Nanoporous carbon from corn cobs and its application

Chemical activation of corn cobs using phosphoric acid or potassium hydroxide can lead to nanoporous carbon having surface area in excess of 3800 m²/g and pore volume of 2.5cc/g. Dried, crushed, corn cobs were carbonized at temperatures between 450- 900⁰C and chemically activated using H₃PO₄ and KOH. The effect of different variables of activation such as heat treatment temperature, rate of heating and concentration of activating agent was studied. The mechanism of phosphoric acid activation was studied using thermogravimetric analysis. The nanoporous carbon was characterized by N2 adsorption at 77 K, and the isotherms were analyzed using BET, T-method and D-R method for determining surface area and pore volume. The nanoporous carbon obtained from corn cobs was further converted to monolithic form and its capacity to store natural gas at 500psi and 298K was measured using gravimetric and volumetric measuring techniques. Methane capacity as high as 173V/V or 0.21g/g or 108g/L were obtained on the carbon produced from corn cobs. The effect of various parameters of carbon production on the methane storage and delivery capacity was studied.

Name thesis:degree_name

Ph. D.

Level thesis:degree_level

Doctoral

Discipline thesis:degree_discipline

Chemical engineering (MU)

Grantor dc:publisher

University of Missouri--Columbia

Year dc:date.issued

2007

Author dc:creator

• Shah, Parag S.

Advisor dc:contributor.advisor

• Suppes, Galen J.

Statement dc:rights

• OpenAccess.

Language dc:language.iso

eng, English

DOI

https://doi.org/10.32469/10355/4815

OAI identifier oai:identifier

oai:mospace.umsystem.edu:10355/4815