Präparation und Charakterisierung ferroelektrischer perowskitischer Multilagen.

This work deals with the structural and dielectric properties of Bariumtitanate (BTO) / Strontiumtitanate (STO) superlattices. The investigations were carried during the research for a doctoral thesis on the IFW Dresden, Institute for Metallic Materials (under supervision of Prof. Schulz). These multilayers have been prepared on single crystalline STO of (100) and (111) orientated substrates. All films where grown in an epitaxial mode. Additional superlattices and Bariumstrontiumtitanate (BSTO) thin films on silicon substrates with platinum bottom electrodes have been prepared. Thereby, (111) fibre-textured polycrystalline superlattices were produced. According to our knowledge this result was achieved for the first time (is unique in the world at the moment). According to high resolution TEM investigations of (001) oriented superlattices multilayers with atomically thin interfaces without noticeable interdiffusion have been prepared. XRD pattern of a multilayer consisting of BTO and STO monolayers that have only a thickness adequate one unit cell of BTO respective STO confirm this assumption. Multilayers on (111) oriented STO substrates show a much higher interface roughness than (001) orientated films. Regarding to the examinations in this thesis it is suggested that the roughness is correlated with the reduction of internal stresses by deformation of the stack and not with interdiffusion between the monolayers. For electrical measurements the film thickness has been varied from 30 nm to 300 nm and the periodicity in the range from 0.8 nm to 20 nm. Additionally, BSTO films of equivalent thickness and integral chemical composition were produced. Dielectical measurements were carried out in the temperature range from 20 K to 600 K and hysteresis measurements were done. It has to be pointed out, that multilayers have always lower dielectrical performances then BSTO films. In all cases the dielectric constant (DC) decreases with decreasing film thickness. Multilayers of a small periodicity show the highest DC?s, decreasing with increasing monolayer thickness in all cases. The maximum of DC shifted with decreasing film thickness to higher temperatures thus correlating with an increase of the out of plane lattice parameter. In this paper the mismatch between the stack respectivly the BSTO layers and the substrate has widely been discussed. In the case of BSTO the dielectric data can be qualitatively explained with the theory of strained films, developed mainly by Pertsev, under the assumption of a strain gradient in the thin film. Strain effects do also play an important role in ferroelectric multilayers as well as size and coupling effects between the monolayers. An adequate theory for the description of the dielectric behaviour of the ferroelectric superlattice produced during this research does yet not exist. Some thesis where pointed out, which effects have to be essentially included in to a consistent theory of ferroelectric multilayer. Some practical tips are also given, how to prepare monolayers and superlattices with very high DC and exellent hysteretic behaviour.

Level thesis:degree_level

thesis.doctoral

Grantor dc:publisher

Technische Universität Dresden

Year

2004

Author dc:creator

• Köbernik, Gert

Contributors dc:contributor

• Schultz, Ludwig
• Weiss, François
• Eng, Lukas

• Bariumtitanat
• Dielektrizitätskonstante
• Dünnschicht
• Epitaxie
• Ferroelektrisch
• Laser Abscheidung
• Multilagen
• Perowskite
• Strontiumtitanat
• Epitaxy
• Ferroelectric properties
• Laser ablation
• Perovskite
• Superlattices
• Thin films