Microstructural effects on capacity-rate performance of vanadium oxide cathodes in lithium-ion batteries

Vanadium oxide thin film cathodes were analyzed to determine whether smaller average grain size and/or a narrower average grain size distribution affects the capacity-rate performance in lithium-ion batteries. Vanadium oxide thin films were prepared by sputtering onto ITO-coated glass substrates and crystallized in a refined annealing process to generate diverse microstructures. Average grain size and grain size distribution were determined in SEM analysis. No significant difference was observed in capacity rate behavior with changes in microstructure. However, it is speculated that further in situ analysis may show different relative diffusion rates into grains of differing sizes is related to different microstructures.

Department dc:contributor.department

Massachusetts Institute of Technology. Dept. of Materials Science and Engineering.

Grantor dc:publisher

Massachusetts Institute of Technology

Year dc:date.issued

2005

Author dc:creator

• Davis, Robin M. (Robin Manes)

Advisor dc:contributor.advisor

• Donald R. Sadoway.

• Materials Science and Engineering.

Statement dc:rights

• M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission.

Licence dc:rights.uri

• http://dspace.mit.edu/handle/1721.1/7582

Language dc:language.iso

eng

Handle dc:identifier.uri

http://hdl.handle.net/1721.1/32852

OAI identifier oai:identifier

oai:dspace.mit.edu:1721.1/32852