{"id":{"repo_id":"uiuc","oai_identifier":"oai:www.ideals.illinois.edu:2142/16306"},"canonical_url":"https://search.dev.ndltd.org/etd/uiuc/oai:www.ideals.illinois.edu:2142/16306","repository":{"repo_id":"uiuc","name":"University of Illinois - Urbana-Champaign","base_url":"https://www.ideals.illinois.edu/oai-pmh"},"display":{"title":"The electrical impedance responses of protective oxide scales on stainless steels that are immersed in molten lead-bismuth-eutectic alloy at temperatures up to 600°C","abstract":"This research explored the electrical impedance responses of oxide scales on stainless steel, when the steel was immersed in molten lead-bismuth-eutectic alloy (LBE) at high temperatures (up to 600°C). LBE is a candidate coolant for future fast-neutron-spectrum nuclear reactors and for accelerator-driven nuclear systems, in which the LBE can also act as the spallation target. Stainless steels, out of which such systems are usually fabricated, oxidize in the molten LBE. This research used small-amplitude AC signals to measure the electrical impedances of these oxide layers, as a function of time, temperature, oxygen content of the LBE, and applied DC bias. DC voltages that were apparently generated by the oxide layers themselves were also observed. The resistances were one or more orders of magnitude greater than the published resistances of pressed, sintered pellets of similar oxide material, but they showed a similar Arrhenius dependence on temperature. The resistances declined significantly with reducing levels of oxygen and with applied DC bias, also exhibiting rectifying properties. The capacitance was much less variable. The cumulative result of the research has laid a foundation for the technique of making impedance measurements in LBE and other liquid metals; the technique could be used in the future for further scientific investigations of oxidation in LBE and for engineering applications of in situ monitoring of the oxidation.","abstract_html":"This research explored the electrical impedance responses of oxide scales on stainless steel, when the steel was immersed in molten lead-bismuth-eutectic alloy (LBE) at high temperatures (up to 600°C). LBE is a candidate coolant for future fast-neutron-spectrum nuclear reactors and for accelerator-driven nuclear systems, in which the LBE can also act as the spallation target. Stainless steels, out of which such systems are usually fabricated, oxidize in the molten LBE. This research used small-amplitude AC signals to measure the electrical impedances of these oxide layers, as a function of time, temperature, oxygen content of the LBE, and applied DC bias. DC voltages that were apparently generated by the oxide layers themselves were also observed. The resistances were one or more orders of magnitude greater than the published resistances of pressed, sintered pellets of similar oxide material, but they showed a similar Arrhenius dependence on temperature. The resistances declined significantly with reducing levels of oxygen and with applied DC bias, also exhibiting rectifying properties. The capacitance was much less variable. The cumulative result of the research has laid a foundation for the technique of making impedance measurements in LBE and other liquid metals; the technique could be used in the future for further scientific investigations of oxidation in LBE and for engineering applications of in situ monitoring of the oxidation.","abstract_has_math":false,"creators":["Bolind, Alan M."],"institution":"University of Illinois at Urbana-Champaign","degree_name":"Ph.D.","degree_level":"Dissertation","degree_discipline":"Nuclear Engineering","degree_department":null,"school":null,"contributors":["Stubbins, James F.","Heuser, Brent J.","Jones, Barclay G.","Payne, David A.","Shang, Jian Ku"],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2010,"date_issued":"2010-05-25T15:12:34Z","date_published":"2010-05-25T15:12:34Z","updated_at":"2026-07-22T22:25:09Z","subjects":["lead-bismuth eutectic (LBE)","impedance spectroscopy","liquid-metal corrosion","electrical impedance response","oxidation"],"languages":["en"],"rights":["© 2009 Alan M. Bolind"],"rights_urls":[],"identifier_entries":[]},"links":{"outbound_url":"http://hdl.handle.net/2142/16306","outbound_label":"Handle","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor","label":"Contributor","values":["Stubbins, James F.","Heuser, Brent J.","Jones, Barclay G.","Payne, David A.","Shang, Jian Ku"]},{"key":"dc:creator","label":"Author","values":["Bolind, Alan M."]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date","label":"Dc Date","values":["2010-05-25T15:12:34Z","2009-12"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Nuclear Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Dissertation"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Ph.D."