Microfabrication and electrical characterization of lead-free sodium potassium niobate thin film ribbons on conformal substrates

There have been recent concerns regarding the use, recycling, and disposal of the predominantly used leaded piezoelectric ceramic- Lead Zirconate Titanate (PZT). The European Union has initiated restricting the use of lead in commercial products, with countries such as China and Japan. These regulations provide further motivation for the development of an alternative to leaded piezoelectric materials. The aim of this thesis is to characterize the more recently researched lead-free piezoelectric alternative, Sodium Potassium Niobate (KNN). Thin films of KNN ribbons with gold interconnects are microfabricated on various conformal substrates such as Kapton, Ecoflex, Polydimethylsiloxane (PDMS), and Silbione/fabric and characterized electrically using the Keithley Semiconductor Parameter Analyzer. In this initial experimental evaluation, it was found that at the frequency of 100 KHz, the dielectric constant of the KNN on PDMS is the highest at 427 followed by the Kapton at 410. The Ecoflex and Silbione/fabric both have a dielectric of about 387. In the literature, the dielectric constant of KNN is reported to fall between 185 and 598 based on the substrate it is on, and our values are well within this reported range. The results from the other electrical characterization tests indicate that the KNN behaves similarly on the different tested substrates as the capacitance, polarization curve, and leakage current of all the devices are in the same range and are close as the ribbons are swept from -40 V to 40 V.

Name thesis:degree_name

Master

Department dc:contributor.department

Program in Media Arts and Sciences (Massachusetts Institute of Technology)

Grantor dc:publisher

Massachusetts Institute of Technology

Year dc:date.issued

2019

Author dc:creator

• Sadraei, Atieh.

Advisor dc:contributor.advisor

• Canan Dagdeviren.

• Program in Media Arts and Sciences

Statement dc:rights

• MIT theses are protected by copyright. They may be viewed, downloaded, or printed from this source but further reproduction or distribution in any format is prohibited without written permission.

Licence dc:rights.uri

• http://dspace.mit.edu/handle/1721.1/7582

Language dc:language.iso

eng

Handle dc:identifier.uri

https://hdl.handle.net/1721.1/123646

OAI identifier oai:identifier

oai:dspace.mit.edu:1721.1/123646