Cerium-based conversion coatings on magnesium alloys

"This research is primarily focused on gaining a better understanding of the deposition and corrosion behavior of cerium-based conversion coatings (CeCCs) on AZ31B and AZ91D Mg alloys. Deposition of homogenous and protective CeCCs was highly dependent on the surface preparation steps. The best results were obtained when Mg samples underwent grinding, acid cleaning, and alkaline cleaning processes. This reduced the number of active cathodic sites and promoted the formation of a protective Al-rich Mg oxide/hydroxide layer. Electrochemical properties of the CeCCs were also strongly correlated with morphological, microstructural, and chemical characteristics. Protective CeCCs were deposited on both AZ31 and AZ91 Mg alloys using a range of deposition times (5 to 180 s) and temperatures (10 to 80 ºC). However, shorter deposition times (5 s) and lower deposition temperatures (~10 ºC) showed higher impedance and longer bath stability than other deposition conditions. The increase in impedance was related with fewer cracks and smaller nodule sizes. Additional investigations of post-treated CeCCs exposed to NaCl environments showed an increased in the total impedance. The increase in corrosion protection of the CeCCs was associated with an overall increase in coating thickness from 400 to 800 nm. A microstructural evolution from ~3 nm nodular nanocrystals of CeO₂/CePO₄·H₂O embedded in an amorphous matrix to >50 nm CePO₄·H₂O nanocrystals was responsible for the electrochemically active corrosion protection. Exposure of CeCCs to sunlight in humid environments promoted the reduction of Ce(IV) into Ce(III) species compared to unexposed coatings. This reduction process was related with photocatalytic water oxidation reaction."--Abstract, page iv.

Name thesis:degree_name

Ph. D. in Materials Science and Engineering

Grantor

Missouri University of Science and Technology

Year dc:date.available

2016

Author dc:creator

• Castaño, Carlos E.

• Materials Science and Engineering

Repository record dc:identifier

https://scholarsmine.mst.edu/doctoral_dissertations/2140

OAI identifier oai:identifier

oai:scholarsmine.mst.edu:doctoral_dissertations-3142