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["University of Illinois at Urbana-Champaign"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["lead-bismuth eutectic (LBE)","impedance spectroscopy","liquid-metal corrosion","electrical impedance response","oxidation"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["© 2009 Alan M. Bolind"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["http://hdl.handle.net/2142/16306"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["This research explored the electrical impedance responses of oxide scales on stainless steel, when the steel was immersed in molten lead-bismuth-eutectic alloy (LBE) at high temperatures (up to 600°C). LBE is a candidate coolant for future fast-neutron-spectrum nuclear reactors and for accelerator-driven nuclear systems, in which the LBE can also act as the spallation target. Stainless steels, out of which such systems are usually fabricated, oxidize in the molten LBE. This research used small-amplitude AC signals to measure the electrical impedances of these oxide layers, as a function of time, temperature, oxygen content of the LBE, and applied DC bias. DC voltages that were apparently generated by the oxide layers themselves were also observed. The resistances were one or more orders of magnitude greater than the published resistances of pressed, sintered pellets of similar oxide material, but they showed a similar Arrhenius dependence on temperature. The resistances declined significantly with reducing levels of oxygen and with applied DC bias, also exhibiting rectifying properties. The capacitance was much less variable. The cumulative result of the research has laid a foundation for the technique of making impedance measurements in LBE and other liquid metals; the technique could be used in the future for further scientific investigations of oxidation in LBE and for engineering applications of in situ monitoring of the oxidation.","Item withdrawn by Mark Zulauf (zulauf@illinois.edu) on 2009-11-13T22:50:30Z Item was in collections: University of Illinois Theses & Dissertations (ID: 1) No. of bitstreams: 2 Bolind_Alan.pdf: 31204963 bytes, checksum: 79b055c6deb3b61f60f83ee1f5b64e9e (MD5) Bolind_Alan.zip: 105045211 bytes, checksum: 93c4d51be061cfcc4da0d48b6d5894fb (MD5)","Made available in DSpace on 2010-05-25T15:12:34Z (GMT). No. of bitstreams: 6 Bolind_Alan.pdf: 31204963 bytes, checksum: 79b055c6deb3b61f60f83ee1f5b64e9e (MD5) Bolind_Alan.zip: 105045211 bytes, checksum: 93c4d51be061cfcc4da0d48b6d5894fb (MD5) Appendix of Figures 09.doc: 100335616 bytes, checksum: c053de43854419022ed89c687dff37c5 (MD5) Thesis 09.doc: 8228864 bytes, checksum: f8f218adee4aeefd2677880a9c3afcd4 (MD5) 1_Bolind_Alan.pdf: 31167311 bytes, checksum: 849158137ad6e8572a55a65c710d41f1 (MD5) license.txt: 4059 bytes, checksum: 8deb50071baf07769e0b234e0a25e078 (MD5)"]},{"key":"dc:title","label":"Title","values":["The electrical impedance responses of protective oxide scales on stainless steels that are immersed in molten lead-bismuth-eutectic alloy at temperatures up to 600°C"]}]}],"canonical_facts":{"dc:contributor":["Stubbins, James F.","Heuser, Brent J.","Jones, Barclay G.","Payne, David A.","Shang, Jian Ku"],"dc:creator":["Bolind, Alan M."],"dc:date":["2010-05-25T15:12:34Z","2009-12"],"dc:description":["This research explored the electrical impedance responses of oxide scales on stainless steel, when the steel was immersed in molten lead-bismuth-eutectic alloy (LBE) at high temperatures (up to 600°C). LBE is a candidate coolant for future fast-neutron-spectrum nuclear reactors and for accelerator-driven nuclear systems, in which the LBE can also act as the spallation target. Stainless steels, out of which such systems are usually fabricated, oxidize in the molten LBE. This research used small-amplitude AC signals to measure the electrical impedances of these oxide layers, as a function of time, temperature, oxygen content of the LBE, and applied DC bias. DC voltages that were apparently generated by the oxide layers themselves were also observed. The resistances were one or more orders of magnitude greater than the published resistances of pressed, sintered pellets of similar oxide material, but they showed a similar Arrhenius dependence on temperature. The resistances declined significantly with reducing levels of oxygen and with applied DC bias, also exhibiting rectifying properties. The capacitance was much less variable. The cumulative result of the research has laid a foundation for the technique of making impedance measurements in LBE and other liquid metals; the technique could be used in the future for further scientific investigations of oxidation in LBE and for engineering applications of in situ monitoring of the oxidation.","Item withdrawn by Mark Zulauf (zulauf@illinois.edu) on 2009-11-13T22:50:30Z Item was in collections: University of Illinois Theses & Dissertations (ID: 1) No. of bitstreams: 2 Bolind_Alan.pdf: 31204963 bytes, checksum: 79b055c6deb3b61f60f83ee1f5b64e9e (MD5) Bolind_Alan.zip: 105045211 bytes, checksum: 93c4d51be061cfcc4da0d48b6d5894fb (MD5)","Made available in DSpace on 2010-05-25T15:12:34Z (GMT). No. of bitstreams: 6 Bolind_Alan.pdf: 31204963 bytes, checksum: 79b055c6deb3b61f60f83ee1f5b64e9e (MD5) Bolind_Alan.zip: 105045211 bytes, checksum: 93c4d51be061cfcc4da0d48b6d5894fb (MD5) Appendix of Figures 09.doc: 100335616 bytes, checksum: c053de43854419022ed89c687dff37c5 (MD5) Thesis 09.doc: 8228864 bytes, checksum: f8f218adee4aeefd2677880a9c3afcd4 (MD5) 1_Bolind_Alan.pdf: 31167311 bytes, checksum: 849158137ad6e8572a55a65c710d41f1 (MD5) license.txt: 4059 bytes, checksum: 8deb50071baf07769e0b234e0a25e078 (MD5)"],"dc:identifier":["http://hdl.handle.net/2142/16306"],"dc:language":["en"],"dc:rights":["© 2009 Alan M. Bolind"],"dc:subject":["lead-bismuth eutectic (LBE)","impedance spectroscopy","liquid-metal corrosion","electrical impedance response","oxidation"],"dc:title":["The electrical impedance responses of protective oxide scales on stainless steels that are immersed in molten lead-bismuth-eutectic alloy at temperatures up to 600°C"],"thesis:degree_discipline":["Nuclear Engineering"],"thesis:degree_level":["Dissertation"],"thesis:degree_name":["Ph.D."],"thesis:institution_name":["University of Illinois at Urbana-Champaign"]},"updated_at":"2026-07-22T22:25:09Z"}