Effects of catalyst pretreatment for carbon nanotube growth

The effects of pretreatment of iron catalyst for carbon nanotube (CNT) growth was studied. CNTs were grown on Fe/A1203 (1/10 nm) thin-film catalyst deposited on silicon substrates via exposure to C2H4 in a thermal chemical vapor deposition (CVD) furnace. During CVD, the sample was exposed to a carrier gas (Argon) for the 35-minute temperature ramp, and 15-minute anneal, then to a mix of carrier gas and ethylene for a 15-minute growth stage. Experiments were performed varying the amount of oxygen contaminant in the carrier gas, and the time of hydrogen introduction. Samples were characterized via atomic force microscopy (AFM), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). It was found that the later hydrogen was introduced, the higher the catalyst density and the taller the CNT carpet. The catalyst efficiency was also shown to increase with later hydrogen introduction. No clear trend was observed between the amount of oxygen in the carrier gas and the height of CNT growth. Data points to the model of catalyst coarsening being crucial to the nucleation and growth of CNTs and the parameters of CNTs grown. Variations in trends are discussed.

Department dc:contributor.department

Massachusetts Institute of Technology. Department of Materials Science and Engineering

Grantor dc:publisher

Massachusetts Institute of Technology

Year dc:date.issued

2007

Author dc:creator

• Morgan, Caitlin D

Advisor dc:contributor.advisor

• Carl V. Thompson.

• Materials Science and Engineering.

Statement dc:rights

• M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission.

Licence dc:rights.uri

• http://dspace.mit.edu/handle/1721.1/7582

Language dc:language.iso

eng

Handle dc:identifier.uri

http://hdl.handle.net/1721.1/44816

OAI identifier oai:identifier

oai:dspace.mit.edu:1721.1/44816