{"id":{"repo_id":"uiuc","oai_identifier":"oai:www.ideals.illinois.edu:2142/102447"},"canonical_url":"https://search.dev.ndltd.org/etd/uiuc/oai:www.ideals.illinois.edu:2142/102447","repository":{"repo_id":"uiuc","name":"University of Illinois - Urbana-Champaign","base_url":"https://www.ideals.illinois.edu/oai-pmh"},"display":{"title":"Understanding effects of pre-soaked lightweight aggregate on volume stability of mortar and concrete mixtures","abstract":"Shrinkage cracking is a predominant deterioration mechanism greatly affecting the durability and integrity of concrete structures. This is especially the case for concrete bridge decks due to the large surface-to-volume ratio of these types of structures, which results in a high rate of moisture loss from the exposed surface. An extensive body of literature suggests that pre-soaked lightweight aggregate (LWA) is greatly beneficial for curing concrete internally and reducing autogenous shrinkage by providing additional water reservoirs for the mixture. However, the literature on the effect of LWA on drying shrinkage is limited. Therefore, the main objective of this work is to improve our understanding of the influence of LWA on microstructure development and shrinkage of mortar and concrete mixtures in an unsealed condition. The effect of LWA on drying shrinkage under different boundary conditions is examined. By varying the number of faces exposed to the surrounding unsaturated environment, the severity of drying condition is altered and its effect on drying shrinkage of internally cured mixtures is studied. The efficiency of LWA in reducing drying shrinkage is shown to be significantly dependent upon the severity of the drying condition, and the duration and type (sealed versus moist) of external curing. The effect of sample size on the efficiency of LWA in reducing drying shrinkage is also studied. It is shown that incorporation of LWA to internally cure concrete may be an inadequate shrinkage compensating strategy, particularly in a severe drying condition. Nonetheless, internally cured mixtures exhibited a denser microstructure which can be advantageous in terms of durability. An attempt was made to design a low-shrinkage internally cured mixture using expansive cement. The expansive nature of Calcium Sulfoaluminate (CSA)–based cements can be used to enhance the resistance against shrinkage cracking by inducing compressive stress in concrete. It is shown that combining CSA with internal curing is mutually beneficial; ordinary Portland cement (OPC)–CSA mixtures show increased hydration of CSA and a denser microstructure when LWA is added to the mixture. Furthermore, the addition of CSA to the mixtures with LWA results in a positive deformation even in an unsealed condition. Moreover, moisture movement in internally cured cement-based materials is modeled using diffusion equation to better understand the characteristics of LWA that influence its effectiveness. A two-dimensional diffusion equation in Cartesian coordinates is used to model moisture movement inside cement-based materials. After defining the governing equation and verifying its various components, the model is solved analytically. The output of the model is compared with experimental measurements of moisture loss and local moisture content to ensure the accuracy of the model. Influence of absorption and desorption characteristics of LWA on its effectiveness in resaturating the emptied pores is then studied using the model.","abstract_html":"Shrinkage cracking is a predominant deterioration mechanism greatly affecting the durability and integrity of concrete structures. This is especially the case for concrete bridge decks due to the large surface-to-volume ratio of these types of structures, which results in a high rate of moisture loss from the exposed surface. An extensive body of literature suggests that pre-soaked lightweight aggregate (LWA) is greatly beneficial for curing concrete internally and reducing autogenous shrinkage by providing additional water reservoirs for the mixture. However, the literature on the effect of LWA on drying shrinkage is limited. Therefore, the main objective of this work is to improve our understanding of the influence of LWA on microstructure development and shrinkage of mortar and concrete mixtures in an unsealed condition. The effect of LWA on drying shrinkage under different boundary conditions is examined. By varying the number of faces exposed to the surrounding unsaturated environment, the severity of drying condition is altered and its effect on drying shrinkage of internally cured mixtures is studied. The efficiency of LWA in reducing drying shrinkage is shown to be significantly dependent upon the severity of the drying condition, and the duration and type (sealed versus moist) of external curing. The effect of sample size on the efficiency of LWA in reducing drying shrinkage is also studied. It is shown that incorporation of LWA to internally cure concrete may be an inadequate shrinkage compensating strategy, particularly in a severe drying condition. Nonetheless, internally cured mixtures exhibited a denser microstructure which can be advantageous in terms of durability. An attempt was made to design a low-shrinkage internally cured mixture using expansive cement. The expansive nature of Calcium Sulfoaluminate (CSA)–based cements can be used to enhance the resistance against shrinkage cracking by inducing compressive stress in concrete. It is shown that combining CSA with internal curing is mutually beneficial; ordinary Portland cement (OPC)–CSA mixtures show increased hydration of CSA and a denser microstructure when LWA is added to the mixture. Furthermore, the addition of CSA to the mixtures with LWA results in a positive