BSCCO superconductors processed by the glass-ceramic route

Glassy Bi-Sr-Ca-Cu-O (BSCCO) precursors were prepared by different melt-quenching methods to investigate the melt properties of the BSCCO system before the crystallization investigations were started. In order to fabricate superconductors having high critical temperature and current density using the glass-ceramic route, it is necessary to clarify the total chemical composition of the quenched precursor. For the first time the total chemical composition of such precursors has been directly measured by the direct element analysis and correlated with the taken process steps. The results from the element analysis demonstrated significant chemical deviations in composition with respect to the starting composition and strong chemical inhomogeneities of the sample. The crystallization dependence was investigated on numerous parameters for the BSCCO system such as initial composition, atmosphere, Sr:Ca ratio, average valence state of the glassy precursor and the dependence of Bi substitution by Pb. It could be demonstrated that the copper valence dependence on the phase formation and crystallization of the high-TC phase plays an important role in the BSCCO system. It could also be demonstrated that the smallest chemical deviation could strongly influence the phase formation in dependence of melt temperature, influencing not only the average copper valence but also the different cation concentrations. From literature there are barely any results or conclusions drawn of the chemical composition of the quenched glassy precursors that however is critical to control the crystallization behavior and understanding the influences on the superconductive properties as demonstrated in this work.

Level thesis:degree_level

thesis.doctoral

Grantor dc:publisher

Technische Universität Dresden

Year

2009

Author dc:creator

• Nilsson, Andreas

Contributors dc:contributor

• Wetzig, Klaus
• Eckert, Jürgen
• Komatsu, Takayuki

• glass-ceramic
• BSCCO
• superconductor
• oxygen
• phase formation,
• Supraleiter
• Glas-Keramik
• Amorph
• Sauerstoff