{"id":{"repo_id":"uiuc","oai_identifier":"oai:www.ideals.illinois.edu:2142/19992"},"canonical_url":"https://search.dev.ndltd.org/etd/uiuc/oai:www.ideals.illinois.edu:2142/19992","repository":{"repo_id":"uiuc","name":"University of Illinois - Urbana-Champaign","base_url":"https://www.ideals.illinois.edu/oai-pmh"},"display":{"title":"A study of dislocation structures in bulk-strained and in situ TEM strained nickel aluminide alloys","abstract":"In the research work presented in this thesis, the dislocation structures in bulk strained and in situ TEM strained alloys of hypo-stoichiometric Ni$\\sb3$Al with and without boron, and hyper-stoichiometric Ni$\\sb3$Al with boron have been studied. Bulk samples were deformed in tension to 3% and 9% strain and the resulting dislocation structure studied using transmission electron microscopy (TEM). Particular emphasis has been placed on the dislocation structure vicinal to grain boundaries and transgranular cracks. At both strain levels, the dislocation structures are similar near the grain boundaries and transgranular cracks, and are similar to those observed in in situ TEM straining studies.","abstract_html":"In the research work presented in this thesis, the dislocation structures in bulk strained and in situ TEM strained alloys of hypo-stoichiometric Ni$\\sb3$Al with and without boron, and hyper-stoichiometric Ni$\\sb3$Al with boron have been studied. Bulk samples were deformed in tension to 3% and 9% strain and the resulting dislocation structure studied using transmission electron microscopy (TEM). Particular emphasis has been placed on the dislocation structure vicinal to grain boundaries and transgranular cracks. At both strain levels, the dislocation structures are similar near the grain boundaries and transgranular cracks, and are similar to those observed in in situ TEM straining studies.","abstract_has_math":true,"creators":["Subramanian, Raja"],"institution":"University of Illinois at Urbana-Champaign","degree_name":"Ph.D.","degree_level":"Dissertation","degree_discipline":"Materials Science and Engineering","degree_department":null,"school":null,"contributors":["Birnbaum, Howard K."],"advisors":[],"committee_chairs":[],"committee_members":[],"year":1992,"date_issued":"1992","date_published":"1992","updated_at":"2026-07-22T22:25:15Z","subjects":["Engineering, Metallurgy","Engineering, Materials Science"],"languages":["eng"],"rights":["Copyright 1992 Subramanian, Raja"],"rights_urls":[],"identifier_entries":[{"key":"dc:identifier","label":"Identifier","values":["AAI9215890","(UMI)AAI9215890"],"render_values":[{"text":"AAI9215890","href":null,"code":true},{"text":"(UMI)AAI9215890","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/2142/19992","outbound_label":"Handle","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor","label":"Contributor","values":["Birnbaum, Howard K."]},{"key":"dc:creator","label":"Author","values":["Subramanian, Raja"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date","label":"Dc Date","values":["1992","2011-05-07T12:25:19Z","10000-01-01"]},{"key":"dc:type","label":"Dc Type","values":["text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Materials Science and Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Dissertation"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Ph.D."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["University of Illinois at Urbana-Champaign"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Engineering, Metallurgy","Engineering, Materials Science"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["eng"]},{"key":"dc:rights","label":"Dc Rights","values":["Copyright 1992 Subramanian, Raja"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["AAI9215890","(UMI)AAI9215890","http://hdl.handle.net/2142/19992"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["In the research work presented in this thesis, the dislocation structures in bulk strained and in situ TEM strained alloys of hypo-stoichiometric Ni$\\sb3$Al with and without boron, and hyper-stoichiometric Ni$\\sb3$Al with boron have been studied. Bulk samples were deformed in tension to 3% and 9% strain and the resulting dislocation structure studied using transmission electron microscopy (TEM). Particular emphasis has been placed on the dislocation structure vicinal to grain boundaries and transgranular cracks. At both strain levels, the dislocation structures are similar near the grain boundaries and transgranular cracks, and are similar to those observed in in situ TEM straining studies.","Samples have been deformed in tension inside the TEM and the dynamic results have been video recorded. During in situ straining, the glide of dislocations bounding stacking faults in the slip trace ahead of a crack tip, nucleation of partial dislocations at the surface, and the glide of these nucleated partial dislocations in the fault plane have been observed. Pinning of super-Shockley partial dislocations and glide of segments of pinned partial dislocations have been observed. Similar stacking fault structures have been observed near