Tearing of Black-Filled (N660) Synthetic Polyisoprene Rubber Vulcanizates at Various Temperatures

Natural rubber (NR) has outstanding tack and strength in the unvulcanized state and high tensile and tear strength when vulcanized. These features are attributed to its ability to crystallize rapidly on straining. Synthetic isoprene rubber (IR), synthesized employing a stereospecific catalyst, although close to natural rubber in chemical composition, has reported to be inferior in strength compared to NR. This occurs because IR crystallizes more slowly than NR.Edge-cut tensile specimens of gum natural rubber vulcanizates show an abrupt drop in strength at a critical cut size and normal (no cut) tensile specimens show a sharp decrease in strength at a critical temperature. These two effects are due to bulk strain crystallization at small cut sizes or low temperatures, but the lack thereof at large cut depth or high temperature. The addition of carbon black affects tearing; this depends on the type and concentration of black. Tearing behavior of IR with various amount of N660 carbon black at various temperatures was investigated, and the results are compared to those obtained with natural rubber. The addition of low concentrations of carbon black decrease cut resistance. When temperature or carbon black content increase, anisotropy in strength increases, while critical cut size and exclusion zone decrease. There is a critical level of black needed for reinforcement of IR; this level is higher than that needed for natural rubber. When containing the same amount of black, NR compounds have at least the tear strength of the corresponding IR compounds, and in some cases the NR compounds are much stronger.

Name thesis:degree_name

Doctor of Philosophy

Level thesis:degree_level

doctoral

Discipline thesis:degree_discipline

Polymer Science

Grantor dc:publisher

University of Akron

Year dc:date

2013

Author dc:creator

• Xue, Tianxiang

Contributors dc:contributor

• Hamed, Gard
• Reneker, Darrell

• Polymers
• Synthetic isoprene rubber
• Natural Rubber
• Tearing
• Carbon black

Statement dc:rights

• unrestricted
• This thesis or dissertation is protected by copyright: all rights reserved. It may not be copied or redistributed beyond the terms of applicable copyright laws.

Language dc:language

English

Repository record dc:identifier

http://rave.ohiolink.edu/etdc/view?acc_num=akron1366125713

OAI identifier oai:identifier

oai:etd.ohiolink.edu:akron1366125713