deformation even in an unsealed condition. Moreover, moisture movement in internally cured cement-based materials is modeled using diffusion equation to better understand the characteristics of LWA that influence its effectiveness. A two-dimensional diffusion equation in Cartesian coordinates is used to model moisture movement inside cement-based materials. After defining the governing equation and verifying its various components, the model is solved analytically. The output of the model is compared with experimental measurements of moisture loss and local moisture content to ensure the accuracy of the model. Influence of absorption and desorption characteristics of LWA on its effectiveness in resaturating the emptied pores is then studied using the model.","abstract_has_math":false,"creators":["Ardeshirilajimi, Ardavan"],"institution":"University of Illinois at Urbana-Champaign","degree_name":"Ph.D.","degree_level":"Dissertation","degree_discipline":"Civil Engineering","degree_department":null,"school":null,"contributors":["Mondal, Paramita","Lange, David A.","Popovics, John S.","Roesler, Jeffery R."],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2019,"date_issued":"2019-02-06T19:36:07Z","date_published":"2019-02-06T19:36:07Z","updated_at":"2026-07-22T22:24:40Z","subjects":["Lightweight Aggregate, Shrinkage Cracking, Concrete, Internal Curing"],"languages":["en"],"rights":["Copyright 2018 Ardavan Ardeshirilajimi"],"rights_urls":[],"identifier_entries":[]},"links":{"outbound_url":"http://hdl.handle.net/2142/102447","outbound_label":"Handle","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor","label":"Contributor","values":["Mondal, Paramita","Lange, David A.","Popovics, John S.","Roesler, Jeffery R."]},{"key":"dc:creator","label":"Author","values":["Ardeshirilajimi, Ardavan"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date","label":"Dc Date","values":["2019-02-06T19:36:07Z","2018-11-30","2018-12"]},{"key":"dc:type","label":"Dc Type","values":["text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Civil Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Dissertation"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Ph.D."]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["University of Illinois at Urbana-Champaign"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Lightweight Aggregate, Shrinkage Cracking, Concrete, Internal Curing"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["Copyright 2018 Ardavan Ardeshirilajimi"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["http://hdl.handle.net/2142/102447"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["Shrinkage cracking is a predominant deterioration mechanism greatly affecting the durability and integrity of concrete structures. This is especially the case for concrete bridge decks due to the large surface-to-volume ratio of these types of structures, which results in a high rate of moisture loss from the exposed surface. An extensive body of literature suggests that pre-soaked lightweight aggregate (LWA) is greatly beneficial for curing concrete internally and reducing autogenous shrinkage by providing additional water reservoirs for the mixture. However, the literature on the effect of LWA on drying shrinkage is limited. Therefore, the main objective of this work is to improve our understanding of the influence of LWA on microstructure development and shrinkage of mortar and concrete mixtures in an unsealed condition. The effect of LWA on drying shrinkage under different boundary conditions is examined. By varying the number of faces exposed to the surrounding unsaturated environment, the severity of drying condition is altered and its effect on drying shrinkage of internally cured mixtures is studied. The efficiency of LWA in reducing drying shrinkage is shown to be significantly dependent upon the severity of the drying condition, and the duration and type (sealed versus moist) of external curing. The effect of sample size on the efficiency of LWA in reducing drying shrinkage is also studied. It is shown that incorporation of LWA to internally cure concrete may be an inadequate shrinkage compensating strategy, particularly in a severe drying condition. Nonetheless, internally cured mixtures exhibited a denser microstructure which can be advantageous in terms of durability. An attempt was made to design a low-shrinkage internally cured mixture using expansive cement. The expansive nature of Calcium Sulfoaluminate (CSA)–based cements can be used to enhance the resistance against shrinkage cracking by inducing compressive stress in concrete. It is shown that combining CSA with internal curing is mutually beneficial; ordinary Portland cement (OPC)–CSA mixtures show increased hydration of CSA and a denser microstructure when LWA is added to the mixture. Furthermore, the addition of CSA to the mixtures with LWA results in a positive deformation even in an unsealed condition. Moreover, moisture movement in internally cured cement-based materials is modeled using diffusion equation to better understand the characteristics of LWA that influence its effectiveness. A two-dimensional diffusion equation in Cartesian coordinates is used to model moisture movement inside cement-based materials. After defining the governing equation and verifying its various components, the model is solved analytically. The output of the model is compared with experimental measurements of moisture loss and local moisture content to ensure the accuracy of the model. Influence of absorption and desorption characteristics of LWA on its effectiveness in resaturating the emptied pores is then studied using the model.","Submission original under an indefinite embargo labeled 'Open Access'. The submission was exported from vireo on 