Removal of metal oxide defects through improved semi-anisotropic wet etching process

Data recently collected from an industrial thin film manufacturer indicate that almost 8% of devices are rejected due to excess metal, or unwanted metal on the device surface. Experimentation and analysis suggest that almost half of these defects are caused by incomplete removal of nickel oxides that form on top of the conductive nickel surface throughout the heated environment of the upstream process. This study classified and identified the composition of these excess metal defects, evaluated recommended wet etch methods to remove nickel oxide, and finally proposes a wet etch process that will rapidly remove defects while continuing to maintain the desired semi-anisotropic etch profile, uncharacteristic of most wet immersion etch processes. Results attested that rapid exposure to dilute (40%) nitric acid followed by immediate immersion into a cleaning agent, proprietary nickel etchant, and titanium tungsten etchant removed all nickel oxide defects. Upon implementation, this method has the potential to reduce scrap due to excess metal by 3% and reduce overall etch process time by 25%. In addition, a process was developed to completely etch patterned substrates with high defect density mid process and rework them from raw substrates.

Department dc:contributor.department

Massachusetts Institute of Technology. Dept. of Mechanical Engineering.

Grantor dc:publisher

Massachusetts Institute of Technology

Year dc:date.issued

2012

Author dc:creator

• Dave, Neha H. (Neha Hemang)

Advisor dc:contributor.advisor

• Jung-Hoon Chun.

• Mechanical Engineering.

Statement dc:rights

• M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission.

Licence dc:rights.uri

• http://dspace.mit.edu/handle/1721.1/7582

Language dc:language.iso

eng

Handle dc:identifier.uri

http://hdl.handle.net/1721.1/78167

OAI identifier oai:identifier

oai:dspace.mit.edu:1721.1/78167