Roles of grain boundaries in cleavage cracking and thermal crack arrest experiments in iron-silicon alloy

High-angle grain boundaries in steel offer an important resistance to the propagation of cleavage cracks that affects the fracture toughness and can modulate the ductile-to-brittle transition temperature of fracture downward. This behavior has been studied in this thesis in detail. In grain-boundary toughness measurement experiments in bicrystals of Fe-3%Si alloy, specific measurements of the fracture resistance of a random selection of high angle grain boundaries and associated fractographic studies have led to quantitative models of the resistance that high-angle grain boundaries offer to cleavage cracks. The study has also revealed a transition from pure cleavage to mixed cleavage (PC/MC) around OC for this alloy. Experiments were also carried out on the modes of advance of cleavage cracks through a field of randomly oriented grains at -30C in the pure cleavage range (lower shelf) in very large grain-sized Fe-2%Si alloy, permitting detailed observations of the chronology of percolation of the cleavage crack front. Utilizing previously developed model-based information on the peak resistance to fracture of high angle grain boundaries, with a given tilt and twist misorientation across them, and detailed measurements of orientations of individual grains in the samples, it was possible to develop percolation maps of cleavage through the field of grains that for the initial phases of fracture through grains predicted the actual path with about 70% accuracy when compared with experimental observations.

Department dc:contributor.department

Massachusetts Institute of Technology. Dept. of Mechanical Engineering.

Grantor dc:publisher

Massachusetts Institute of Technology

Year dc:date.issued

2002

Author dc:creator

• Qiao, Yu, 1972-

Advisor dc:contributor.advisor

• Ali S. Argon.

• Mechanical Engineering.

Statement dc:rights

• M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission.

Licence dc:rights.uri

• http://dspace.mit.edu/handle/1721.1/7582

Language dc:language.iso

eng

Handle dc:identifier.uri

http://hdl.handle.net/1721.1/29253

OAI identifier oai:identifier

oai:dspace.mit.edu:1721.1/29253