{"id":{"repo_id":"uiuc","oai_identifier":"oai:www.ideals.illinois.edu:2142/29434"},"canonical_url":"https://search.dev.ndltd.org/etd/uiuc/oai:www.ideals.illinois.edu:2142/29434","repository":{"repo_id":"uiuc","name":"University of Illinois - Urbana-Champaign","base_url":"https://www.ideals.illinois.edu/oai-pmh"},"display":{"title":"Synthesis, characterization, and photocatalytic activity of tantalum oxide thin films","abstract":"An increasing demand for a low cost alternative for water disinfection and the recent push for green energy has caused an explosion of research in photocatalysis. While TiO2 is considered to be the standard for photocatalysis, there are a number of issues that need to be overcome to push photocatalysis into mainstream applications. In an effort to improve the overall reaction rate, a wider energy gap material, such as Ta2O5, that provides a higher cathodic potential and more flexibility in shifting the energy gap provides a possible alternative. Ta2O5 thin films were synthesized using a sol-gel method and deposited by dip-coating and spin-coating. The thicknesses of the films ranged from 8 nm to 230 nm and were tested to find an optimum thickness based on the quantum efficiency. The photoactivity of the films was measured using a recirculating methylene blue solution. Above 15 nm, the film thickness did not have an effect on the methylene blue degradation rate. To test the premise of being limited by electron-hole transport, the annealing temperature of the films was varied to increase the crystallinity. The films were annealed under a range of temperatures from 450°C to 1200°C. By x ray diffraction measurements, the grain size of the films was found to be relatively stable from 638°C to 1075°C. The films annealed at 1200°C showed the presence of a TaO phase and lacked any indication of a Ta2O5 phase. No correlation between the annealing temperature and photoactivity of the film was found. The photodegradation rate of methylene blue was determined to be limited by surface interactions of the film. A comparison to a TiO2 film synthesized from Degussa P25 powder was used to compare to the Ta2O5 films. The activity was found to be higher for the TiO2 films. However, the amount of catalyst and surface area of the TiO2 were unknown and made conclusive quantitative comparisons challenging.","abstract_html":"An increasing demand for a low cost alternative for water disinfection and the recent push for green energy has caused an explosion of research in photocatalysis. While TiO2 is considered to be the standard for photocatalysis, there are a number of issues that need to be overcome to push photocatalysis into mainstream applications. In an effort to improve the overall reaction rate, a wider energy gap material, such as Ta2O5, that provides a higher cathodic potential and more flexibility in shifting the energy gap provides a possible alternative. Ta2O5 thin films were synthesized using a sol-gel method and deposited by dip-coating and spin-coating. The thicknesses of the films ranged from 8 nm to 230 nm and were tested to find an optimum thickness based on the quantum efficiency. The photoactivity of the films was measured using a recirculating methylene blue solution. Above 15 nm, the film thickness did not have an effect on the methylene blue degradation rate. To test the premise of being limited by electron-hole transport, the annealing temperature of the films was varied to increase the crystallinity. The films were annealed under a range of temperatures from 450°C to 1200°C. By x ray diffraction measurements, the grain size of the films was found to be relatively stable from 638°C to 1075°C. The films annealed at 1200°C showed the presence of a TaO phase and lacked any indication of a Ta2O5 phase. No correlation between the annealing temperature and photoactivity of the film was found. The photodegradation rate of methylene blue was determined to be limited by surface interactions of the film. A comparison to a TiO2 film synthesized from Degussa P25 powder was used to compare to the Ta2O5 films. The activity was found to be higher for the TiO2 films. However, the amount of catalyst and surface area of the TiO2 were unknown and made conclusive quantitative comparisons challenging.","abstract_has_math":false,"creators":["Jensen, Cody"],"institution":"University of Illinois at Urbana-Champaign","degree_name":"M.S.","degree_level":"Thesis","degree_discipline":"Chemical Engineering","degree_department":null,"school":null,"contributors":["Shannon, Mark A.","Cahill, David G."],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2012,"date_issued":"2012-02-01T00:46:16Z","date_published":"2012-02-01T00:46:16Z","updated_at":"2026-07-22T22:25:27Z","subjects":["tantalum oxide","ta2o5","photocatalysis","photocatalyst"],"languages":["en"],"rights":["Copyright 2011 Cody Jensen"],"rights_urls":[],"identifier_entries":[]},"links":{"outbound_url":"http://hdl.handle.net/2142/29434","outbound_label":"Handle","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor","label":"Contributor","values":["Shannon, Mark A.","Cahill, David G."]