{"id":{"repo_id":"mit","oai_identifier":"oai:dspace.mit.edu:1721.1/45267"},"canonical_url":"https://search.dev.ndltd.org/etd/mit/oai:dspace.mit.edu:1721.1/45267","repository":{"repo_id":"mit","name":"MIT","base_url":"https://dspace.mit.edu/oai/request"},"display":{"title":"Investigation of cork as filler for fiber-reinforced composite material in kayaks","abstract":"This project is a continuation in the investigation of ways in which cork can be incorporated into composite material for boats and kayaks without significant performance losses. Fiberglass lay-ups (cloth, mat, and epoxy) and cork-epoxy samples are prepared by vacuum bagging. Samples undergo a three-point bending test (ASTM D79o) and a Charpy impact test (ASTM D611o) to investigate maximum flexural stress, effective elastic modulus, and impact resistance. Fiberglass-epoxy samples serve as the control for comparing the results of the cork composite samples. The average flexural strength of the fiberglass ranged from 191-234 MPa with the different configurations of fiberglass cloth. The effective elastic modulus ranged from 8.4-10 MPa. These values fall in the lower range of other composites when compared to general Ashby charts. Its impact resistance, taken with respect to cross-sectional area to account for variations in the thickness from sample to sample in the formation process, ranged from 54.9 to 64.5 kJ/m2. The cork composite samples were at least four times weaker than their fiberglass counterparts in all investigated respects. However, the cork samples were up to three times lighter and needed less than half of the epoxy the fiberglass samples required. The inclusion of fiberglass cloth helped increase its strength significantly without sacrifice to weight, indicating the likely need to incorporate chopped fiberglass strands in future testing.","abstract_html":"This project is a continuation in the investigation of ways in which cork can be incorporated into composite material for boats and kayaks without significant performance losses. Fiberglass lay-ups (cloth, mat, and epoxy) and cork-epoxy samples are prepared by vacuum bagging. Samples undergo a three-point bending test (ASTM D79o) and a Charpy impact test (ASTM D611o) to investigate maximum flexural stress, effective elastic modulus, and impact resistance. Fiberglass-epoxy samples serve as the control for comparing the results of the cork composite samples. The average flexural strength of the fiberglass ranged from 191-234 MPa with the different configurations of fiberglass cloth. The effective elastic modulus ranged from 8.4-10 MPa. These values fall in the lower range of other composites when compared to general Ashby charts. Its impact resistance, taken with respect to cross-sectional area to account for variations in the thickness from sample to sample in the formation process, ranged from 54.9 to 64.5 kJ/m2. The cork composite samples were at least four times weaker than their fiberglass counterparts in all investigated respects. However, the cork samples were up to three times lighter and needed less than half of the epoxy the fiberglass samples required. The inclusion of fiberglass cloth helped increase its strength significantly without sacrifice to weight, indicating the likely need to incorporate chopped fiberglass strands in future testing.","abstract_has_math":false,"creators":["Yeh, Chihjiun Connie"],"institution":"Massachusetts Institute of Technology","degree_name":null,"degree_level":null,"degree_discipline":null,"degree_department":"Massachusetts Institute of Technology. Department of Mechanical Engineering","school":null,"contributors":[],"advisors":["David Wallace."],"committee_chairs":[],"committee_members":[],"year":2008,"date_issued":"2008","date_published":"2008","updated_at":"2026-07-22T22:20:44Z","subjects":["Mechanical Engineering."],"languages":["eng"],"rights":["M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission."],"rights_urls":["http://dspace.mit.edu/handle/1721.1/7582"],"identifier_entries":[]},"links":{"outbound_url":"http://hdl.handle.net/1721.1/45267","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.advisor","label":"Advisor","values":["David Wallace."]},{"key":"dc:contributor.department","label":"Department","values":["Massachusetts Institute of Technology. Department of Mechanical Engineering"]},{"key":"dc:contributor.other","label":"Dc Contributor Other","values":["Massachusetts Institute of Technology. Dept. of Mechanical Engineering."]},{"key":"dc:creator","label":"Author","values":["Yeh, Chihjiun Connie"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2009-04-29T17:17:38Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2009-04-29T17:17:38Z"]},{"key":"dc:date.issued","label":"Date","values":["2008"]},{"key":"dc:publisher","label":"Institution","values":["Massachusetts Institute of Technology"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Mechanical Engineering."]