{"id":{"repo_id":"mit","oai_identifier":"oai:dspace.mit.edu:1721.1/41270"},"canonical_url":"https://search.dev.ndltd.org/etd/mit/oai:dspace.mit.edu:1721.1/41270","repository":{"repo_id":"mit","name":"MIT","base_url":"https://dspace.mit.edu/oai/request"},"display":{"title":"Effects of thermal aging on Stress Corrosion Cracking and mechanical properties of stainless steel weld metals","abstract":"Stress Corrosion Cracking (SCC) in and around primary loop piping welds in Boiling Water Reactors has been observed worldwide as plants continue to operate at temperatures and pressures near 2880C (5500F) and 6.9 MPa (1000 PSI). An experimental program was designed to explore the effect of thermal aging on the SCC crack growth rate in weld materials for type 316 and 304 stainless steels. An autoclave facility was designed and constructed for the measurement of SCC crack growth rates under BWR conditions and testing was underway at the time of this writing. The effects of composition and thermal aging on mechanical properties (i.e. tensile, micro-hardness, nano-hardness, Jic, and Charpy-impact toughness) was in process and initial results show an increase in yield strength and a decrease in fracture toughness after aging for 1000 hours at 430 and 400 *C. Thermal aging results in no discernable changes to the 6-ferrite morphology when viewed optically at 500 X agnifications and in the scanning electron microscope.","abstract_html":"Stress Corrosion Cracking (SCC) in and around primary loop piping welds in Boiling Water Reactors has been observed worldwide as plants continue to operate at temperatures and pressures near 2880C (5500F) and 6.9 MPa (1000 PSI). An experimental program was designed to explore the effect of thermal aging on the SCC crack growth rate in weld materials for type 316 and 304 stainless steels. An autoclave facility was designed and constructed for the measurement of SCC crack growth rates under BWR conditions and testing was underway at the time of this writing. The effects of composition and thermal aging on mechanical properties (i.e. tensile, micro-hardness, nano-hardness, Jic, and Charpy-impact toughness) was in process and initial results show an increase in yield strength and a decrease in fracture toughness after aging for 1000 hours at 430 and 400 *C. Thermal aging results in no discernable changes to the 6-ferrite morphology when viewed optically at 500 X agnifications and in the scanning electron microscope.","abstract_has_math":false,"creators":["Hixon, Jeff"],"institution":"Massachusetts Institute of Technology","degree_name":null,"degree_level":null,"degree_discipline":null,"degree_department":"Massachusetts Institute of Technology. Dept. of Nuclear Science and Engineering.","school":null,"contributors":[],"advisors":["Ronald G. Ballinger."],"committee_chairs":[],"committee_members":[],"year":2006,"date_issued":"2006","date_published":"2006","updated_at":"2026-07-22T22:21:25Z","subjects":["Nuclear Science and Engineering."],"languages":["eng"],"rights":["M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission."],"rights_urls":["http://dspace.mit.edu/handle/1721.1/7582"],"identifier_entries":[]},"links":{"outbound_url":"http://hdl.handle.net/1721.1/41270","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.advisor","label":"Advisor","values":["Ronald G. Ballinger."]},{"key":"dc:contributor.department","label":"Department","values":["Massachusetts Institute of Technology. Dept. of Nuclear Science and Engineering."]},{"key":"dc:contributor.other","label":"Dc Contributor Other","values":["Massachusetts Institute of Technology. Dept. of Nuclear Science and Engineering."]},{"key":"dc:creator","label":"Author","values":["Hixon, Jeff"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2008-04-23T14:37:53Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2008-04-23T14:37:53Z"]},{"key":"dc:date.issued","label":"Date","values":["2006"]},{"key":"dc:publisher","label":"Institution","values":["Massachusetts Institute of Technology"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Nuclear Science and Engineering."]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language.iso","label":"Language (ISO)","values":["eng"]},{"key":"dc:rights","label":"Dc Rights","values":["M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission."]},{"key":"dc:rights.uri","label":"Rights URI","values":["http://dspace.mit.edu/handle/1721.1/7582"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/1721.1/41270"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["Thesis (S.M.)--Massachusetts Institute of Technology, Dept. of Nuclear Science and Engineering, 2006.","Includes bibliographical references (p. 589)."]},{"key":"dc:description.abstract","label":"Abstract","values":["Stress Corrosion Cracking (SCC) in and around primary loop piping welds in Boiling Water Reactors has been observed worldwide as plants continue to operate at temperatures and pressures near 2880C (5500F) and 6.9 MPa (1000 PSI). An experimental program was designed to explore the effect of thermal aging on the SCC crack growth rate in weld materials for type 316 and 304 stainless steels. An autoclave facility was designed and constructed for the measurement of SCC crack growth rates under BWR conditions and testing was underway at the time of this writing. The effects of composition and thermal aging on mechanical properties (i.e. tensile, micro-hardness, nano-hardness, Jic, and Charpy-impact toughness) was in process and initial results show an increase in yield strength and a decrease in fracture toughness after aging for 1000 hours at 430 and 400 *C. Thermal aging results in no discernable changes to the 6-ferrite morphology when viewed optically at 500 X agnifications and in the scanning electron microscope."]},{"key":"dc:description.degree","label":"Dc Description Degree","values":["S.M."]},{"key":"dc:title","label":"Title","values":["Effects of thermal aging on Stress Corrosion Cracking and mechanical properties of stainless steel weld metals"]}]}],"canonical_facts":{"dc:contributor.advisor":["Ronald G. Ballinger."],"dc:contributor.department":["Massachusetts Institute of Technology. Dept. of Nuclear Science and Engineering."],"dc:contributor.other":["Massachusetts Institute of Technology. Dept. of Nuclear Science and Engineering."],"dc:creator":["Hixon, Jeff"],"dc:date.accessioned":["2008-04-23T14:37:53Z"],"dc:date.available":["2008-04-23T14:37:53Z"],"dc:date.issued":["2006"],"dc:description":["Thesis (S.M.)--Massachusetts Institute of Technology, Dept. of Nuclear Science and Engineering, 2006.","Includes bibliographical references (p. 589)."],"dc:description.abstract":["Stress Corrosion Cracking (SCC) in and around primary loop piping welds in Boiling Water Reactors has been observed worldwide as plants continue to operate at temperatures and pressures near 2880C (5500F) and 6.9 MPa (1000 PSI). An experimental program was designed to explore the effect of thermal aging on the SCC crack growth rate in weld materials for type 316 and 304 stainless steels. An autoclave facility was designed and constructed for the measurement of SCC crack growth rates under BWR conditions and testing was underway at the time of this writing. The effects of composition and thermal aging on mechanical properties (i.e. tensile, micro-hardness, nano-hardness, Jic, and Charpy-impact toughness) was in process and initial results show an increase in yield strength and a decrease in fracture toughness after aging for 1000 hours at 430 and 400 *C. Thermal aging results in no discernable changes to the 6-ferrite morphology when viewed optically at 500 X agnifications and in the scanning electron microscope."],"dc:description.degree":["S.M."],"dc:identifier.uri":["http://hdl.handle.net/1721.1/41270"],"dc:language.iso":["eng"],"dc:publisher":["Massachusetts Institute of Technology"],"dc:rights":["M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission."],"dc:rights.uri":["http://dspace.mit.edu/handle/1721.1/7582"],"dc:subject":["Nuclear Science and Engineering."],"dc:title":["Effects of thermal aging on Stress Corrosion Cracking and mechanical properties of stainless steel weld metals"],"dc:type":["Thesis"]},"updated_at":"2026-07-22T22:21:25Z"}