},{"key":"dc:creator","label":"Author","values":["Jensen, Cody"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date","label":"Dc Date","values":["2012-02-01T00:46:16Z","2014-02-01T11:00:26Z","2011-12"]},{"key":"dc:type","label":"Dc Type","values":["Dissertation / Thesis","text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Chemical Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Thesis"]},{"key":"thesis:degree_name","label":"Degree Name","values":["M.S."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["University of Illinois at Urbana-Champaign"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["tantalum oxide","ta2o5","photocatalysis","photocatalyst"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["Copyright 2011 Cody Jensen"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["http://hdl.handle.net/2142/29434"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["An increasing demand for a low cost alternative for water disinfection and the recent push for green energy has caused an explosion of research in photocatalysis. While TiO2 is considered to be the standard for photocatalysis, there are a number of issues that need to be overcome to push photocatalysis into mainstream applications. In an effort to improve the overall reaction rate, a wider energy gap material, such as Ta2O5, that provides a higher cathodic potential and more flexibility in shifting the energy gap provides a possible alternative. Ta2O5 thin films were synthesized using a sol-gel method and deposited by dip-coating and spin-coating. The thicknesses of the films ranged from 8 nm to 230 nm and were tested to find an optimum thickness based on the quantum efficiency. The photoactivity of the films was measured using a recirculating methylene blue solution. Above 15 nm, the film thickness did not have an effect on the methylene blue degradation rate. To test the premise of being limited by electron-hole transport, the annealing temperature of the films was varied to increase the crystallinity. The films were annealed under a range of temperatures from 450°C to 1200°C. By x ray diffraction measurements, the grain size of the films was found to be relatively stable from 638°C to 1075°C. The films annealed at 1200°C showed the presence of a TaO phase and lacked any indication of a Ta2O5 phase. No correlation between the annealing temperature and photoactivity of the film was found. The photodegradation rate of methylene blue was determined to be limited by surface interactions of the film. A comparison to a TiO2 film synthesized from Degussa P25 powder was used to compare to the Ta2O5 films. The activity was found to be higher for the TiO2 films. However, the amount of catalyst and surface area of the TiO2 were unknown and made conclusive quantitative comparisons challenging.","Item withdrawn by Mark Zulauf (zulauf@illinois.edu) on 2011-12-08T18:25:24Z Item was in collections: University of Illinois Theses & Dissertations (ID: 1) No. of bitstreams: 3 Jensen, Cody.pdf: 1226213 bytes, checksum: 591c9fb50837baa0a6eaef6da6454664 (MD5) Jensen, Cody.docx: 863275 bytes, checksum: 7bbc1534456435bc501d3777ac62c200 (MD5) Jensen, Cody.pdf: 1230805 bytes, checksum: 1a4e039d98d3d24220d086edf8e5d276 (MD5)","Made available in DSpace on 2012-02-01T00:46:16Z (GMT). No. of bitstreams: 3 Jensen, Cody.pdf: 1230805 bytes, checksum: 1a4e039d98d3d24220d086edf8e5d276 (MD5) license.txt: 4061 bytes, checksum: 30cf4e5813e0ad667ca690952e0a35bd (MD5) Jensen, Cody.docx: 863275 bytes, checksum: 7bbc1534456435bc501d3777ac62c200 (MD5)","Item marked as restricted to the 'UIUC Users [automated]' Group (id=2) by William Ingram (wingram2@illinois.edu) on 2012-02-01T00:50:22Z Item is restricted until 2014-02-01T00:50:07Z","Item reinstated by Sarah Shreeves (sshreeve@illinois.edu) on 2014-02-01T11:00:26Z Item was in collections: Dissertations and Theses - Chemical and Biomolecular Engineering (ID: 591) Graduate Theses and Dissertations at Illinois (ID: 204) No. of bitstreams: 4 Jensen, Cody.pdf: 1230805 bytes, checksum: 1a4e039d98d3d24220d086edf8e5d276 (MD5) license.txt: 4061 bytes, checksum: 30cf4e5813e0ad667ca690952e0a35bd (MD5) Jensen, Cody.docx: 863275 