{"id":{"repo_id":"uiuc","oai_identifier":"oai:www.ideals.illinois.edu:2142/19177"},"canonical_url":"https://search.dev.ndltd.org/etd/uiuc/oai:www.ideals.illinois.edu:2142/19177","repository":{"repo_id":"uiuc","name":"University of Illinois - Urbana-Champaign","base_url":"https://www.ideals.illinois.edu/oai-pmh"},"display":{"title":"An investigation into thermomechanical fatigue of metal matrix composites","abstract":"Experimental and theoretical approaches are used to characterize the thermomechanical deformation behavior of metal matrix composites. Experiments on unreinforced and SiC particulate reinforced Al 2xxx-T4 have been conducted under several mechanical strain-temperature phasing conditions. Based on stress range, substantial improvements in fatigue life have been observed. However, based on strain range, the effect of reinforcement on fatigue lives differs depending on the mechanical strain-temperature phasing, temperature, and strain rate. Several deformation mechanisms of unreinforced and reinforced Al 2xxx-T4 have been identified, including void formation, crack initiation, intergranular/transgranular crack growth, oxide penetration at the crack tips, crack deflection due to particle interference, and mean stress effects.","abstract_html":"Experimental and theoretical approaches are used to characterize the thermomechanical deformation behavior of metal matrix composites. Experiments on unreinforced and SiC particulate reinforced Al 2xxx-T4 have been conducted under several mechanical strain-temperature phasing conditions. Based on stress range, substantial improvements in fatigue life have been observed. However, based on strain range, the effect of reinforcement on fatigue lives differs depending on the mechanical strain-temperature phasing, temperature, and strain rate. Several deformation mechanisms of unreinforced and reinforced Al 2xxx-T4 have been identified, including void formation, crack initiation, intergranular/transgranular crack growth, oxide penetration at the crack tips, crack deflection due to particle interference, and mean stress effects.","abstract_has_math":false,"creators":["Karayaka, Metin"],"institution":"University of Illinois at Urbana-Champaign","degree_name":"Ph.D.","degree_level":"Dissertation","degree_discipline":"Mechanical Engineering","degree_department":null,"school":null,"contributors":["Sehitoglu, Huseyin"],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2011,"date_issued":"2011-05-07T11:59:18Z","date_published":"2011-05-07T11:59:18Z","updated_at":"2026-07-22T22:25:12Z","subjects":["Engineering, Mechanical","Engineering, Metallurgy","Engineering, Materials Science"],"languages":["eng"],"rights":["Copyright 1992 Karayaka, Metin"],"rights_urls":[],"identifier_entries":[{"key":"dc:identifier","label":"Identifier","values":["AAI9215835","(UMI)AAI9215835"],"render_values":[{"text":"AAI9215835","href":null,"code":true},{"text":"(UMI)AAI9215835","href":null,"code":true}]}]},"links":{"outbound_url":"http://hdl.handle.net/2142/19177","outbound_label":"Handle","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor","label":"Contributor","values":["Sehitoglu, Huseyin"]},{"key":"dc:creator","label":"Author","values":["Karayaka, Metin"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date","label":"Dc Date","values":["2011-05-07T11:59:18Z","10000-01-01","1992"]},{"key":"dc:type","label":"Dc Type","values":["text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Mechanical Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Dissertation"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Ph.D."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["University of Illinois at Urbana-Champaign"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Engineering, Mechanical","Engineering, Metallurgy","Engineering, Materials Science"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["eng"]},{"key":"dc:rights","label":"Dc Rights","values":["Copyright 1992 Karayaka, Metin"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["AAI9215835","(UMI)AAI9215835","http://hdl.handle.net/2142/19177"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["Experimental and theoretical approaches are used to characterize the thermomechanical deformation behavior of metal matrix composites. Experiments on unreinforced and SiC particulate reinforced Al 2xxx-T4 have been conducted under several mechanical strain-temperature phasing conditions. Based on stress range, substantial improvements in fatigue life have been observed. However, based on strain range, the effect of reinforcement on fatigue lives differs depending on the mechanical strain-temperature phasing, temperature, and strain rate. Several deformation mechanisms of unreinforced and reinforced Al 2xxx-T4 have been identified, including void formation, crack initiation, intergranular/transgranular crack growth, oxide penetration at