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["eng"]},{"key":"dc:rights","label":"Dc Rights","values":["M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission."]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://dspace.mit.edu/handle/1721.1/7582"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/1721.1/45267"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["Thesis (S.B.)--Massachusetts Institute of Technology, Dept. of Mechanical Engineering, 2008.","Includes bibliographical references (p. 43)."]},{"key":"dc:description.abstract","label":"Abstract","values":["This project is a continuation in the investigation of ways in which cork can be incorporated into composite material for boats and kayaks without significant performance losses. Fiberglass lay-ups (cloth, mat, and epoxy) and cork-epoxy samples are prepared by vacuum bagging. Samples undergo a three-point bending test (ASTM D79o) and a Charpy impact test (ASTM D611o) to investigate maximum flexural stress, effective elastic modulus, and impact resistance. Fiberglass-epoxy samples serve as the control for comparing the results of the cork composite samples. The average flexural strength of the fiberglass ranged from 191-234 MPa with the different configurations of fiberglass cloth. The effective elastic modulus ranged from 8.4-10 MPa. These values fall in the lower range of other composites when compared to general Ashby charts. Its impact resistance, taken with respect to cross-sectional area to account for variations in the thickness from sample to sample in the formation process, ranged from 54.9 to 64.5 kJ/m2. The cork composite samples were at least four times weaker than their fiberglass counterparts in all investigated respects. However, the cork samples were up to three times lighter and needed less than half of the epoxy the fiberglass samples required. The inclusion of fiberglass cloth helped increase its strength significantly without sacrifice to weight, indicating the likely need to incorporate chopped fiberglass strands in future testing."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["S.B."]},{"key":"dc:title","label":"Title","values":["Investigation of cork as filler for fiber-reinforced composite material in kayaks"]}]}],"canonical_facts":{"dc:contributor.advisor":["David Wallace."],"dc:contributor.department":["Massachusetts Institute of Technology. Department of Mechanical Engineering"],"dc:contributor.other":["Massachusetts Institute of Technology. Dept. of Mechanical Engineering."],"dc:creator":["Yeh, Chihjiun Connie"],"dc:date.accessioned":["2009-04-29T17:17:38Z"],"dc:date.available":["2009-04-29T17:17:38Z"],"dc:date.issued":["2008"],"dc:description":["Thesis (S.B.)--Massachusetts Institute of Technology, Dept. of Mechanical Engineering, 2008.","Includes bibliographical references (p. 43)."],"dc:description.abstract":["This project is a continuation in the investigation of ways in which cork can be incorporated into composite material for boats and kayaks without significant performance losses. Fiberglass lay-ups (cloth, mat, and epoxy) and cork-epoxy samples are prepared by vacuum bagging. Samples undergo a three-point bending test (ASTM D79o) and a Charpy impact test (ASTM D611o) to investigate maximum flexural stress, effective elastic modulus, and impact resistance. Fiberglass-epoxy samples serve as the control for comparing the results of the cork composite samples. The average flexural strength of the fiberglass ranged from 191-234 MPa with the different configurations of fiberglass cloth. The effective elastic modulus ranged from 8.4-10 MPa. These values fall in the lower range of other composites when compared to general Ashby charts. Its impact resistance, taken with respect to cross-sectional area to account for variations in the thickness from sample to sample in the formation process, ranged from 54.9 to 64.5 kJ/m2. The cork composite samples were at least four times weaker than their fiberglass counterparts in all investigated respects. However, the cork samples were up to three times lighter and needed less than half of the epoxy the fiberglass samples required. The inclusion of fiberglass cloth helped increase its strength significantly without sacrifice to weight, indicating the likely need to incorporate chopped fiberglass strands in future testing."],"dc:description.degree":["S.B."],"dc:identifier.uri":["http://hdl.handle.net/1721.1/45267"],"dc:language.iso":["eng"],"dc:publisher":["Massachusetts Institute of Technology"],"dc:rights":["M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission."],"dc:rights.uri":["http://dspace.mit.edu/handle/1721.1/7582"],"dc:subject":["Mechanical Engineering."],"dc:title":["Investigation of cork as filler for fiber-reinforced composite material in kayaks"],"dc:type":["Thesis"]},"updated_at":"2026-07-22T22:20:44Z"}