Effects of silica nanoparticle surface treatment and average diameter on the physical and mechanical properties of poly(dimethylsiloxane)-silica nanocomposites

The purpose of this thesis was to quantify the effects of silica nanoparticle surface treatments and average silica nanoparticle diameter on various macroscopic properties of poly(dimethylsiloxane)-silica nanocomposites, specifically stiffness, wettability, and permeability to organic solvents. Poly(dimethylsiloxane)-silica nancomposites were prepared with constant amounts (4.8 wt%, 1.8 vol%) of fumed silica nanoparticles with varying surface treatments (hexamethyldisilazane and octamethylcyclotetrasiloxane) and varying particle diameter (7 and 12 nm). The Young's elastic modulus, mass increase due to dodecane absorption after 10 minutes, and advancing and receding water contact angles were measured for each nanocomposite. PDMS-silica nanocomposites containing untreated silica nanoparticles were found to have a higher Young's elastic modulus than nanocomposites containing hexamethyldisilazane-treated silica nanoparticles with the same diameter. However, nanocomposites containing identically sized silica nanoparticles with and without the octamethylcyclotetrasiloxane surface treatment had the same stiffness. The average nanocomposite stiffness increased slightly as the untreated silica nanoparticle diameter decreased from 12 nm to 7 nm. Varying the surface treatment or particle diameter of the filler did not significantly affect the level of dodecane absorption or the wettability of the nanocomposite. All nanocomposites showed approximately 20-23 wt% increase from dodecane absorption after 10 minutes of dodecane immersion. All nanocomposites exhibited average advancing contact angles around 115-120° and average receding contact angles around 85-90°. Nanocomposites were imaged using optical coherence tomography to examine particle dispersion. Potential differences in particle dispersion are discussed.

Department dc:contributor.department

Massachusetts Institute of Technology. Department of Materials Science and Engineering.

Grantor dc:publisher

Massachusetts Institute of Technology

Year dc:date.issued

2010

Author dc:creator

• Guha, Ingrid F

Advisor dc:contributor.advisor

• Krystyn J. Van Vliet.

• Materials Science and Engineering.

Statement dc:rights

• MIT theses are protected by copyright. They may be viewed, downloaded, or printed from this source but further reproduction or distribution in any format is prohibited without written permission.

Licence dc:rights.uri

• http://dspace.mit.edu/handle/1721.1/7582

Language dc:language.iso

eng

Handle dc:identifier.uri

http://hdl.handle.net/1721.1/118564

OAI identifier oai:identifier

oai:dspace.mit.edu:1721.1/118564