Long-Term Performance of HDPE Geomembranes as Landfill Liners
type: CreativeWork
description: High density polyethylene (HDPE) geomembranes are normally used as part of a composite liner for waste containment facilities such as municipal solid waste (MSW) landfills and heap leach pads. Field conditions, which include physical stresses on the geomembrane, elevated operating temperatures, and contact with leachate constituents, have the potential to affect the service life of the HDPE geomembranes. This thesis examined the long-term performance of different HDPE geomembranes based on both conventional laboratory accelerated immersion tests and simulated landfill liner tests. A 1.5mm HDPE geomembrane was immersed in different synthetic leachates at different temperatures in order to evaluate the effects of leachate chemical constituents on the depletion of antioxidants. The results showed that a basic leachate with trace metals, surfactant, and a reducing agent was the most appropriate for evaluating the potential degradation of HDPE geomembranes. A similar immersion test was performed to evaluate the effects of thickness on the ageing of HDPE geomembranes. Three commercially available HDPE geomembranes having nominal thicknesses of 1.5, 2.0, and 2.5mm were immersed in a synthetic leachate at four different temperatures in this experiment. The results showed that a thicker geomembrane may have a longer service life if other things are similar. The depletion of antioxidants from a 1.5mm thick HDPE geomembrane was examined by conducting accelerated ageing tests at 55, 70, and 85oC under simulated landfill liner conditions. The results showed that the antioxidant depletion rate was consistently lower for the simulated landfill liner tests compared to the leachate immersion tests. The effectiveness of the aged HDPE geomembrane on the migration of volatile organic compounds (VOCs) was examined by conducting diffusion and partitioning tests using both unaged and aged HDPE geomembranes. The results showed that the ageing of HDPE geomembranes did not increase diffusive…
abstract: High density polyethylene (HDPE) geomembranes are normally used as part of a composite liner for waste containment facilities such as municipal solid waste (MSW) landfills and heap leach pads. Field conditions, which include physical stresses on the geomembrane, elevated operating temperatures, and contact with leachate constituents, have the potential to affect the service life of the HDPE geomembranes. This thesis examined the long-term performance of different HDPE geomembranes based on both conventional laboratory accelerated immersion tests and simulated landfill liner tests. A 1.5mm HDPE geomembrane was immersed in different synthetic leachates at different temperatures in order to evaluate the effects of leachate chemical constituents on the depletion of antioxidants. The results showed that a basic leachate with trace metals, surfactant, and a reducing agent was the most appropriate for evaluating the potential degradation of HDPE geomembranes. A similar immersion test was performed to evaluate the effects of thickness on the ageing of HDPE geomembranes. Three commercially available HDPE geomembranes having nominal thicknesses of 1.5, 2.0, and 2.5mm were immersed in a synthetic leachate at four different temperatures in this experiment. The results showed that a thicker geomembrane may have a longer service life if other things are similar. The depletion of antioxidants from a 1.5mm thick HDPE geomembrane was examined by conducting accelerated ageing tests at 55, 70, and 85oC under simulated landfill liner conditions. The results showed that the antioxidant depletion rate was consistently lower for the simulated landfill liner tests compared to the leachate immersion tests. The effectiveness of the aged HDPE geomembrane on the migration of volatile organic compounds (VOCs) was examined by conducting diffusion and partitioning tests using both unaged and aged HDPE geomembranes. The results showed that the ageing of HDPE geomembranes did not increase diffusive…
author: Islam, Mohammad
language: eng
keywords: Antioxidant, Degradation, Diffusive Migration, Geomembrane, HDPE, Landfill, Leachate, Long-Term Performance, Service Life, Simulated Landfill Liner, Temperature, Thickness, Volatile Organic Compounds, Geoenvironmental Engineering, Geotechnical Engineering, Civil Engineering
date published: 2009-02-02T19:22:03Z
date modified: 2026-07-27T20:35:23Z
provider: Queens University
publisher: Networked Digital Library of Theses and Dissertations
type: WebPage
source organization: Queens University

PropertyValue
property ID: Handle
value: http://hdl.handle.net/1974/1686