{"id":{"repo_id":"njit","oai_identifier":"oai:digitalcommons.njit.edu:theses-1448"},"canonical_url":"https://search.dev.ndltd.org/etd/njit/oai:digitalcommons.njit.edu:theses-1448","repository":{"repo_id":"njit","name":"NJIT","base_url":"https://digitalcommons.njit.edu/do/oai/"},"display":{"title":"Characterization of thermally diffused bordie layers on AISI 1018 steel : residual stresses (by synchrotron radiation) and microhardness","abstract":"Boronization is a thermal diffusion process in which needle like boride layers are formed at the surface of the metallic substrate. The boride coatings formed by the diffusion process have high hardness and strong ware and corrosion resistance. In order for coatings of this nature to be industrially successful, their service life should be long and characterization should be extensive. Measuring the residual stresses of the coatings caters to each of these aspects. In this study, AISI 1018 steel samples were boronized by a powder-pack process for four hours at 850 C in an argon atmosphere. Characterization techniques included coating thickness, microhardness, residual stresses and elemental distributions. The average thickness of the coating was determined to be 45um while the average boride needle penetration was found to be 57um Line-scan energy dispersive x-ray analysis helped verify the presence of the boride layers. It also showed an accumulation of carbon at the boride layer/substrate interface. Microhardness distributions revealed a maximum Knoop and Vickers hardness of 2,050 and 2,150, respectively. Residual stress measurements were obtained from x-ray diffraction data and evaluated using the multiple tilt sin^2[psi] technique for the iron monoboride layer and the substrate. The residual stresses were found to be compressive for both the iron monoboride layer and the substrate. Their respective values were found to be -237MPa and -l50MPa.","abstract_html":"Boronization is a thermal diffusion process in which needle like boride layers are formed at the surface of the metallic substrate. The boride coatings formed by the diffusion process have high hardness and strong ware and corrosion resistance. In order for coatings of this nature to be industrially successful, their service life should be long and characterization should be extensive. Measuring the residual stresses of the coatings caters to each of these aspects. In this study, AISI 1018 steel samples were boronized by a powder-pack process for four hours at 850 C in an argon atmosphere. Characterization techniques included coating thickness, microhardness, residual stresses and elemental distributions. The average thickness of the coating was determined to be 45um while the average boride needle penetration was found to be 57um Line-scan energy dispersive x-ray analysis helped verify the presence of the boride layers. It also showed an accumulation of carbon at the boride layer/substrate interface. Microhardness distributions revealed a maximum Knoop and Vickers hardness of 2,050 and 2,150, respectively. Residual stress measurements were obtained from x-ray diffraction data and evaluated using the multiple tilt sin^2[psi] technique for the iron monoboride layer and the substrate. The residual stresses were found to be compressive for both the iron monoboride layer and the substrate. Their respective values were found to be -237MPa and -l50MPa.","abstract_has_math":false,"creators":["Payne, Joel A."],"institution":null,"degree_name":"Master of Science in Materials Science and Engineering - (M.S.)","degree_level":null,"degree_discipline":"Committee for the Interdisciplinary Program in Materials Science and Engineering","degree_department":null,"school":null,"contributors":["Roumiana S. Petrova","Roland A. Levy","Reginald Farrow"],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2006,"date_issued":"2006-08-31T07:00:00Z","date_published":"2006-08-31T07:00:00Z","updated_at":"2026-07-24T03:23:22Z","subjects":["Boronization","Steel","Residual stress measurement","Corrosion resistance","Materials Science and Engineering"],"languages":[],"rights":[],"rights_urls":[],"identifier_entries":[]},"links":{"outbound_url":"https://digitalcommons.njit.edu/theses/449","outbound_label":"Repository record","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor","label":"Contributor","values":["Roumiana S. Petrova","Roland A. Levy","Reginald Farrow"]},{"key":"dc:creator","label":"Author","values":["Payne, Joel A."]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Committee for the Interdisciplinary Program in Materials Science and Engineering"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Master of Science in Materials Science and Engineering - (M.S.)"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Boronization","Steel","Residual stress measurement","Corrosion resistance","Materials Science and Engineering"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["https://digitalcommons.njit.edu/theses/449"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["Boronization is a thermal diffusion process in which needle like boride layers are formed at the surface of the metallic substrate. The boride coatings formed by the diffusion process have high hardness and strong ware and corrosion resistance. In order for coatings of this nature to be industrially successful, their service life should be long and characterization should be extensive. Measuring the residual stresses of the coatings caters to each of these aspects. In this study, AISI 1018 steel samples were boronized by a powder-pack process for four hours at 850 C in an argon atmosphere. Characterization techniques included coating thickness, microhardness, residual stresses and elemental distributions. The average thickness of the coating was determined to be 45um while the average boride needle penetration was found to be 57um Line-scan energy dispersive x-ray analysis helped verify the presence of the boride layers. It also showed an accumulation of carbon at the boride layer/substrate interface. Microhardness distributions revealed a maximum Knoop and Vickers hardness of 2,050 and 2,150, respectively. Residual stress measurements were obtained from x-ray diffraction data and evaluated using the multiple tilt sin^2[psi] technique for the iron monoboride layer and the substrate. The residual stresses were found to be compressive for both the iron monoboride layer and the substrate. Their respective values were found to be -237MPa and -l50MPa."]},{"key":"dc:title","label":"Title","values":["Characterization of thermally diffused bordie layers on AISI 1018 steel : residual stresses (by synchrotron radiation) and microhardness"]}]}],"canonical_facts":{"dc:contributor":["Roumiana S. Petrova","Roland A. Levy","Reginald Farrow"],"dc:creator":["Payne, Joel A."],"dc:description.abstract":["Boronization is a thermal diffusion process in which needle like boride layers are formed at the surface of the metallic substrate. The boride coatings formed by the diffusion process have high hardness and strong ware and corrosion resistance. In order for coatings of this nature to be industrially successful, their service life should be long and characterization should be extensive. Measuring the residual stresses of the coatings caters to each of these aspects. In this study, AISI 1018 steel samples were boronized by a powder-pack process for four hours at 850 C in an argon atmosphere. Characterization techniques included coating thickness, microhardness, residual stresses and elemental distributions. The average thickness of the coating was determined to be 45um while the average boride needle penetration was found to be 57um Line-scan energy dispersive x-ray analysis helped verify the presence of the boride layers. It also showed an accumulation of carbon at the boride layer/substrate interface. Microhardness distributions revealed a maximum Knoop and Vickers hardness of 2,050 and 2,150, respectively. Residual stress measurements were obtained from x-ray diffraction data and evaluated using the multiple tilt sin^2[psi] technique for the iron monoboride layer and the substrate. The residual stresses were found to be compressive for both the iron monoboride layer and the substrate. Their respective values were found to be -237MPa and -l50MPa."],"dc:identifier":["https://digitalcommons.njit.edu/theses/449"],"dc:subject":["Boronization","Steel","Residual stress measurement","Corrosion resistance","Materials Science and Engineering"],"dc:title":["Characterization of thermally diffused bordie layers on AISI 1018 steel : residual stresses (by synchrotron radiation) and microhardness"],"dc:type":["Thesis"],"thesis:degree_discipline":["Committee for the Interdisciplinary Program in Materials Science and Engineering"],"thesis:degree_name":["Master of Science in Materials Science and Engineering - (M.S.)"]},"updated_at":"2026-07-24T03:23:22Z"}