Properties and sensor performance of zinc oxide thin films

Reactively sputtered ZnO thin film gas sensors were fabricated onto Si wafers. The atmosphere dependent electrical response of the ZnO micro arrays was examined. The effects of processing conditions on the properties and sensor performance of ZnO films were investigated. Using AFM, SEM, XRD and WDS, the 02/Ar ratios during sputtering and Al dopant were found to control the property of ZnO films. Subsequent annealing at 700 C improved the sensor response of the films considerably although it had only minor effects on the microstructure. DC resistance, I-V curves and AC impedance were utilized to investigate the gas response of ZnO sensors. ZnO films prepared with high O2/Ar ratios showed better sensitivity to various gases, a feature believed to be related to their lower carrier density. Al doped ZnO showed measurable sensitivity even with lower resistance attributable to their porous microstructure. AC impedance identified two major components of the total resistance including Schottky barriers at the Pt-ZnO interfaces and a DC bias induced constriction resistance within the ZnO films. Time dependent drift in resistance of ZnO films has been observed. Without applied bias, the ZnO films showed a fast and a slow resistance change response when exposed to gases with varying oxygen partial pressure with both response components dependent on operating temperature. Even at the relatively low operating temperatures of these thin film sensors, bulk diffusion cannot be discounted. The oxygen partial pressure dependence of the sensor resistance and its corresponding activation energy were related to defect process controlling the reduction/oxidation behavior of the ZnO.

Department dc:contributor.department

Massachusetts Institute of Technology. Dept. of Materials Science and Engineering.

Grantor dc:publisher

Massachusetts Institute of Technology

Year dc:date.issued

2003

Author dc:creator

• Min, Yongki, 1965-

Advisor dc:contributor.advisor

• Harry L. Tuller.

• Materials Science and Engineering.

Statement dc:rights

• M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission.

Licence dc:rights.uri

• http://dspace.mit.edu/handle/1721.1/7582

Language dc:language.iso

eng

Handle dc:identifier.uri

http://hdl.handle.net/1721.1/17032

OAI identifier oai:identifier

oai:dspace.mit.edu:1721.1/17032