Fracture and plasticity characterization of DH-36 Navy steel

Multi-layered plates consisting of DH-36 steel coated by a thick layer of polyurea, for increased blast and impact protection, are of increasing importance to the Department of Defense. A hybrid approach of experiments and simulation was performed to characterize fracture and plasticity of DH-36 Navy steel, which is the first step in creating an accurate model of the composite material. The performance limit to this material during an impact is ductile fracture. The prediction follows that the onset of fracture occurs when a certain critical value of plastic strain is reached. This value is highly dependent on the state of stress. Seven different types of tests were performed, including tensile tests on dog-bone and notched specimens and punch indentation tests on circular blanks. Also, tensile and shear tests were performed on butterfly specimens using the dual actuator loading frame. Fracture surface strains were measured using digital image correlation. Local fracture strains were obtained by using an inverse engineering method of matching measured displacement to fracture with computer simulations. The results are used to calibrate the Modified Mohr Coulomb fracture model which is expressed by the stress state invariants of Lode angle and triaxiality.

Department dc:contributor.department

Massachusetts Institute of Technology. Dept. of Mechanical Engineering.

Grantor dc:publisher

Massachusetts Institute of Technology

Year dc:date.issued

2012

Author dc:creator

• MacLean, Christopher Glenn

Advisor dc:contributor.advisor

• Tomasz Wierzbicki.

• Mechanical Engineering.

Statement dc:rights

• M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission.

Licence dc:rights.uri

• http://dspace.mit.edu/handle/1721.1/7582

Language dc:language.iso

eng

Handle dc:identifier.uri

http://hdl.handle.net/1721.1/74894

OAI identifier oai:identifier

oai:dspace.mit.edu:1721.1/74894