Energy dissipation in shape memory zirconia particles, packings, and composites

This research project lies at the intersection of two classes of materials, namely superelastic materials and granular materials, each known for their ability to dissipate large amounts of kinetic energy. Because of their energy-absorbing properties, superelastic granular materials are of interest for development into applications involving force protection. Quasi-static, closed-die compression tests were conducted on granular packings of ceria-doped zirconia, a material which is well-known to exhibit shape memory and superelastic behavior. The doping level of ceria in the zirconia system was controlled to experimentally determine the mole percent for optimal energy dissipation in a granular packing. Various particle size distributions were selected to study mechanisms of energy dissipation in a granular packing including particle friction, fracture, and martensitic phase transformation. To study the behavior of encapsulated shape memory and superelastic zirconia particles, composites were fabricated using polyurea as a matrix material, and the bonding between the zirconia particles and polyurea matrix was studied along with mechanical properties. Finally, the effect of high strain rate impact was observed on ceria-doped zirconia pellets using laser induced particle impact testing (LIPIT) which launches single, micron-sized particles at high velocities. This thesis provides further insight into the mechanical behavior of granular superelastic ceramics under different constraints and loading conditions while optimizing for energy dissipation.

Name thesis:degree_name

Master

Department dc:contributor.department

Massachusetts Institute of Technology. Department of Materials Science and Engineering

Grantor dc:publisher

Massachusetts Institute of Technology

Year dc:date.issued

2019

Author dc:creator

• Champagne, Victor K.,III(Victor Kenneth)

Advisor dc:contributor.advisor

• Christopher A. Schuh.

• Materials Science and Engineering.

Statement dc:rights

• MIT theses are protected by copyright. They may be viewed, downloaded, or printed from this source but further reproduction or distribution in any format is prohibited without written permission.

Licence dc:rights.uri

• http://dspace.mit.edu/handle/1721.1/7582

Language dc:language.iso

eng

Handle dc:identifier.uri

https://hdl.handle.net/1721.1/123621

OAI identifier oai:identifier

oai:dspace.mit.edu:1721.1/123621