bytes, checksum: 7bbc1534456435bc501d3777ac62c200 (MD5) Jensen, Cody.pdf.txt: 70844 bytes, checksum: 84d2330eb3d435c60944990e73628c12 (MD5)","Item released from any restrictions by Sarah Shreeves (sshreeve@illinois.edu) on 2014-02-01T11:00:26Z"]},{"key":"dc:title","label":"Title","values":["Synthesis, characterization, and photocatalytic activity of tantalum oxide thin films"]}]}],"canonical_facts":{"dc:contributor":["Shannon, Mark A.","Cahill, David G."],"dc:creator":["Jensen, Cody"],"dc:date":["2012-02-01T00:46:16Z","2014-02-01T11:00:26Z","2011-12"],"dc:description":["An increasing demand for a low cost alternative for water disinfection and the recent push for green energy has caused an explosion of research in photocatalysis. While TiO2 is considered to be the standard for photocatalysis, there are a number of issues that need to be overcome to push photocatalysis into mainstream applications. In an effort to improve the overall reaction rate, a wider energy gap material, such as Ta2O5, that provides a higher cathodic potential and more flexibility in shifting the energy gap provides a possible alternative. Ta2O5 thin films were synthesized using a sol-gel method and deposited by dip-coating and spin-coating. The thicknesses of the films ranged from 8 nm to 230 nm and were tested to find an optimum thickness based on the quantum efficiency. The photoactivity of the films was measured using a recirculating methylene blue solution. Above 15 nm, the film thickness did not have an effect on the methylene blue degradation rate. To test the premise of being limited by electron-hole transport, the annealing temperature of the films was varied to increase the crystallinity. The films were annealed under a range of temperatures from 450°C to 1200°C. By x ray diffraction measurements, the grain size of the films was found to be relatively stable from 638°C to 1075°C. The films annealed at 1200°C showed the presence of a TaO phase and lacked any indication of a Ta2O5 phase. No correlation between the annealing temperature and photoactivity of the film was found. The photodegradation rate of methylene blue was determined to be limited by surface interactions of the film. A comparison to a TiO2 film synthesized from Degussa P25 powder was used to compare to the Ta2O5 films. The activity was found to be higher for the TiO2 films. However, the amount of catalyst and surface area of the TiO2 were unknown and made conclusive quantitative comparisons challenging.","Item withdrawn by Mark Zulauf (zulauf@illinois.edu) on 2011-12-08T18:25:24Z Item was in collections: University of Illinois Theses & Dissertations (ID: 1) No. of bitstreams: 3 Jensen, Cody.pdf: 1226213 bytes, checksum: 591c9fb50837baa0a6eaef6da6454664 (MD5) Jensen, Cody.docx: 863275 bytes, checksum: 7bbc1534456435bc501d3777ac62c200 (MD5) Jensen, Cody.pdf: 1230805 bytes, checksum: 1a4e039d98d3d24220d086edf8e5d276 (MD5)","Made available in DSpace on 2012-02-01T00:46:16Z (GMT). No. of bitstreams: 3 Jensen, Cody.pdf: 1230805 bytes, checksum: 1a4e039d98d3d24220d086edf8e5d276 (MD5) license.txt: 4061 bytes, checksum: 30cf4e5813e0ad667ca690952e0a35bd (MD5) Jensen, Cody.docx: 863275 bytes, checksum: 7bbc1534456435bc501d3777ac62c200 (MD5)","Item marked as restricted to the 'UIUC Users [automated]' Group (id=2) by William Ingram (wingram2@illinois.edu) on 2012-02-01T00:50:22Z Item is restricted until 2014-02-01T00:50:07Z","Item reinstated by Sarah Shreeves (sshreeve@illinois.edu) on 2014-02-01T11:00:26Z Item was in collections: Dissertations and Theses - Chemical and Biomolecular Engineering (ID: 591) Graduate Theses and Dissertations at Illinois (ID: 204) No. of bitstreams: 4 Jensen, Cody.pdf: 1230805 bytes, checksum: 1a4e039d98d3d24220d086edf8e5d276 (MD5) license.txt: 4061 bytes, checksum: 30cf4e5813e0ad667ca690952e0a35bd (MD5) Jensen, Cody.docx: 863275 bytes, checksum: 7bbc1534456435bc501d3777ac62c200 (MD5) Jensen, Cody.pdf.txt: 70844 bytes, checksum: 84d2330eb3d435c60944990e73628c12 (MD5)","Item released from any restrictions by Sarah Shreeves (sshreeve@illinois.edu) on 2014-02-01T11:00:26Z"],"dc:identifier":["http://hdl.handle.net/2142/29434"],"dc:language":["en"],"dc:rights":["Copyright 2011 Cody Jensen"],"dc:subject":["tantalum oxide","ta2o5","photocatalysis","photocatalyst"],"dc:title":["Synthesis, characterization, and photocatalytic activity of tantalum oxide thin films"],"dc:type":["Dissertation / Thesis","text"],"thesis:degree_discipline":["Chemical Engineering"],"thesis:degree_level":["Thesis"],"thesis:degree_name":["M.S."],"thesis:institution_name":["University of Illinois at Urbana-Champaign"]},"updated_at":"2026-07-22T22:25:27Z"}