the crack tips, crack deflection due to particle interference, and mean stress effects.","Theoretical approaches include the development of a general micromechanistic constitutive equation, based on Eshelby's equivalent inclusion theory, and a life prediction methodology for metal matrix composites. Synergistic effects of particulate reinforcement on high temperature thermomechanical behavior are studied. The constitutive model provides insight into the internal stress-strain behavior, including effective and hydrostatic stresses, of both the matrix and the reinforcement developed during cyclic loading conditions. The deformation behavior of the constituents is used to develop an experimentally based micromechanistic life prediction model. The damage caused by internal stresses, oxidation, creep, and fatigue mechanisms as a function of reinforcement volume fraction is quantified for wide range of loading conditions.","Made available in DSpace on 2011-05-07T11:59:18Z (GMT). No. of bitstreams: 2 license.txt: 4922 bytes, checksum: 910b249b4beec47e7ab768910c8f966f (MD5) 9215835.pdf: 5481339 bytes, checksum: 670ee8ae4f235d19f6d778987e98009c (MD5) Previous issue date: 1992","Item marked as restricted to the 'UIUC Users [automated]' Group (id=2) by Howard Ding (hding2@illinois.edu) on 2011-05-07T14:35:11Z Item is restricted indefinitely.","Restriction data tranferred 2014-07-01T11:13:45-05:00 Original Data Group with Access UIUC Users [automated] Release Date: none Reason: ETDs are only available to UIUC Users without author permission","ETDs are only available to UIUC Users without author permission","U of I Only"]},{"key":"dc:title","label":"Title","values":["An investigation into thermomechanical fatigue of metal matrix composites"]}]}],"canonical_facts":{"dc:contributor":["Sehitoglu, Huseyin"],"dc:creator":["Karayaka, Metin"],"dc:date":["2011-05-07T11:59:18Z","10000-01-01","1992"],"dc:description":["Experimental and theoretical approaches are used to characterize the thermomechanical deformation behavior of metal matrix composites. Experiments on unreinforced and SiC particulate reinforced Al 2xxx-T4 have been conducted under several mechanical strain-temperature phasing conditions. Based on stress range, substantial improvements in fatigue life have been observed. However, based on strain range, the effect of reinforcement on fatigue lives differs depending on the mechanical strain-temperature phasing, temperature, and strain rate. Several deformation mechanisms of unreinforced and reinforced Al 2xxx-T4 have been identified, including void formation, crack initiation, intergranular/transgranular crack growth, oxide penetration at the crack tips, crack deflection due to particle interference, and mean stress effects.","Theoretical approaches include the development of a general micromechanistic constitutive equation, based on Eshelby's equivalent inclusion theory, and a life prediction methodology for metal matrix composites. Synergistic effects of particulate reinforcement on high temperature thermomechanical behavior are studied. The constitutive model provides insight into the internal stress-strain behavior, including effective and hydrostatic stresses, of both the matrix and the reinforcement developed during cyclic loading conditions. The deformation behavior of the constituents is used to develop an experimentally based micromechanistic life prediction model. The damage caused by internal stresses, oxidation, creep, and fatigue mechanisms as a function of reinforcement volume fraction is quantified for wide range of loading conditions.","Made available in DSpace on 2011-05-07T11:59:18Z (GMT). No. of bitstreams: 2 license.txt: 4922 bytes, checksum: 910b249b4beec47e7ab768910c8f966f (MD5) 9215835.pdf: 5481339 bytes, checksum: 670ee8ae4f235d19f6d778987e98009c (MD5) Previous issue date: 1992","Item marked as restricted to the 'UIUC Users [automated]' Group (id=2) by Howard Ding (hding2@illinois.edu) on 2011-05-07T14:35:11Z Item is restricted indefinitely.","Restriction data tranferred 2014-07-01T11:13:45-05:00 Original Data Group with Access UIUC Users [automated] Release Date: none Reason: ETDs are only available to UIUC Users without author permission","ETDs are only available to UIUC Users without author permission","U of I Only"],"dc:identifier":["AAI9215835","(UMI)AAI9215835","http://hdl.handle.net/2142/19177"],"dc:language":["eng"],"dc:rights":["Copyright 1992 Karayaka, Metin"],"dc:subject":["Engineering, Mechanical","Engineering, Metallurgy","Engineering, Materials Science"],"dc:title":["An investigation into thermomechanical fatigue of metal matrix composites"],"dc:type":["text"],"thesis:degree_discipline":["Mechanical Engineering"],"thesis:degree_level":["Dissertation"],"thesis:degree_name":["Ph.D."],"thesis:institution_name":["University of Illinois at Urbana-Champaign"]},"updated_at":"2026-07-22T22:25:12Z"}