SiGe-on-insulator and strained-Si-on-insulator for strained-Si CMOS and nanocrystalline-Ge waveguides

SiGe-on-insulator (SGOI) and strained-Si-on-insulator (SSOI) substrates combine both the benefits of a high-quality, monocrystalline SiGe or strained-Si surface layer with the advantages of an insulating substrate. In particular, many electronic and photonic devices are greatly enhanced by the use of such substrates. In this thesis, techniques were developed for the fabrication of SGOI and SSOI substrates for applications including strained-Si complementary metal-oxide-semiconductor (CMOS) field-effect transistors, and nanocrystalline-Ge waveguides and photonic devices. A versatile fabrication technique was pioneered for the fabrication of low defect density SGOI and SSOI substrates, allowing for the creation of ultra-thin SGOI and SSOI, combining both the benefits of high-mobility strained-Si and SOI. The method pioneered employed wafer bonding of polished, relaxed SiGe virtual substrates to oxidized handle wafers. Layer transfer onto insulating handle wafers was accomplished using grind-etchback or delamination via implantation. Both methods were found to produce a rough transferred layer, but chemical mechanical polishing (CMP) was found to be unacceptable due to non-uniform material removal across the wafer and the lack of precise control over the final layer thickness. To solve these problems, a strained-Si stop layer was incorporated into the bonding structure. After layer transfer, excess SiGe was removed using a selective etch process, stopping on the strained-Si. Within the context of ultra-thin SGOI and SSOI fabrication, this work describes recent improvements including metastable stop layers, low- temperature wafer bonding, and improved selective SiGe removal. Such ultra-thin SSOI substrates are ideal for fully-depleted CMOS, in comparison to some thicker SGOI substrates that were fabricated, which are required for partially-depleted CMOS. SGOI substrates can also be used as a platform for novel photonic devices. In this work, one such example is presented, whereby nanocrystalline-Ge waveguides were fabricated using SGOI substrates. These waveguides contained Ge nanocrystals embedded in an oxide matrix and isolated from the underlying Si substrate by a buried silicon dioxide layer. Fabrication challenges revolved around the instability of SiGe- oxide, which was required as an initial material for the nanocrystalline-Ge fabrication

Department dc:contributor.department

Massachusetts Institute of Technology. Dept. of Materials Science and Engineering.

Grantor dc:publisher

Massachusetts Institute of Technology

Year dc:date.issued

2003

Author dc:creator

• Taraschi, Gianni, 1973-

Advisor dc:contributor.advisor

• Eugene A. Fitzgerald.

• Materials Science and Engineering.

Statement dc:rights

• M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission.

Licence dc:rights.uri

• http://dspace.mit.edu/handle/1721.1/7582

Language dc:language.iso

eng

Handle dc:identifier.uri

http://hdl.handle.net/1721.1/7968

OAI identifier oai:identifier

oai:dspace.mit.edu:1721.1/7968