Sensitivity Analysis of Interface Fatigue Crack Propagation in Elastic Composite Laminates
type: CreativeWork
description: Composite laminates are an important subject of modern technology and engineering. The most common mode of failure in these materials is probably interlaminar fracture (delamination). Delamination growth under applied fatigue loads usually leads to structural integrity loss of the composite laminate, and hence its catastrophic failure. It is known that several parameters can affect the fatigue fracture performance of laminates. These include the constituent material properties, composite geometry, fatigue load variables or environmental factors. The knowledge about effects of these parameters on fatigue delamination growth can lead to a better understanding of composite fatigue fracture behaviour. Effects of some of these parameters can be elucidated by undertaking appropriate sensitivity analysis combined with the finite element method (FEM) and related software. The purpose of this work was three-fold. The first goal was the elaboration and computational implementation of FEM-based numerical strategies for the sensitivity analysis of interface fatigue crack propagation in elastic composite laminates. The second goal of this work was the numerical determination and investigation of displacement and stress fields near the crack tip, contact pressures along crack surfaces, mixed mode angle, energy release rate and the number of cumulative fatigue cycles. The third aim of the present study was to use the developed strategies to evaluate numerically the sensitivity gradients of the total energy release rate and fatigue life with respect to design variables of the curved boron/epoxy-aluminium (B/Ep-Al) composite laminate in two different material configurations under cyclic shear of constant amplitude. This study provided novel strategies for undertaking sensitivity analysis of the delamination growth under fatigue loads for elastic composite laminates using the package ANSYS. The numerical results of the work shed more light on mechanisms of interfacial crack propagati…
abstract: Composite laminates are an important subject of modern technology and engineering. The most common mode of failure in these materials is probably interlaminar fracture (delamination). Delamination growth under applied fatigue loads usually leads to structural integrity loss of the composite laminate, and hence its catastrophic failure. It is known that several parameters can affect the fatigue fracture performance of laminates. These include the constituent material properties, composite geometry, fatigue load variables or environmental factors. The knowledge about effects of these parameters on fatigue delamination growth can lead to a better understanding of composite fatigue fracture behaviour. Effects of some of these parameters can be elucidated by undertaking appropriate sensitivity analysis combined with the finite element method (FEM) and related software. The purpose of this work was three-fold. The first goal was the elaboration and computational implementation of FEM-based numerical strategies for the sensitivity analysis of interface fatigue crack propagation in elastic composite laminates. The second goal of this work was the numerical determination and investigation of displacement and stress fields near the crack tip, contact pressures along crack surfaces, mixed mode angle, energy release rate and the number of cumulative fatigue cycles. The third aim of the present study was to use the developed strategies to evaluate numerically the sensitivity gradients of the total energy release rate and fatigue life with respect to design variables of the curved boron/epoxy-aluminium (B/Ep-Al) composite laminate in two different material configurations under cyclic shear of constant amplitude. This study provided novel strategies for undertaking sensitivity analysis of the delamination growth under fatigue loads for elastic composite laminates using the package ANSYS. The numerical results of the work shed more light on mechanisms of interfacial crack propagati…
author: Figiel, Lukasz
keywords: Schichtverbundwerkstoffe, Delaminationen, Sensitivitätsanalyse, FE-Methode, Composite Laminates, Delaminations, Sensitivity Analysis, Finite Element Method
date published: 2004-11-01
date modified: 2026-07-24T03:58:02Z
provider: QUCOSA
publisher: Networked Digital Library of Theses and Dissertations
type: WebPage
source organization: Technische Universität Dresden