If this is your thesis or dissertation, and want to learn how to access it or for more information about readership statistics, contact us at STARS@ucf.edu
","Master of Science (M.S.)","College of Engineering and Computer Science","Mechanical, Materials, and Aerospace Engineering","Materials Science and Engineering"]},{"key":"dc:description.abstract","label":"Abstract","values":["In the present study, the formation and the evolution of lamellar structures in different Al-Ag alloys were investigated by transmission electron microscopy (TEM). Plates of the hexagonal [gamma] phase form semi-coherently on the {111} planes of the face centered cubic lattice of the alloy after the formation of Guinier-Preston zones. Guinier-Preston zones are metastable coherent preprecipitates which are silver rich in the aluminum-rich Al-Ag alloys. The decomposition of aluminum rich Al-Ag alloys, particularly the sequence of the later stages of precipitate formation was studied. With scanning electron microscopy and high-resolution transmission electron microscopy the development of the [gamma] phase was investigated. Samples cut from different Al-Ag alloys were homogenized at temperatures between 530 degrees C to 560 degrees C to obtain a single phase f.c.c solid solution. The samples were then quenched to room temperature, followed by heat treatments at temperatures between 140 degrees C and 220 degrees C for varying lengths of times. While Guinier-Preston zones increase in diameter with increasing aging duration, silver rich platelets of the [gamma] phase form. The [gamma] phase is the next metastable phase in the decomposition sequence before finally the [gamma] phase transforms to the stable silver-rich phase, termed [gamma]. For samples with silver contents above 12 at.% a parallel lamellar alignment of fine [gamma] plates and Alrich matrix is found after extended heat treatments. For all alloys with Ag concentrations below 12 at.% individual [gamma] plates are found on all four possible (111) planes of the [alpha] matrix. A method is presented to calibrate the medium-magnification high-angle annular dark-field contrast in scanning transmission electron microscopy. This calibration allows for the quantitative measurement of plate thicknesses from high-angle annular dark-field scanning transmission electron micrographs of Ag2Al plates inclined to the electron beam. Results from these measurements are in good agreement with direct bright-field micrographs of plates viewed edge-on."]},{"key":"dc:format","label":"Dc Format","values":["application/pdf"]},{"key":"dc:title","label":"Title","values":["Evolution Of Lamellar Structures In Al-ag Alloys"]}]}],"canonical_facts":{"dc:contributor":["Heinrich, Helge"],"dc:creator":["Senapati, Sephalika"],"dc:description":["If this is your thesis or dissertation, and want to learn how to access it or for more information about readership statistics, contact us at STARS@ucf.edu
","Master of Science (M.S.)","College of Engineering and Computer Science","Mechanical, Materials, and Aerospace Engineering","Materials Science and Engineering"],"dc:description.abstract":["In the present study, the formation and the evolution of lamellar structures in different Al-Ag alloys were investigated by transmission electron microscopy (TEM). Plates of the hexagonal [gamma] phase form semi-coherently on the {111} planes of the face centered cubic lattice of the alloy after the formation of Guinier-Preston zones. Guinier-Preston zones are metastable coherent preprecipitates which are silver rich in the aluminum-rich Al-Ag alloys. The decomposition of aluminum rich Al-Ag alloys, particularly the sequence of the later stages of precipitate formation was studied. With scanning electron microscopy and high-resolution transmission electron microscopy the development of the [gamma] phase was investigated. Samples cut from different Al-Ag alloys were homogenized at temperatures between 530 degrees C to 560 degrees C to obtain a single phase f.c.c solid solution. The samples were then quenched to room temperature, followed by heat treatments at temperatures between 140 degrees C and 220 degrees C for varying lengths of times. While Guinier-Preston zones increase in diameter with increasing aging duration, silver rich platelets of the [gamma] phase form. The [gamma] phase is the next metastable phase in the decomposition sequence before finally the [gamma] phase transforms to the stable silver-rich phase, termed [gamma]. For samples with silver contents above 12 at.% a parallel lamellar alignment of fine [gamma] plates and Alrich matrix is found after extended heat treatments. For all alloys with Ag concentrations below 12 at.% individual [gamma] plates are found on all four possible (111) planes of the [alpha] matrix. A method is presented to calibrate the medium-magnification high-angle annular dark-field contrast in scanning transmission electron microscopy. This calibration allows for the quantitative measurement of plate thicknesses from high-angle annular dark-field scanning transmission electron micrographs of Ag2Al plates inclined to the electron beam. Results from these measurements are in good agreement with direct bright-field micrographs of plates viewed edge-on."],"dc:format":["application/pdf"],"dc:identifier":["CFE0000874"],"dc:identifier.uri":["https://stars.library.ucf.edu/etd/617"],"dc:language":["English"],"dc:subject":["TEM","HRTEM","HAADF-STEM","Engineering","Materials Science and Engineering"],"dc:title":["Evolution Of Lamellar Structures In Al-ag Alloys"],"dc:type":["Masters Thesis (Open Access)"]},"updated_at":"2026-07-24T05:08:59Z"}