2019-02-05 without embargo terms","The student, Ardavan Ardeshirilajimi, accepted the attached license on 2018-11-28 at 21:46.","The student, Ardavan Ardeshirilajimi, submitted this Dissertation for approval on 2018-11-28 at 21:50.","This Dissertation was approved for publication on 2018-11-30 at 08:32.","DSpace SAF Submission Ingestion Package generated from Vireo submission #13136 on 2019-02-05 at 11:09:49","Made available in DSpace on 2019-02-06T19:36:07Z (GMT). No. of bitstreams: 3 ARDESHIRILAJIMI-DISSERTATION-2018.pdf: 14726517 bytes, checksum: 031217ea94faffe79d0b01ff27def945 (MD5) LICENSE.txt: 4220 bytes, checksum: 93c30e427f9d8a37251d5de177b5252f (MD5) PROQUEST_LICENSE.txt: 4566 bytes, checksum: dc15c362e0fbbaabb599ba44419c2e36 (MD5) Previous issue date: 2018-11-30"]},{"key":"dc:format","label":"Dc Format","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["Understanding effects of pre-soaked lightweight aggregate on volume stability of mortar and concrete mixtures"]}]}],"canonical_facts":{"dc:contributor":["Mondal, Paramita","Lange, David A.","Popovics, John S.","Roesler, Jeffery R."],"dc:creator":["Ardeshirilajimi, Ardavan"],"dc:date":["2019-02-06T19:36:07Z","2018-11-30","2018-12"],"dc:description":["Shrinkage cracking is a predominant deterioration mechanism greatly affecting the durability and integrity of concrete structures. This is especially the case for concrete bridge decks due to the large surface-to-volume ratio of these types of structures, which results in a high rate of moisture loss from the exposed surface. An extensive body of literature suggests that pre-soaked lightweight aggregate (LWA) is greatly beneficial for curing concrete internally and reducing autogenous shrinkage by providing additional water reservoirs for the mixture. However, the literature on the effect of LWA on drying shrinkage is limited. Therefore, the main objective of this work is to improve our understanding of the influence of LWA on microstructure development and shrinkage of mortar and concrete mixtures in an unsealed condition. The effect of LWA on drying shrinkage under different boundary conditions is examined. By varying the number of faces exposed to the surrounding unsaturated environment, the severity of drying condition is altered and its effect on drying shrinkage of internally cured mixtures is studied. The efficiency of LWA in reducing drying shrinkage is shown to be significantly dependent upon the severity of the drying condition, and the duration and type (sealed versus moist) of external curing. The effect of sample size on the efficiency of LWA in reducing drying shrinkage is also studied. It is shown that incorporation of LWA to internally cure concrete may be an inadequate shrinkage compensating strategy, particularly in a severe drying condition. Nonetheless, internally cured mixtures exhibited a denser microstructure which can be advantageous in terms of durability. An attempt was made to design a low-shrinkage internally cured mixture using expansive cement. The expansive nature of Calcium Sulfoaluminate (CSA)–based cements can be used to enhance the resistance against shrinkage cracking by inducing compressive stress in concrete. It is shown that combining CSA with internal curing is mutually beneficial; ordinary Portland cement (OPC)–CSA mixtures show increased hydration of CSA and a denser microstructure when LWA is added to the mixture. Furthermore, the addition of CSA to the mixtures with LWA results in a positive deformation even in an unsealed condition. Moreover, moisture movement in internally cured cement-based materials is modeled using diffusion equation to better understand the characteristics of LWA that influence its effectiveness. A two-dimensional diffusion equation in Cartesian coordinates is used to model moisture movement inside cement-based materials. After defining the governing equation and verifying its various components, the model is solved analytically. The output of the model is compared with experimental measurements of moisture loss and local moisture content to ensure the accuracy of the model. Influence of absorption and desorption characteristics of LWA on its effectiveness in resaturating the emptied pores is then studied using the model.","Submission original under an indefinite embargo labeled 'Open Access'. The submission was exported from vireo on 2019-02-05 without embargo terms","The student, Ardavan Ardeshirilajimi, accepted the attached license on 2018-11-28 at 21:46.","The student, Ardavan Ardeshirilajimi, submitted this Dissertation for approval on 2018-11-28 at 21:50.","This Dissertation was approved for publication on 2018-11-30 at 08:32.","DSpace SAF Submission Ingestion Package generated from Vireo submission #13136 on 2019-02-05 at 11:09:49","Made available in DSpace on 2019-02-06T19:36:07Z (GMT). No. of bitstreams: 3 ARDESHIRILAJIMI-DISSERTATION-2018.pdf: 14726517 bytes, checksum: 031217ea94faffe79d0b01ff27def945 (MD5) LICENSE.txt: 4220 bytes, checksum: 93c30e427f9d8a37251d5de177b5252f (MD5) PROQUEST_LICENSE.txt: 4566 bytes, checksum: dc15c362e0fbbaabb599ba44419c2e36 (MD5) Previous issue date: 2018-11-30"],"dc:format":["application/pdf"],"dc:identifier":["http://hdl.handle.net/2142/102447"],"dc:language":["en"],"dc:rights":["Copyright 2018 Ardavan Ardeshirilajimi"],"dc:subject":["Lightweight Aggregate, Shrinkage Cracking, Concrete, Internal Curing"],"dc:title":["Understanding effects of pre-soaked lightweight aggregate on volume stability of mortar and concrete mixtures"],"dc:type":["text"],"thesis:degree_discipline":["Civil Engineering"],"thesis:degree_level":["Dissertation"],"thesis:degree_name":["Ph.D."],"thesis:institution_name":["University of Illinois at Urbana-Champaign"]},"updated_at":"2026-07-22T22:24:40Z"}