Magneto-mechanical properties and applications of Ni-Mn-Ga ferromagnetic shape memory alloy

Ferromagnetic shape memory alloys (FSMA's) have shown large strains under magnetic field as magnetic variants in the rnartensite rearrange to accommodate the applied field. The theoretical maximum field-induced strain is 6.3% in Ni-Mn-Ga FSMA, and results of 6.1% are presented. These strain establish FSMA's as a new class of active materials with strains much larger than piezoelectric or magnetostrictive actuators. This work looks at Ni-Mn-Ga FSMA and explores the correlation between structure and properties, field induced strain at various stresses, and devices based on this new class of active materials. Martensitic Ni-Mn-Ga was found to have a tetragonal 14/mmm crystal structure with a cla ratio of 1.3 3. Twinning can occur on the { 112} planes. A twin boundary in such a crystal should cause a change of direction in the crystal axes of 7 .1 degrees. This angle was measured at 6.5 degrees in a single crystal of Ni-Mn-Ga. Twin angles and strains in the material are dependent on c/a. Surface magnetization measurements show that for this sample each variant is dominated by a single direction of magnetization, with a change in magnetization at the twin boundary. Using a constrained sample technique, the rnagnetocrystalline anisotropy was measured at 0.16 MJ/m3, and the permeability was measured at 22 along the easy axis of the crystal and 2.1 along the hard axis. A model is proposed which predicts a threshold type strain behavior both with internal field at constant stress, and with stress at constant internal field. An experimental apparatus was built to test these conditions. The predictions of the model were largely verified in experiment and field-induced strains up to 6.1 % are measured. Blocking stress matched that predicts at about 1. 7 MP a A prototype magnetic actuator based on Ni-Mn-Ga was built to demonstrate the feasibility of the technology. lbis actuator applied fields of up to 600 kNm to a slender sample in the transverse direction. A maximum deflection of 1.6 mm is achieved for an active material length of 41 mm. AC testing shows the response degrades at frequencies above a few Hz.

Department dc:contributor.department

Massachusetts Institute of Technology. Dept. of Materials Science and Engineering.

Grantor dc:publisher

Massachusetts Institute of Technology

Year dc:date.issued

2000

Author dc:creator

• Murray, Steven J. (Steven James), 1974-

Advisor dc:contributor.advisor

• Samuel M. Allen and Robert C. O'Handley.

• Materials Science and Engineering.

Statement dc:rights

• M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission.

Licence dc:rights.uri

• http://dspace.mit.edu/handle/1721.1/7582

Language dc:language.iso

eng

Handle dc:identifier.uri

http://hdl.handle.net/1721.1/9163

OAI identifier oai:identifier

oai:dspace.mit.edu:1721.1/9163