the grain boundaries and the transgranular cracks in bulk strained samples and in in situ TEM deformed samples.","The change in the stacking fault structures at high temperature has been studied in in situ TEM heating experiments. The super-Shockley partial dislocations slowly overcome the pinning obstacles at 773 K and glide to eliminate the faulted area. The effect of planar-fault energies, line tension of the dislocation, and the elastic anisotropy has been discussed.","The Ni segregation at grain boundaries of known $\\Sigma$ value in the alloys, Ni$\\sb{76}$Al$\\sb{24}$ with and without 100 wt ppm boron, and Ni$\\sb{74}$Al$\\sb{26}$ 100 wt ppm boron has been studied by x-ray microanalysis in the HB5 Scanning Transmission Electron Microscope.","Made available in DSpace on 2011-05-07T12:25:19Z (GMT). No. of bitstreams: 2 license.txt: 4922 bytes, checksum: 910b249b4beec47e7ab768910c8f966f (MD5) 9215890.pdf: 5347477 bytes, checksum: 7e9f61db352548b4a66146d1221be668 (MD5) Previous issue date: 1992","Item marked as restricted to the 'UIUC Users [automated]' Group (id=2) by Howard Ding (hding2@illinois.edu) on 2011-05-07T14:40:48Z Item is restricted indefinitely.","Restriction data tranferred 2014-07-01T11:17:34-05:00 Original Data Group with Access UIUC Users [automated] Release Date: none Reason: ETDs are only available to UIUC Users without author permission","ETDs are only available to UIUC Users without author permission","U of I Only"]},{"key":"dc:title","label":"Title","values":["A study of dislocation structures in bulk-strained and in situ TEM strained nickel aluminide alloys"]}]}],"canonical_facts":{"dc:contributor":["Birnbaum, Howard K."],"dc:creator":["Subramanian, Raja"],"dc:date":["1992","2011-05-07T12:25:19Z","10000-01-01"],"dc:description":["In the research work presented in this thesis, the dislocation structures in bulk strained and in situ TEM strained alloys of hypo-stoichiometric Ni$\\sb3$Al with and without boron, and hyper-stoichiometric Ni$\\sb3$Al with boron have been studied. Bulk samples were deformed in tension to 3% and 9% strain and the resulting dislocation structure studied using transmission electron microscopy (TEM). Particular emphasis has been placed on the dislocation structure vicinal to grain boundaries and transgranular cracks. At both strain levels, the dislocation structures are similar near the grain boundaries and transgranular cracks, and are similar to those observed in in situ TEM straining studies.","Samples have been deformed in tension inside the TEM and the dynamic results have been video recorded. During in situ straining, the glide of dislocations bounding stacking faults in the slip trace ahead of a crack tip, nucleation of partial dislocations at the surface, and the glide of these nucleated partial dislocations in the fault plane have been observed. Pinning of super-Shockley partial dislocations and glide of segments of pinned partial dislocations have been observed. Similar stacking fault structures have been observed near the grain boundaries and the transgranular cracks in bulk strained samples and in in situ TEM deformed samples.","The change in the stacking fault structures at high temperature has been studied in in situ TEM heating experiments. The super-Shockley partial dislocations slowly overcome the pinning obstacles at 773 K and glide to eliminate the faulted area. The effect of planar-fault energies, line tension of the dislocation, and the elastic anisotropy has been discussed.","The Ni segregation at grain boundaries of known $\\Sigma$ value in the alloys, Ni$\\sb{76}$Al$\\sb{24}$ with and without 100 wt ppm boron, and Ni$\\sb{74}$Al$\\sb{26}$ 100 wt ppm boron has been studied by x-ray microanalysis in the HB5 Scanning Transmission Electron Microscope.","Made available in DSpace on 2011-05-07T12:25:19Z (GMT). No. of bitstreams: 2 license.txt: 4922 bytes, checksum: 910b249b4beec47e7ab768910c8f966f (MD5) 9215890.pdf: 5347477 bytes, checksum: 7e9f61db352548b4a66146d1221be668 (MD5) Previous issue date: 1992","Item marked as restricted to the 'UIUC Users [automated]' Group (id=2) by Howard Ding (hding2@illinois.edu) on 2011-05-07T14:40:48Z Item is restricted indefinitely.","Restriction data tranferred 2014-07-01T11:17:34-05:00 Original Data Group with Access UIUC Users [automated] Release Date: none Reason: ETDs are only available to UIUC Users without author permission","ETDs are only available to UIUC Users without author permission","U of I Only"],"dc:identifier":["AAI9215890","(UMI)AAI9215890","http://hdl.handle.net/2142/19992"],"dc:language":["eng"],"dc:rights":["Copyright 1992 Subramanian, Raja"],"dc:subject":["Engineering, Metallurgy","Engineering, Materials Science"],"dc:title":["A study of dislocation structures in bulk-strained and in situ TEM strained nickel aluminide alloys"],"dc:type":["text"],"thesis:degree_discipline":["Materials Science and Engineering"],"thesis:degree_level":["Dissertation"],"thesis:degree_name":["Ph.D."],"thesis:institution_name":["University of Illinois at Urbana-Champaign"]},"updated_at":"2026-07-22T22:25:15Z"}