COF) compared to the multilayer HfB2/HfBN. The amorphous as-deposited films were subjected to annealing at 700 oC in order to study their mechanical properties in the post-treatment conditions. In comparison to as-deposited films the annealed films possessed lower COF (COF 0.02 lower). The overall response of the annealed HfBN is outstanding making it compatible for wear resistant, very low roughness coating.","Item withdrawn by Mark Zulauf (zulauf@illinois.edu) on 2013-07-17T19:41:23Z Item was in collections: University of Illinois Theses & Dissertations (ID: 1) No. of bitstreams: 4 1st part.pdf: 103955 bytes, checksum: 5e3a2114b12aef10d5b9cb5a528d96ef (MD5) S.Chowdhury.MS.thesis.pdf: 1873576 bytes, checksum: 4b1aa9b8dcf044cf20aebf01694a32ed (MD5) S.Chowdhury.MS.thesis.pdf: 1873576 bytes, checksum: 4b1aa9b8dcf044cf20aebf01694a32ed (MD5) Chowdhury_Shahla.pdf: 1987570 bytes, checksum: 14c3afe4f461d7a7d501f5c61e490e6a (MD5)","Made available in DSpace on 2013-08-22T16:55:30Z (GMT). No. of bitstreams: 2 Shahla_Chowdhury.pdf: 10199634 bytes, checksum: 8917c1d220107b0e06d69dd39cbdec7b (MD5) license.txt: 4066 bytes, checksum: 75fd1bc71bb8dff3e1204fc76522ac01 (MD5)","Item marked as restricted to the 'Administrator' Group (id=1) by Seth Robbins (srobbins@illinois.edu) on 2013-08-22T16:57:30Z Item is restricted until 2015-08-22T16:57:26Z","Restriction data tranferred 2014-07-01T11:11:46-05:00 Original Data Group with Access Administrator Release Date: 2015-08-22 11:57:26 UTC Reason: Author requested closed access (OA after 2yrs) in Vireo ETD system","Limited Restriction Lifted for Item 45597 on 2015-08-22T10:00:33Z."]},{"key":"dc:title","label":"Title","values":["Molecularly thin rheological and contact interfaces"]}]}],"canonical_facts":{"dc:contributor":["Polycarpou, Andreas A."],"dc:creator":["Chowdhury, Shahla"],"dc:date":["2013-08-22T16:55:30Z","2015-08-22T10:00:33Z","2013-08"],"dc:description":["A molecularly thin lubricant layer (of the order of 1-2 nanometers thick) has been shown to provide bearing forces at the interface between contacting solid surfaces under light loads and high shear rates. This phenomenon is important, for example, in the head-disk contact in magnetic storage hard disk drives to ensure that some of the contact is sustained by the lubricant layer and thus avoiding damage of the solid surfaces. The magnitude of the normal and tangential bearing forces that the lubricant layer can provide depends on temperature, viscosity of the lubricant, sliding velocity and radius of gyration of the lubricant molecules. This study shows that viscosity has the greatest effect on the load bearing capacity of the molecularly thin lubricant. Thus, by controlling the flash temperature and the ratio of molecularly thin lubricant-to-bulk viscosity, the bearing load carrying capacity of the layer can be controlled. This would allow for the contact to be sustained within the mobile lubricant layer, avoiding solid contact so as to protect the diamond-like carbon coating, and thus reduce wear and potential catastrophic failures. Another part of the thesis is the work on nano-tribological behavior of Hafnium-Diboride thin films. Dense, hard nanocrystalline films of HfBN and multilayer ones of HfB2/HfBN compositions having thickness in the range of 100-600 nm were deposited using chemical vapor deposition (CVD) technique. The roughness values of HfBN film is extremely small, with a value of 5.38-7.63 nm so it is compatible for use as a very smooth surface such as in microscale miniature systems. Nano-indentation and nano-scratch experiments were done to investigate friction and wear behavior of the films. HfBN exhibited lower coefficient of friction (COF) compared to the multilayer HfB2/HfBN. The amorphous as-deposited films were subjected to annealing at 700 oC in order to study their mechanical properties in the post-treatment conditions. In comparison to as-deposited films the annealed films possessed lower COF (COF 0.02 lower). The overall response of the annealed HfBN is outstanding making it compatible for wear resistant, very low roughness coating.","Item withdrawn by Mark Zulauf (zulauf@illinois.edu) on 2013-07-17T19:41:23Z Item was in collections: University of Illinois Theses & Dissertations (ID: 1) No. of bitstreams: 4 1st part.pdf: 103955 bytes, checksum: 5e3a2114b12aef10d5b9cb5a528d96ef (MD5) S.Chowdhury.MS.thesis.pdf: 1873576 bytes, checksum: 4b1aa9b8dcf044cf20aebf01694a32ed (MD5) S.Chowdhury.MS.thesis.pdf: 1873576 bytes, checksum: 4b1aa9b8dcf044cf20aebf01694a32ed (MD5) Chowdhury_Shahla.pdf: 1987570 bytes, checksum: 14c3afe4f461d7a7d501f5c61e490e6a (MD5)","Made available in DSpace on 2013-08-22T16:55:30Z (GMT). No. of bitstreams: 2 Shahla_Chowdhury.pdf: 10199634 bytes, checksum: 8917c1d220107b0e06d69dd39cbdec7b (MD5) license.txt: 4066 bytes, checksum: 75fd1bc71bb8dff3e1204fc76522ac01 (MD5)","Item marked as restricted to the 'Administrator' Group (id=1) by Seth Robbins (srobbins@illinois.edu) on 2013-08-22T16:57:30Z Item is restricted until 2015-08-22T16:57:26Z","Restriction data tranferred 2014-07-01T11:11:46-05:00 Original Data Group with Access Administrator Release Date: 2015-08-22 11:57:26 UTC Reason: Author requested closed access (OA after 2yrs) in Vireo ETD system","Limited Restriction Lifted for Item 45597 on 2015-08-22T10:00:33Z."],"dc:identifier":["http://hdl.handle.net/2142/45615"],"dc:language":["en"],"dc:rights":["Copyright reserved by Shahla Chowdhury"],"dc:subject":["Molecularly thin lubricant","Hard disk drive","Coating"],"dc:title":["Molecularly thin rheological and contact interfaces"],"dc:type":["text"],"thesis:degree_discipline":["Theoretical & Applied Mechans"],"thesis:degree_level":["Thesis"],"thesis:degree_name":["M.S."],"thesis:institution_name":["University of Illinois at Urbana-Champaign"]},"updated_at":"2026-07-22T22:25:36Z"}